Load-displacement experimental data from axial tensile loading of CFRP-SPCC hybrid laminates.

ABSTRACT: The current paper shows a data set of load-displacement output from axial tensile loading of CFRP-SPCC hybrid laminates. The specimen geometries are cut based on standard procedure from ASTM D-3039. At least 3 positions in each specimen, we measured its width and thickness. Data of the load and displacement were repeated at least 3 samples in each combination of hybrid laminates. Tensile test was conducted with a 1 mm/min of loading rate. The data were recorded from unloading until failure of specimens. The data gives information about the highest load and the behavior of load-displacement in axial tensile loading. By using width and thickness, normalized data can be obtained, the load can be calculated into stress (MPa) unit. The data are useful for researchers and structural engineers that deals with CFRP, SPCC, and hybrid CFRP-SPCC laminates.

SUBMITTER: Muflikhun MA

PROVIDER: S-EPMC7058899 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Load-displacement experimental data from axial tensile loading of CFRP-SPCC hybrid laminates.

Muflikhun Muhammad Akhsin MA Chua Alvin Y AY

Data in brief 20200219

The current paper shows a data set of load-displacement output from axial tensile loading of CFRP-SPCC hybrid laminates. The specimen geometries are cut based on standard procedure from ASTM D-3039. At least 3 positions in each specimen, we measured its width and thickness. Data of the load and displacement were repeated at least 3 samples in each combination of hybrid laminates. Tensile test was conducted with a 1 mm/min of loading rate. The data were recorded from unloading until failure of sp ...[more]

PMID: 32154344

Similar Datasets

Experimental data on fracture of open-hole composite laminates subjected to tension loading.

Project description:In this data article, we present detailed failure process of big open-hole carbon fibre reinforced polymer (CFRP) composite laminates subjected to tension loading, which are tested by digital image correlation (DIC) system and electrical strain gauge system. In experiments, three different lay-ups are applied tension loading until specimens' failure. Several strain gages are distributed in different locations of specimens to measure strains during loading, at the same time, DIC is adopted to obtain field strains of specimens. The maximum force and failure modes of different lay-ups composite laminates are tested. The failure process is displayed by strain field images, and final failure images are also supplied in this article. Detailed numerical analysis are reported in [1].

| S-EPMC8010642 | biostudies-literature

Dataset for surface and internal damage after impact on CFRP laminates.

Project description:Various foreign objects can collide with CFRP structures, such as CFRP aircraft. Once something impacts with CFRP laminates, both surface damage and internal damage can occur. Even if the external damage is such invisible as called barely visible impact damage, there are matrix cracks or delamination that are the main cause of compressive strength reduction, so it is difficult to find the relationship between external and internal damage on CFRP laminates. This dataset is prepared for predicting impact information only from surface damage profiles using Machine Learning (Hasebe et al., 2022). It includes three data, surface damage image (png), surface depth contour image(png), and internal damage image after ultrasound C-scanning (jpg) after low-velocity impact testing under various impact conditions. The data are helpful for researchers and engineers who deal with the impact behavior of CFRP or data science.

| S-EPMC9294053 | biostudies-literature

Modelling of stiffness degradation due to cracking in laminates subjected to multi-axial loading.

Project description:The paper presents an analytical approach to predicting the effect of intra- and interlaminar cracking on residual stiffness properties of the laminate, which can be used in the post-initial failure analysis, taking full account of damage mode interaction. The approach is based on a two-dimensional shear lag stress analysis and the equivalent constraint model of the laminate with multiple damaged plies. The application of the approach to predicting degraded stiffness properties of multidirectional laminates under multi-axial loading is demonstrated on cross-ply glass/epoxy and carbon/epoxy laminates with transverse and longitudinal matrix cracks and crack-induced transverse and longitudinal delaminations. This article is part of the themed issue 'Multiscale modelling of the structural integrity of composite materials'.

| S-EPMC4901253 | biostudies-other

Theoretical nonlinear response of complex single crystal under multi-axial tensile loading.

Project description:The mechanical properties of single crystals are of interest as they represent the behavior of the basic building blocks. Using the density functional theory based ab initio technique we have devised an approach to analyze the behavior of single crystal so their mechanical properties can be studied beyond linear elasticity. Here we have applied the approach to investigate the mechanical properties of a single stoichiometric hydroxyapatite (HAP) crystal using a large supercell subjected to multi-axial tensile loading. The results reveal a complex nonlinear and loading-path dependent behavior with evolving anisotropy for the HAP crystal. Further, we have introduced a failure envelope index to quantify the strength behavior for comparison of similar materials. We have found that the complexities of the behavior of a single crystal originate from the local structural changes in these multi-component materials.

| S-EPMC3601370 | biostudies-other

Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates.

Project description:Many body armor designs incorporate unidirectional (UD) laminates. UD laminates are constructed of thin (<0.05 mm) layers of high-performance yarns, where the yarns in each layer are oriented parallel to each other and held in place using binder resins and thin polymer films. The armor is constructed by stacking the unidirectional layers in different orientations. To date, only very preliminary work has been performed to characterize the ageing of the binder resins used in unidirectional laminates and the effects on their performance. For example, during the development of the conditioning protocol used in the National Institute of Justice Standard-0101.06, UD laminates showed visual signs of delamination and reductions in V50, which is the velocity at which half of the projectiles are expected to perforate the armor, after ageing. A better understanding of the material property changes in UD laminates is necessary to comprehend the long-term performance of armors constructed from these materials. There are no current standards recommended for mechanically interrogating unidirectional (UD) laminate materials. This study explores methods and best practices for accurately testing the mechanical properties of these materials and proposes a new test methodology for these materials. Best practices for ageing these materials are also described.

| S-EPMC7485147 | biostudies-literature

Tensile Testing of Aged Flexible Unidirectional Composite Laminates for Body Armor.

Project description:Flexible Unidirectional (UD) composite laminates are commonly being used for ballistic-resistant body armor. These laminates comprise UD layers, each constructed by laminating thin layers of high-performance fibers held in place using very low modulus binder resins, with the fibers in each layer oriented parallel to each other. As these materials are used in body armor, it is important to investigate their long-term reliability, particularly with regards to exposure to temperature and humidity as these are known causes of degradation in other commonly used body armor materials. This work investigates the tensile behavior of a poly(p-phenylene terephthalamide), or PPTA flexible UD laminate aged for up to 150 d at accelerated conditions of 70 °C and 76 % relative humidity (RH). Tests were performed at three different crosshead displacement rates and three different gauge lengths. The effect of ageing on the mechanical properties of the material resulted in less than 10 % degradation in tensile strength, with a more significant reduction in longer specimens when tested at slower rates.

| S-EPMC7542579 | biostudies-literature

Effects of the Electrophoretic Deposition of CNTs on the Mechanical Properties of Ti/CFRP Composite Laminates.

Project description:The interfacial performance between metals and resins significantly affects the mechanical properties of fiber-metal laminates. In this study, CNTs were deposited on a titanium surface via electrophoretic deposition (EPD) to improve the interfacial performance of Ti/carbon fiber-reinforced polymer composite laminates. Before EPD, the titanium plates were treated by either sandblasting, anodizing, or sandblasting/anodizing. A macroscopically rough surface and an oxide layer were formed by sandblasting and anodizing, then CNTs were deposited, and a porous layer was obtained, which improved the wettability and bonding strength. Finally, the static mechanical properties (single-lap properties, bending properties, and interlaminar shear properties) and dynamic mechanical properties (impact resistance) of the laminates were systematically explored. The introduction of CNTs played an important role in dispersing and carrying loads and providing a strong crack propagation resistance, which improved the laminates' static mechanical properties and reduced the delamination damage under dynamic impact. Compared with the original composite laminates, the bond strength, bending strength, and interlaminar shear strength of the laminates deposited with CNTs after sandblasting were increased by 117.94, 46.85, and 145.61%, respectively. When the impact energy was 35 J, the damage area of the composite laminate deposited with CNTs was decreased by 27.75%.

| S-EPMC8757327 | biostudies-literature

The effect of different levels of pre-damage loading on the strength and structural behavior of CFRP strengthened R.C. beams: Experimental and analytical investigation.

Project description:In order to investigate the effect of pre-loading damage on the structural performance of Carbon Fiber Reinforced Polymer (CFRP) strengthened Reinforced Concrete (R.C.) beams, experimental and Finite Element Modelling (FEM) investigation was carried out on six R.C. beams. Five of the R.C. beams were damaged up to different levels of strain in the main steel bars before Flexure CFRP strengthening. One of the R.C. beams loaded up to failure and was kept as a control beam for comparison. The experimental results showed that the failure mode of the CFRP strengthened specimen was controlled by CFRP debonding followed by concrete crushing; however, the control beam failed in concrete crushing after yielding the steel bars, which is a ductile failure. The CFRP sheet increases the strength and initial stiffness of the R.C. beams and reduces ductility and toughness. Also, CFRP application increases the first crack and yielding steel bars load by 87.4% and 34.4%, respectively. Furthermore, the pre-damage level does not influence the strength and ductility of the strengthened R.C. beams except for the highest damage levels, which experienced a slight decrease in load capacity and ductility. However, the initial stiffness decreases with increasing pre-damage levels by 40%. Design guideline ACI 440.2R (2004) predicts the ultimate load capacity marvelously for externally bonded Fiber-Reinforced Polymer (FRP) beams compared to the experimental maximum load capacity. The excellent agreement between experimental and FEM results indicates that the constitutive models used for concrete and reinforcement and the cohesive interface model can well capture fracture behavior. However, The FEM analysis predicts the beam to be slightly stiffer and more robust, probably because of the assumed perfect bond between concrete and reinforcement. The developed FEM can be used for further parametric study.

| S-EPMC8717972 | biostudies-literature

Stiffening of the nucleus pulposus upon axial loading of the intervertebral disc: An experimental in situ study.

Project description:Mechanical loading is inherently related to the function and degeneration of the intervertebral disc. We present a series of experiments aimed at measuring the effect of a loading/unloading cycle of the intervertebral disc on the mechanical properties of the nucleus pulposus. The study relies on our new minimally invasive microindenter, which allows us to quantify the storage and loss moduli of the nucleus pulposus by inserting an optomechanical probe in an intact (resected) intervertebral disk through the annulus fibrosis via a small needle. Our results indicate that, under the influence of compressive loading, the nucleus pulposus exhibits a more solid-like behavior.

| S-EPMC6686818 | biostudies-literature

Transcriptome analysis of human periodontal ligament cells under tensile loading

Project description:This study explored the expression profiles of messenger RNAs (mRNAs) and long non-coding RNAs (lncRNAs) in human periodontal ligament (PDL) cells subjected to tensile loading.

2021-12-08 | GSE173891 | GEO

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data