Effects of the Electrophoretic Deposition of CNTs on the Mechanical Properties of Ti/CFRP Composite Laminates.

ABSTRACT: The interfacial performance between metals and resins significantly affects the mechanical properties of fiber-metal laminates. In this study, CNTs were deposited on a titanium surface via electrophoretic deposition (EPD) to improve the interfacial performance of Ti/carbon fiber-reinforced polymer composite laminates. Before EPD, the titanium plates were treated by either sandblasting, anodizing, or sandblasting/anodizing. A macroscopically rough surface and an oxide layer were formed by sandblasting and anodizing, then CNTs were deposited, and a porous layer was obtained, which improved the wettability and bonding strength. Finally, the static mechanical properties (single-lap properties, bending properties, and interlaminar shear properties) and dynamic mechanical properties (impact resistance) of the laminates were systematically explored. The introduction of CNTs played an important role in dispersing and carrying loads and providing a strong crack propagation resistance, which improved the laminates' static mechanical properties and reduced the delamination damage under dynamic impact. Compared with the original composite laminates, the bond strength, bending strength, and interlaminar shear strength of the laminates deposited with CNTs after sandblasting were increased by 117.94, 46.85, and 145.61%, respectively. When the impact energy was 35 J, the damage area of the composite laminate deposited with CNTs was decreased by 27.75%.

SUBMITTER: Hu Y

PROVIDER: S-EPMC8757327 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Dataset on mechanical properties of damaged fibre composite laminates with drilled vent-holes for resin-injection repair procedure.

Project description:This dataset comprises the mechanical properties of pristine and barely visible impact damaged (BVID) carbon fibre reinforced epoxy composite (CFRP) laminates. The mechanical dataset describes the compressive strength, compressive strain at fracture, strain energy density for resilience and strain energy density to fracture of the CFRP laminates with different number of vent holes (namely 4, 5 and 6) in the respective pristine and BVID states. The vent holes were created in the laminate to facilitate the resin-injection repair process. The mechanical properties were determined from in-plane compression test of the CFRP laminates. Structure-related dataset, namely infrared thermographs and ultrasonic C-scan images of BVID and other damage features induced by mechanical drilling, are included for completeness.

| S-EPMC6488824 | biostudies-literature

Dataset for surface and internal damage after impact on CFRP laminates.

Project description:Various foreign objects can collide with CFRP structures, such as CFRP aircraft. Once something impacts with CFRP laminates, both surface damage and internal damage can occur. Even if the external damage is such invisible as called barely visible impact damage, there are matrix cracks or delamination that are the main cause of compressive strength reduction, so it is difficult to find the relationship between external and internal damage on CFRP laminates. This dataset is prepared for predicting impact information only from surface damage profiles using Machine Learning (Hasebe et al., 2022). It includes three data, surface damage image (png), surface depth contour image(png), and internal damage image after ultrasound C-scanning (jpg) after low-velocity impact testing under various impact conditions. The data are helpful for researchers and engineers who deal with the impact behavior of CFRP or data science.

| S-EPMC9294053 | biostudies-literature

Effects of Ti Target Purity and Microstructure on Deposition Rate, Microstructure and Properties of Ti Films.

Project description:Three titanium (Ti) targets with different purities were used to prepare Ti films on polyimide substrates by DC magnetron sputtering. The microstructures of Ti films were characterized by a metallographic microscope, X-ray diffractometer, field emission scanning electron microscope and three-dimensional surface topography instrument. In this study, we investigated the effects of Ti target purity and microstructure on film deposition rate, surface roughness, microstructure and resistivity. The results show that the deposition rate increased with increasing Ti target purity. Ti film deposited by the high-purity (99.999%) Ti target has fewer surface particles with smaller size, lower surface roughness and lower resistivity when compared to that prepared by the Ti target of low purity (99.7%). The surface roughness of Ti film prepared by the high-purity Ti target was Sa = 121 nm, the deposition rate was 16.3 nm/min and the resistivity was 6.9 × 10-6 Ω·m. For Ti targets of the same purity, the performance of Ti film prepared by a target with equiaxed α-phase grains is better than that of Ti film prepared by a target with twins and β-phase grains.

| S-EPMC9000231 | biostudies-literature

Cutting Modeling of Hybrid CFRP/Ti Composite with Induced Damage Analysis.

Project description:In hybrid carbon fiber reinforced polymer (CFRP)/Ti machining, the bi-material interface is the weakest region vulnerable to severe damage formation when the tool cutting from one phase to another phase and vice versa. The interface delamination as well as the composite-phase damage is the most serious failure dominating the bi-material machining. In this paper, an original finite element (FE) model was developed to inspect the key mechanisms governing the induced damage formation when cutting this multi-phase material. The hybrid composite model was constructed by establishing three disparate physical constituents, i.e., the Ti phase, the interface, and the CFRP phase. Different constitutive laws and damage criteria were implemented to build up the entire cutting behavior of the bi-material system. The developed orthogonal cutting (OC) model aims to characterize the dynamic mechanisms of interface delamination formation and the affected interface zone (AIZ). Special focus was made on the quantitative analyses of the parametric effects on the interface delamination and composite-phase damage. The numerical results highlighted the pivotal role of AIZ in affecting the formation of interface delamination, and the significant impacts of feed rate and cutting speed on delamination extent and fiber/matrix failure.

| S-EPMC5456579 | biostudies-other

Load-displacement experimental data from axial tensile loading of CFRP-SPCC hybrid laminates.

Project description:The current paper shows a data set of load-displacement output from axial tensile loading of CFRP-SPCC hybrid laminates. The specimen geometries are cut based on standard procedure from ASTM D-3039. At least 3 positions in each specimen, we measured its width and thickness. Data of the load and displacement were repeated at least 3 samples in each combination of hybrid laminates. Tensile test was conducted with a 1 mm/min of loading rate. The data were recorded from unloading until failure of specimens. The data gives information about the highest load and the behavior of load-displacement in axial tensile loading. By using width and thickness, normalized data can be obtained, the load can be calculated into stress (MPa) unit. The data are useful for researchers and structural engineers that deals with CFRP, SPCC, and hybrid CFRP-SPCC laminates.

| S-EPMC7058899 | biostudies-literature

Synthesis and Mechanical Characterisation of an Ultra-Fine Grained Ti-Mg Composite.

Project description:The importance of lightweight materials such as titanium and magnesium in various technical applications, for example aerospace, medical implants and lightweight construction is well appreciated. The present study is an attempt to combine and improve the mechanical properties of these two materials by forming an ultra-fine grained composite. The material, with a composition of 75 vol% (88.4 wt%) Ti and 25 vol% (11.4 wt%) Mg , was synthesized by powder compression and subsequently deformed by high-pressure torsion. Using focused ion beam machining, miniaturised compression samples were prepared and tested in-situ in a scanning electron microscope to gain insights into local deformation behaviour and mechanical properties of the nanocomposite. Results show outstanding yield strength of around 1250 MPa, which is roughly 200 to 500 MPa higher than literature reports of similar materials. The failure mode of the samples is accounted for by cracking along the phase boundaries.

| S-EPMC5512354 | biostudies-literature

Poly(ether ether ketone)-Grafted Graphene Oxide "Interconnects" Enhance Mechanical, Dynamic Mechanical, and Flame-Retardant Properties in Epoxy Laminates.

Project description:Herein, the interface of epoxy and graphene oxide (GO) is tailored through hydroxylated poly(ether ether ketone) (HPEEK). The resultant modification (HPEEK-g-GO) improved the interfacial adhesion between epoxy and carbon fiber (CF) in the laminates. This strategy resulted in improved tensile strength, modulus, and storage modulus by 8, 10, and 26%, respectively, with respect to control samples (epoxy/CF laminates). The HPEEK-g-GO was thoroughly characterized using spectroscopic techniques and was infused using vacuum-enhanced resin infusion technology into the epoxy/CF laminates. To address the challenges involved with primary agglomeration, the composite formulation was subjected to mechanical stirring coupled with bath sonication throughout the mixing process. The improved structural properties in epoxy/CF laminates were attributed to HPEEK-g-GO "interconnects", which provided the necessary reinforcement owing to better interfacial adhesion with the CF mat as inferred from the fracture surface morphology assessed using SEM. In addition, the epoxy laminates containing HPEEK-g-GO also showed flame-retardant properties along with good thermal stability. The electromagnetic interference shielding capability of the modified laminates was also evaluated in the frequency range of 12-18 GHz. It was observed that the laminates exhibited a shielding effectiveness of -50 dB. Thus, this strategy offers some promise in fabricating epoxy/CF laminates with multifunctional properties through HPEEK-g-GO "interconnects".

| S-EPMC6643512 | biostudies-literature

Green's functions for unsymmetric composite laminates with inclusions.

Project description:It is known that the stretching and bending deformations will be coupled together for the unsymmetric composite laminates under in-plane force and/or out-of-plane bending moment. Although Green's functions for unsymmetric composite laminates with elliptical elastic inclusions have been obtained by using Stroh-like formalism around 10 years ago, due to the ignoring of inconsistent rigid body movements of matrix and inclusion, the existing solution may lead to displacement discontinuity across the interface between matrix and inclusion. Due to the multi-valued characteristics of complex logarithmic functions appeared in Green's functions, special attention should be made on the proper selection of branch cuts of mapped variables. To solve these problems, in this study, the existing Green's functions are corrected and a simple way to correctly evaluate the mapped complex variable logarithmic functions is suggested. Moreover, to apply the obtained solutions to boundary element method, we also derive the explicit closed-form solution for Green's function of deflection. Since the continuity conditions along the interface have been satisfied in Green's functions, no meshes are required along the interface, which will save a lot of computational time and the results are much more accurate than any other numerical methods.

| S-EPMC7016552 | biostudies-literature

Thermal Mechanical Processing Effects on Microstructure Evolution and Mechanical Properties of the Sintered Ti-22Al-25Nb Alloy.

Project description:This work illustrates the effect of thermal mechanical processing parameters on the microstructure and mechanical properties of the Ti-22Al-25Nb alloy prepared by reactive sintering with element powders, consisting of O, B2 and Ti₃Al phases. Tensile and plane strain fracture toughness tests were carried out at room temperature to understand the mechanical behavior of the alloys and its correlation with the microstructural features characterized by scanning and transmission electron microscopy. The results show that the increased tensile strength (from 340 to 500 MPa) and elongation (from 3.6% to 4.2%) is due to the presence of lamellar O/B2 colony and needle-like O phase in B2 matrix in the as-processed Ti-22Al-25Nb alloys, as compared to the coarse lath O adjacent to B2 in the sintered alloys. Changes in morphologies of O phase improve the fracture toughness (KIC) of the sintered alloys from 7 to 15 MPa·m-1/2. Additionally, the fracture mechanism shifts from cleavage fracture in the as-sintered alloys to quasi-cleavage fracture in the as-processed alloys.

| S-EPMC5456733 | biostudies-other

Electrophoretic Deposition of Chitosan/45S5 Bioactive Glass Composite Coatings Doped with Zn and Sr.

Project description:In this research work, the original 45S5 bioactive glass was modified by introducing zinc and/or strontium oxide (6?mol%) in place of calcium oxide. Sr was added for its ability to stimulate bone formation and Zn for its role in bone metabolism, antibacterial properties, and anti-inflammatory effect. The glasses were produced by means of melting and quenching process. SEM and XRD analyses evidenced that Zr and Sr introduction did not modify the glass structure and morphology while compositional analysis (EDS) demonstrated the effective incorporation of these elements in the glass network. Bioactivity test in simulated body fluid (SBF) up to 1?month evidenced a reduced bioactivity kinetics for Zn-doped glasses. Doped glasses were combined with chitosan to produce organic/inorganic composite coatings on stainless steel AISI 316L by electrophoretic deposition (EPD). Two EPD processes were considered for coating development, namely direct current EPD (DC-EPD) and alternating current EPD (AC-EPD). The stability of the suspension was analyzed and the deposition parameters were optimized. Tape and bending tests demonstrated a good coating-substrate adhesion for coatings containing 45S5-Sr and 45S5-ZnSr glasses, whereas the adhesion to the substrate decreased by using 45S5-Zn glass. FTIR analyses demonstrated the composite nature of coatings and SEM observations indicated that glass particles were well integrated in the polymeric matrix, the coatings were fairly homogeneous and free of cracks; moreover, the AC-EPD technique provided better results than DC-EPD in terms of coating quality. SEM, XRD analyses, and Raman spectroscopy, performed after bioactivity test in SBF solution, confirmed the bioactive behavior of 45S5-Sr-containing coating while coatings containing Zn exhibited no hydroxyapatite formation.

| S-EPMC4609893 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data