Dataset Information

Comprehensive NMR Analysis of Pore Structures in Superabsorbing Cellulose Nanofiber Aerogels.

ABSTRACT: Highly porous cellulose nanofiber (CNF) aerogels are promising, environmentally friendly, reusable, and low-cost materials for several advanced environmental, biomedical, and electronic applications. The aerogels have a complex and hierarchical 3D porous network structure with pore sizes ranging from nanometers to hundreds of micrometers. The morphology of the network has a critical role on the performance of aerogels, but it is difficult to characterize thoroughly with traditional techniques. Here, we introduce a combination of nuclear magnetic resonance (NMR) spectroscopy techniques for comprehensive characterization of pore sizes and connectivity in the CNF aerogels. Cyclohexane absorbed in the aerogels was used as a probe fluid. NMR cryoporometry enabled us to characterize the size distribution of nanometer scale pores in between the cellulose nanofibers in the solid matrix of the aerogels. Restricted diffusion of cyclohexane revealed the size distribution of the dominant micrometer scale pores as well as the tortuosity of the pore network. T ₂ relaxation filtered microscopic magnetic resonance imaging (MRI) method allowed us to determine the size distribution of the largest, submillimeter scale pores. The NMR techniques are nondestructive, and they provide information about the whole sample volume (not only surfaces). Furthermore, they show how absorbed liquids experience the complex 3D pore structure. Thorough characterization of porous structures is important for understanding the properties of the aerogels and optimizing them for various applications. The introduced comprehensive NMR analysis set is widely usable for a broad range of different kinds of aerogels used in different applications, such as catalysis, batteries, supercapacitors, hydrogen storage, etc.

SUBMITTER: Kharbanda Y

PROVIDER: S-EPMC6977143 | biostudies-literature | 2019 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Comprehensive NMR Analysis of Pore Structures in Superabsorbing Cellulose Nanofiber Aerogels.

Kharbanda Yashu Y Urbańczyk Mateusz M Laitinen Ossi O Kling Kirsten K Pallaspuro Sakari S Komulainen Sanna S Liimatainen Henrikki H Telkki Ville-Veikko VV

The journal of physical chemistry. C, Nanomaterials and interfaces 20191202 51

Highly porous cellulose nanofiber (CNF) aerogels are promising, environmentally friendly, reusable, and low-cost materials for several advanced environmental, biomedical, and electronic applications. The aerogels have a complex and hierarchical 3D porous network structure with pore sizes ranging from nanometers to hundreds of micrometers. The morphology of the network has a critical role on the performance of aerogels, but it is difficult to characterize thoroughly with traditional techniques. H ...[more]

PMID: 31983933

Similar Datasets

Project description:Tunable porous composite materials to control metal and metal oxide functionalization, conductivity, pore structure, electrolyte mass transport, mechanical strength, specific surface area, and magneto-responsiveness are critical for a broad range of energy storage, catalysis, and sensing applications. Biotemplated transition metal composite aerogels present a materials approach to address this need. To demonstrate a solution-based synthesis method to develop cobalt and cobalt oxide aerogels for high surface area multifunctional energy storage electrodes, carboxymethyl cellulose nanofibers (CNF) and alginate biopolymers were mixed to form hydrogels to serve as biotemplates for cobalt nanoparticle formation via the chemical reduction of cobalt salt solutions. The CNF-alginate mixture forms a physically entangled, interpenetrating hydrogel, combining the properties of both biopolymers for monolith shape and pore size control and abundant carboxyl groups that bind metal ions to facilitate biotemplating. The CNF-alginate hydrogels were equilibrated in CaCl2 and CoCl2 salt solutions for hydrogel ionic crosslinking and the prepositioning of transition metal ions, respectively. The salt equilibrated hydrogels were chemically reduced with NaBH4, rinsed, solvent exchanged in ethanol, and supercritically dried with CO2 to form aerogels with a specific surface area of 228 m2/g. The resulting aerogels were pyrolyzed in N2 gas and thermally annealed in air to form Co and Co3O4 porous composite electrodes, respectively. The multifunctional composite aerogel's mechanical, magnetic, and electrochemical functionality was characterized. The coercivity and specific magnetic saturation of the pyrolyzed aerogels were 312 Oe and 114 emu/gCo, respectively. The elastic moduli of the supercritically dried, pyrolyzed, and thermally oxidized aerogels were 0.58, 1.1, and 14.3 MPa, respectively. The electrochemical testing of the pyrolyzed and thermally oxidized aerogels in 1 M KOH resulted in specific capacitances of 650 F/g and 349 F/g, respectively. The rapidly synthesized, low-cost, hydrogel-based synthesis for tunable transition metal multifunctional composite aerogels is envisioned for a wide range of porous metal electrodes to address energy storage, catalysis, and sensing applications.

Project description:The impact of selected cellulose solvent systems based on the principal constituents tetrabutylammonium fluoride (TBAF), 1-ethyl-3-methyl-1H-imidazolium-acetate, N-methylmorpholine-N-oxide, or calcium thiocyanate octahydrate (CTO) on the properties of cellulose II aerogels prepared from these solvent systems has been investigated as a means towards tailoring cellulose aerogel properties with respect to specific applications. Cotton linters were used as representative plant cellulose. Cellulose was coagulated from solutions with comparable cellulose content, and dried with supercritical carbon dioxide after solvent exchange. The resulting bulk aerogels were comprehensively morphologically and mechanically tested to relate structure and mechanical properties. Different solvent systems caused considerable differences in the properties of the bulk samples, such as internal surface area (nitrogen sorption), morphology, porosity (He pycnometry, thermoporosimetry), and mechanical stability (compression testing). The results of SAXS, WAXS, and solid-state 13C NMR spectroscopy suggest that this is due to different mechanisms of cellulose self-assembling on the supramolecular and nanostructural level, respectively, as reflected by the broad ranges of cellulose crystallinity, fibril diameter, fractal dimension and skeletal density. Both solid state NMR and WAXS experiments confirmed the sole existence of the cellulose II allomorph for all aerogels, with crystallinity reaching a maximum of 46-50 % for CTO-derived aerogels. Generally, higher fibril diameter, degree of crystallinity, hence increased skeletal density were associated with good preservation of shape and dimension throughout conversion of lyogels to aerogels, and enhanced mechanical stability, but somewhat reduced specific surface area. Amorphous, yet highly rigid aerogels derived from TBAF/DMSO mixtures deviated from this trend, most likely due to their particular homogeneous and nanostructured morphology.

Dataset Information

Comprehensive NMR Analysis of Pore Structures in Superabsorbing Cellulose Nanofiber Aerogels.

Publications

Comprehensive NMR Analysis of Pore Structures in Superabsorbing Cellulose Nanofiber Aerogels.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets