Adhesive systems effect over bond strength of resin-infiltrated and de/remineralized enamel.

ABSTRACT: Background: The purpose of this study was to evaluate the effect of different bonding agents on bond-strength to demineralized enamel after remineralizing treatments and resin infiltration. Methods: Buccal enamel of 120 bovine incisors was polished and then were divided into five experimental groups: SE (sound enamel); DE (demineralized enamel); AS (demineralized enamel immersed in artificial saliva for eight weeks); NaF (demineralized enamel treated with 0.05% sodium fluoride solution (one minute) for eight weeks); Ic (demineralized enamel infiltrated with a low-viscosity resin (Icon-DGM). These groups were subdivided according to adhesive system used: self-etching adhesive Adper Easy One (3M/ESPE) and etch-and-rinse adhesive Single Bond (3M/ESPE). The composite resin blocks were fabricated using a Teflon matrix. A thermomechanical cycling machine was used to carry out the artificial aging of the specimens and thus were sectioned into sticks. The microtensile tests were performed using a universal testing machine at a cross-head speed of 1 mm/min. Data (in MPa) were subjected to two-way ANOVA and Tukey's tests (5%). Results: Significant differences were found for both factors tested and interactions (p<0.05). Tukey's test results of µTBS (mean ± SD) were: etch-and-rinse SE (28.79±3.93); DE (30.41±7.22); AS (29.03±3.33); NaF (29.81±4.06)a; Ic (29.47±5.5); and self-etching SE (30.37±6.96); DE (14.62±4.47); AS (9.79±2.32); NaF (9.36±2.31); Ic (30.78±8.68). Conclusions: Resin infiltration did not affect the bond strength of demineralized enamel for both adhesive systems tested. For etch-and-rinse adhesive, no differences were observed for the tested groups. For self-etching adhesive, only the resin-infiltrated group showed similar bond strength to sound enamel. Both etch-and-rinse and self-etching adhesive systems can be used in resin-infiltrated enamel, if a composite restoration needs to be further performed. In enamel that has undergone the de/remineralization process, the use of a total-etch adhesive might be preferable for the restorative procedure.

SUBMITTER: Borges AB

PROVIDER: S-EPMC6833993 | biostudies-literature | 2019

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Adhesive systems effect over bond strength of resin-infiltrated and de/remineralized enamel.

Borges Alessandra Buhler AB Abu Hasna Amjad A Matuda Amanda Guedes Nogueira AGN Lopes Stephanie Ribeiro SR Mafetano Ana Paula Valente Pinho APVP Arantes Aline A Duarte Angélica Ferreira AF Barcellos Daphne Camara DC Torres Carlos Rocha Gomes CRG Pucci Cesar Rogério CR

F1000Research 20191011

<b>Background:</b> The purpose of this study was to evaluate the effect of different bonding agents on bond-strength to demineralized enamel after remineralizing treatments and resin infiltration. <b>Methods:</b> Buccal enamel of 120 bovine incisors was polished and then were divided into five experimental groups: SE (sound enamel); DE (demineralized enamel); AS (demineralized enamel immersed in artificial saliva for eight weeks); NaF (demineralized enamel treated with 0.05% sodium fluoride solu ...[more]

PMID: 31723426

Similar Datasets

Project description:IntroductionRoot canal sealing materials play a crucial role in an endodontic procedure by forming a bond between the dentinal walls and the gutta-percha. The current study aims to analyse the dentinal tubule penetration and adhesive pattern, including the push-out bond strength of six commercially available root canal sealers.MethodologyEighty-four mandibular first premolars were split into seven groups (and n = 12), Group 1: Dia-Root, Group 2: One-Fil, Group 3: BioRoot RCS, Group 4: AH Plus, Group 5: CeraSeal, Group 6: iRoot SP, Group 7: GP without sealer (control). Two groups were made, one for dentinal tubule penetration and the other for push-out bond strength; the total sample size was one hundred sixty-eight. Root canal treatment was performed using a method called the crown down technique, and for obturation, the single cone technique was used. A confocal laser scanning microscope (Leica, Microsystem Heidel GmbH, Version 2.00 build 0585, Germany) was used to evaluate dentinal tubule penetration, and Universal Testing Machine was utilised to measure the push-out bond strength (Shimadzu, Japan) using a plunger size of 0.4 mm and speed of 1mm/min. Finally, the adhesive pattern of the sealers was analysed by HIROX digital microscope (KH-7700). Statistical analysis was carried out by a one-way Anova test, Dunnet's T3 test, and Chi-square test.ResultsHighest dentinal tubule penetration was noticed with One-Fil (p<0.05), followed by iRoot SP, CeraSeal, AH Plus, Dia-Root also, the most negligible value was recorded for BioRoot RCS. Meanwhile, BioRoot RCS (p<0.05) demonstrated the greater value of mean push-out bond strength, followed by One-fil, iRoot SP, CeraSeal, AH Plus and Dia-Root. Regarding adhesive pattern, most of the samples were classified as type 3 and type 4 which implies greater sealing ability and better adherence to the dentinal wall. However, BioRoot RCS revealed the most type 4 (p<0.05), followed by AH Plus, One-Fil, CeraSeal and Dia-Root.ConclusionThe highest dentinal tubule penetration was shown by One-Fil compared to other groups. Meanwhile, BioRoot RCS had greater push-out bond strength and more adhesive pattern than other tested materials.

Dataset Information

Adhesive systems effect over bond strength of resin-infiltrated and de/remineralized enamel.

Publications

Adhesive systems effect over bond strength of resin-infiltrated and de/remineralized enamel.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets