Comparison of Enamel Preparations - Bevel, Chamfer and Stair Step Chamfer on Fracture Resistance of Nano Filled Resin Composites Using Bulk Pack Technique - An In Vitro Study.

ABSTRACT: AIM:To evaluate and compare the effect of enamel preparation designs bevel, chamfer and stair-step chamfer on the fracture resistance of nanocomposite. METHODS:The sample group of this study consisted of 72 non-carious permanent maxillary central incisors. The sample is divided into four groups of 18 each. Group, I control Group II bevel preparation, Group III chamfer preparation, group IV stair step chamfer preparation. After the specific preparation, each tooth is filled with nanocomposite using bulk pack technique. The teeth were subjected to fracture resistance test under Universal testing machine and then were examined under a stereomicroscope to evaluate the type of bond failure. The results were subjected to statistical analysis. RESULTS:Results of the One-Way ANOVA revealed a significant difference in the mean peak failure load values of the four different groups. (P < 0.001) Tukey's Post-Hoc comparison test revealed that there was a significant difference in the mean peak failure load values of the bevel and chamfer preparation. But there was no significant difference between chamfer and stair-step chamfer preparation designs. CONCLUSION:Stair-step chamfer preparation demonstrated comparable values to Chamfer preparation but also involved the removal of less amount of tooth structure adjacent to the fractured edge and good esthetic technique.

SUBMITTER: Bommanagoudar J

PROVIDER: S-EPMC7061382 | biostudies-literature | 2019 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Comparison of Enamel Preparations - Bevel, Chamfer and Stair Step Chamfer on Fracture Resistance of Nano Filled Resin Composites Using Bulk Pack Technique - An In Vitro Study.

Bommanagoudar Jyothi J Chandrashekhar Shashidhar S Sharma Shilpa S Jain Hiten H

Open access Macedonian journal of medical sciences 20191210 23

<h4>Aim</h4>To evaluate and compare the effect of enamel preparation designs bevel, chamfer and stair-step chamfer on the fracture resistance of nanocomposite.<h4>Methods</h4>The sample group of this study consisted of 72 non-carious permanent maxillary central incisors. The sample is divided into four groups of 18 each. Group, I control Group II bevel preparation, Group III chamfer preparation, group IV stair step chamfer preparation. After the specific preparation, each tooth is filled with na ...[more]

PMID: 32165958

Similar Datasets

Project description:The design and development of thermal insulation materials is very important for the treatment of offshore oil pipelines. Understanding thermal energy transport in thermal insulation materials and predicting their thermal conductivities have important theoretical and practical value for the design of thermal insulation materials. In this work, lightweight and thermally insulated (LWTI) composites with the desired mechanical strength for offshore oil pipelines applications were prepared using epoxy resin (EP) as the matrix and hollow glass microspheres (HGMs) as the filler. The morphology, density, and mechanical properties of HGM/EP LWTI composites were studied first. The flexural strength and the flexural modulus of HGM/EP LWTI composites could still be as high as 22.34 ± 2.75 Mpa and 1.34 ± 0.03 GPa, respectively, while the density was only 0.591 g/cm3. The relationship between the effective thermal conductivity of HGM/EP LWTI composites and material parameters (sizes and contents together) has been studied systematically. A three-phase prediction model was built using the self-consistent approximation method to predict the effective thermal conductivity of HGM/EP LWTI composites, and the resin matrix, the wall thickness, the HGM particle size, and other parameters (such as air) were fully considered during the derivation of this three-phase thermal conductivity model. Finally, the insulation mechanism of HGM/EP LWTI composites was systematically analyzed. The thermal conductivities of HGM/EP LWTI composites with different diameters and HGM contents calculated by the three-phase prediction model agreed well with the experimental test results, with a minimum error of only 0.69%. Thus, this three-phase thermal conductivity model can be used to theoretically simulate the thermal conductivity of epoxy resin-based LWTI composites and can be the theoretical basis for the design and prediction of the thermal conductivity of other similar hollow spheres filled materials.

Project description:BackgroundDespite recent advances in restorative dentistry adhesive restorations may cause postoperative sensitivity which leads to restoration failure.AimThis study aimed to compare and evaluate the incremental and bulk fill resin Composite postoperative sensitivity in class II posterior restorations bonded with two adhesive systems (self-etch and etch-and-rinse).MethodsSixty patients were randomly selected, their age range from twenty-five to forty years old, divided into two groups according to the packing technique of resin composite material; incremental Tetric Evoceram and Tetric Evoceram bulk-fill resin composite. Thirty patients (n = 30) for incremental Tetric Evoceram resin composite restorations and according to the adhesive systems used they were equally divided (n = 15 teeth).Thirty patients (n = 30) for Tetric Evoceram bulk-fill resin composite restorations and according to the adhesive systems used (etch and rinse or self-etch), they were equally divided (n = 15 teeth). Post-operative pain assessed at 24 hours, 1 week and 1 month using the Visual Analog Scale Score (VAS). Each patient was instructed to put a mark on the VAS line at home to point out the intensity of pain at each assessment period. The problem of measuring the pain that pain tolerance of individuals may be different from the others. This may be due to different reasons, and it is not always because of a problem in the restoration.ResultsAfter 1 day, 1 week as well as 1 month, no statistically significant disagreement between the two resin composite types using self-etch adhesive strategy and total-etch adhesive strategy. Also, when the two adhesive systems were compared using Bulk Fill resin composite and incremental Nano resin composite no statistically significant disagreement between the two adhesive systems after 1 day, 1 week as well as 1 month.ConclusionThe post-operative hypersensitivity is related to many factors as the procedure of cavity preparation, adhesive approach, and type of resin composite used and placement technique of the resin composite.

Project description:The studies focusing on magnesium oxychloride cement (MOC) composites have recently become fairly widespread because of MOC's excellent mechanical properties and environmental sustainability. Numerous fillers, admixtures and nano-dopants were studied in order to improve the overall performance of MOC-based derivatives. Some of them exhibited specific flaws, such as a tendency to aggregate, increase in porosity, aeration of the composite matrix, depreciation in water resistance and mechanical strength, etc. In this manuscript, MOC-based composites doped by multi-walled carbon nanotubes (MWCNTs) are designed and tested. In order to modify the final properties of composites, diatomite was admixed as partial substitution of MgO, which was used in the composition of the researched material in excess, i.e., the majority of MgO constituted part of MOC and the rest served as fine filler. The composites were subjected to the broad experimental campaign that covered SEM (scanning electron microscopy), EDS (energy dispersive spectroscopy), HR-TEM (high-resolution transmission electron microscopy), XRD (X-ray diffraction), OM (optical microscopy) and STA-MS (simultaneous thermal analysis with mass spectroscopy). For 28 days hardened samples, macrostructural and microstructural parameters, mechanical properties, hygric and thermal characteristics were experimentally assessed. The incorporation of MWCNTs and diatomite resulted in the significant enhancement of composites' compactness, mechanical strength and stiffness and reduction in water absorption and rate of water imbibition. The thermal properties of the enriched MOC composites yielded interesting values and provided information for future modification of thermal performance of MOC composites with respect to their specific use in practice, e.g., in passive moderation of indoor climate. The combination of MWCNTs and diatomite represents a valuable modification of the MOC matrix and can be further exploited in the design and development of advanced building materials and components.

Project description:BackgroundIt has been demonstrated that dental restorations with rough surfaces can have several disadvantages such as pigment retention or plaque accumulation, which can facilitate caries formation, color variation, loss of brightness, degradation of restoration, among others. The present study aimed to assess surface roughness in bulk fill and conventional nanohybrid resins with and without polishing, controlling the oxygen inhibited layer.MethodsThis in vitro and longitudinal experimental study consisted of 120 resin blocks of 6 mm diameter and 4 mm depth, divided into two groups: Bulk Fill (Tetric® N-Ceram Bulk-fill, Opus Bulk Fill APS, Filtek™ Bulk Fill) and conventional nanohybrid (Tetric® N-Ceram, Opallis EA2, Filtek™ Z250 XT). Each resin group was divided into two equal parts, placing glycerin only on one of them, in order to control the oxygen inhibited layer. Subsequently, the surface roughness was measured before and after the polishing procedure with Sof-Lex discs. The data were analyzed with the T-test for related measures, and for comparison between groups before and after polishing, the non-parametric Kruskal Wallis test with the Bonferroni post hoc was used, considering a significance level of p < 0.05.ResultsBefore polishing, the resin composites with the lowest surface roughness were Opus Bulk Fill APS (0.383 ± 0.186 µm) and Opallis EA2 (0.430 ± 0. 177 µm) with and without oxygen inhibited layer control, respectively; while after polishing, those with the lowest surface roughness were Opus Bulk Fill APS (0.213 ± 0.214 µm) and Tetric N-Ceram (0.097 ± 0.099 µm), with and without oxygen inhibited layer control, respectively. Furthermore, before and after polishing, all resins significantly decreased their surface roughness (p < 0.05) except Opus Bulk Fill APS resin with oxygen inhibited layer control (p = 0.125). However, when comparing this decrease among all groups, no significant differences were observed (p < 0.05).ConclusionThe Opus Bulk Fill APS resin with oxygen inhibited layer control presented lower surface roughness both before and after polishing, being these values similar at both times. However, after polishing the other bulk fill and conventional nanohybrid resins with and without oxygen inhibited layer control, the surface roughness decreased significantly in all groups, being this decrease similar in all of them.

Dataset Information

Comparison of Enamel Preparations - Bevel, Chamfer and Stair Step Chamfer on Fracture Resistance of Nano Filled Resin Composites Using Bulk Pack Technique - An In Vitro Study.

Publications

Comparison of Enamel Preparations - Bevel, Chamfer and Stair Step Chamfer on Fracture Resistance of Nano Filled Resin Composites Using Bulk Pack Technique - An In Vitro Study.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure