Influence of Different Surface Pretreatments on Shear Bond Strength of an Adhesive Resin Cement to Various Zirconia Ceramics.

ABSTRACT: The aim of this in vitro study was to assess the influence of surface pretreatment on shear bond strength (SBS) of an adhesive resin cement (G-CEM Link Force TM, GC Corporation, Tokyo, Japan) to three different yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramics: (1) Copran Zirconia Monolith HT, COP; (2) Katana ML Zirconia, KAT; and (3) Metoxit Z-CAD HTL Zirconia, MET. In total, 45 cylinders (5 mm in diameter, 1 mm height) for each type of zirconia ceramic were prepared used a computer-aided design and computer-aided manufacturing (CAD/CAM) machine (software CEREC 4.2). Each type of zirconia was subdivided into three groups and each group received a different surface pretreatment; 15 samples were not conditioned as control (groups COP 1, KAT 1, MET 1), 15 samples were air-borne particle abraded with aluminum dioxide particles of 50-?m size at 0.3 MPa for 20 s (groups COP 2, KAT 2, MET 2), and 15 samples were hot-etched with a solution of hydrochloric acid and ferric chloride (groups COP 3, KAT 3, MET 3). After specimen fabrication, the adhesive cement-ceramic interface was analyzed using an SBS test. Subsequently, the adhesive remnant index (ARI) was measured. Data were submitted to statistical analysis. Air-borne particle abraded specimens showed the highest SBS values for COP and KAT groups. For MET, no significant difference was reported between air-borne particle abraded specimens and untreated controls. The lowest values were detected for acid-etched groups. A higher frequency of ARI = "1" and ARI = "2" was reported in control and air-borne particle abraded groups, whereas ARI = "3" was detected in hot-etched groups. No correlation was found between ARI score and shear bond strength. Air-borne particle abrasion is considered the best treatment for Zirconia Copran and Zirconia Katana ML, if it is followed by using dual-curing resin cement.

SUBMITTER: Colombo M

PROVIDER: S-EPMC7040603 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Influence of Different Surface Pretreatments on Shear Bond Strength of an Adhesive Resin Cement to Various Zirconia Ceramics.

Colombo Marco M Gallo Simone S Padovan Sara S Chiesa Marco M Poggio Claudio C Scribante Andrea A

Materials (Basel, Switzerland) 20200201 3

The aim of this in vitro study was to assess the influence of surface pretreatment on shear bond strength (SBS) of an adhesive resin cement (G-CEM Link Force TM, GC Corporation, Tokyo, Japan) to three different yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramics: (1) Copran Zirconia Monolith HT, COP; (2) Katana ML Zirconia, KAT; and (3) Metoxit Z-CAD HTL Zirconia, MET. In total, 45 cylinders (5 mm in diameter, 1 mm height) for each type of zirconia ceramic were prepared used a ...[more]

PMID: 32024198

Similar Datasets

Project description:Background: The purpose of this study was to evaluate the effect of different bonding agents on bond-strength to demineralized enamel after remineralizing treatments and resin infiltration. Methods: Buccal enamel of 120 bovine incisors was polished and then were divided into five experimental groups: SE (sound enamel); DE (demineralized enamel); AS (demineralized enamel immersed in artificial saliva for eight weeks); NaF (demineralized enamel treated with 0.05% sodium fluoride solution (one minute) for eight weeks); Ic (demineralized enamel infiltrated with a low-viscosity resin (Icon-DGM). These groups were subdivided according to adhesive system used: self-etching adhesive Adper Easy One (3M/ESPE) and etch-and-rinse adhesive Single Bond (3M/ESPE). The composite resin blocks were fabricated using a Teflon matrix. A thermomechanical cycling machine was used to carry out the artificial aging of the specimens and thus were sectioned into sticks. The microtensile tests were performed using a universal testing machine at a cross-head speed of 1 mm/min. Data (in MPa) were subjected to two-way ANOVA and Tukey's tests (5%). Results: Significant differences were found for both factors tested and interactions (p<0.05). Tukey's test results of µTBS (mean ± SD) were: etch-and-rinse SE (28.79±3.93); DE (30.41±7.22); AS (29.03±3.33); NaF (29.81±4.06)a; Ic (29.47±5.5); and self-etching SE (30.37±6.96); DE (14.62±4.47); AS (9.79±2.32); NaF (9.36±2.31); Ic (30.78±8.68). Conclusions: Resin infiltration did not affect the bond strength of demineralized enamel for both adhesive systems tested. For etch-and-rinse adhesive, no differences were observed for the tested groups. For self-etching adhesive, only the resin-infiltrated group showed similar bond strength to sound enamel. Both etch-and-rinse and self-etching adhesive systems can be used in resin-infiltrated enamel, if a composite restoration needs to be further performed. In enamel that has undergone the de/remineralization process, the use of a total-etch adhesive might be preferable for the restorative procedure.

Dataset Information

Influence of Different Surface Pretreatments on Shear Bond Strength of an Adhesive Resin Cement to Various Zirconia Ceramics.

Publications

Influence of Different Surface Pretreatments on Shear Bond Strength of an Adhesive Resin Cement to Various Zirconia Ceramics.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets