Evaluation of the Surface Characteristics of Dental CAD/CAM Materials after Different Surface Treatments.

ABSTRACT: Computer-aided design/computer-aided manufacturing (CAD/CAM) technology was developed to ensure the sufficient strength of tooth restorations, to improve esthetic restorations with a natural appearance and to make the techniques easier, faster and more accurate. In the view of the limited research on the surface treatments of the CAD/CAM materials and the need to evaluate the ideal surface characteristics of a material to achieve the best adhesion to tooth tissues, this study aimed to investigate the surface roughness and morphology of four different CAD/CAM materials using four different surface treatments. The CAD/CAM materials used in this study were three composites (Shofu Block HC, Lava Ultimate and Brilliant Crios) and a hybrid ceramic (Enamic). The surface of the specimens of each material received one of the following treatments: no surface treatment, sandblasting with 29 ?m Al2O3 particles, 9% hydrofluoric acid etching and silane application, and the tribochemical method using CoJet System. Surface roughness was evaluated using optical profilometry, and surface morphology was observed by means of scanning electron microscopy. All surface treatments resulted in higher surface roughness values compared to the control group. Different treatments affected the surface properties of the materials, presumably due to discrepancies in their composition and structure.

SUBMITTER: Papadopoulos K

PROVIDER: S-EPMC7078785 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Evaluation of the Surface Characteristics of Dental CAD/CAM Materials after Different Surface Treatments.

Papadopoulos Konstantinos K Pahinis Kimon K Saltidou Kyriaki K Dionysopoulos Dimitrios D Tsitrou Effrosyni E

Materials (Basel, Switzerland) 20200222 4

Computer-aided design/computer-aided manufacturing (CAD/CAM) technology was developed to ensure the sufficient strength of tooth restorations, to improve esthetic restorations with a natural appearance and to make the techniques easier, faster and more accurate. In the view of the limited research on the surface treatments of the CAD/CAM materials and the need to evaluate the ideal surface characteristics of a material to achieve the best adhesion to tooth tissues, this study aimed to investigat ...[more]

PMID: 32098305

Similar Datasets

Project description:The advancement of intraoral scanners has allowed for more efficient workflow in the dental clinical setting. However, limited data exist regarding the accuracy of the digital impressions produced with various scanner settings and scanning approaches. The purpose of this in vitro study was to compare the accuracy of digital impressions at the crown preparation margin using different scanning resolutions of a specific intraoral scanner system. An all-ceramic crown preparation of a mandibular first molar was constructed in a typodont, and a scan (n = 3) was created with an industrial-grade laboratory scanner (3Shape D2000) as the control. Digital impressions were obtained with an intraoral scanner (3Shape TRIOS 3) under three settings-high resolution (HR), standard resolution (SR), and combined resolution (SHR). Comparative 3D analysis of scans was performed with Geomagic Control X software to measure the discrepancy between intraoral scans and the control scan along the preparation finish line. The scan time and number of images captured per scan were recorded. Statistical analysis was performed by one-way ANOVA, two-way repeated measures ANOVA, Pearson's correlation, and Dunnett's T3 test (? = 0.05). Significant differences were observed for scan time and for number of images captured among scan resolution settings (? < 0.05). The scan time for the SR group was, on average, 34.2 s less than the SHR group and 46.5 s less than the HR group. For discrepancy on the finish line, no significant differences were observed among scanning resolutions (HR: 31.5 ± 5.5 ?m, SHR: 33.2 ± 3.7 ?m, SR: 33.6 ± 3.1 ?m). Significant differences in discrepancy were observed among tooth surfaces, with the distal surface showing the highest discrepancies. In conclusion, the resolution of the intra-oral scanner is primarily defined by the system hardware and optimized for default scans. A software high-resolution mode that obtains more data over a longer time may not necessarily benefit the scan accuracy, while the tooth preparation and surface parameters do affect the accuracy.

Project description:PurposeTo assess and compare the impact of various computers aided design/manufacturing (CAD/CAM) materials on internal and marginal discrepancies, fracture resistance and failure probability of Endocrown restorations with 3D Finite Element analysis.Material and methodsForty devitalized human maxillary first molars were collected. After endodontic treatment, they classified into 4 groups (n = 10) based on the materials used for endocrown fabrication. Group V (Vita-Enamic), Group N (Nacera Hybrid), Group T (Translucent Prettau Zirconia) and Group P (Pekkton ivory). All samples were exposed to artificial aging method simulating one year of clinical service. Silicone replica technique and stereomicroscope (25X) utilized to evaluate the marginal and internal gaps of endocrowns at different areas. Fracture resistance test used for cemented specimens followed by qualitative investigation utilizing Stereomicroscopy. Four models representing four endocrown systems used for restoration of severely-damaged endodontically treated upper first molar were generated for finite element analysis (FEA). Axially and centrally static occlusal compressive load was applied. Modified Von Mises and maximum principal stress values on the remaining tooth structure, cement lines and restorative materials were assessed independently. Resulted data were statistically analyzed at P-value ≤ 0.05.ResultsIn the current study, the highest mean values of internal and marginal discrepancies (μm) among studied groups were reported for Zirconia group (100.300 and 102.650) respectively, while the lowest mean value of internal discrepancy (μm) was observed for Nacera group (69.275) and the lowest mean value of marginal discrepancy (μm) was observed for PEKK group (78.4750). Regarding internal discrepancy, Vita-Enamic and PEKK groups did not exhibit any statistically significant differences (P = 0.293), however zirconia and the other tested groups exhibited statistically significant differences in the mean values of the marginal gap region (p 0.05).On the other hand, PEKK group showed the highest mean value of fracture resistance (1845.20 N) and the lowest value was observed for Vita-Enamic group (946.50 N). Regarding to stress distributions through 3D FEA, and according to modified von Mises (mvM) analysis, the greatest possible stress values were noticed in PEKK model in relation to tooth structure, cement line, and flowable composite as the following: (93.1, 64.5, 58.4 MPa) respectively, while Zirconia revealed lower maximum stress values (11.4, 13.6, 11.6 MPa) respectively.ConclusionsStatistically excellent marginal and internal fit was observed for PEKK in relation to other used endocrown materials. Also, PEKK material explained fracture resistance comparable to zirconia value while the lowest value was detected for Vita Enamic material.

Dataset Information

Evaluation of the Surface Characteristics of Dental CAD/CAM Materials after Different Surface Treatments.

Publications

Evaluation of the Surface Characteristics of Dental CAD/CAM Materials after Different Surface Treatments.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets