Effects of Artificial Tooth Brushing and Hydrothermal Aging on the Mechanical Properties and Color Stability of Dental 3D Printed and CAD/CAM Materials.

ABSTRACT: This study analyzed the surface roughness and waviness, Vickers hardness (VHN), and color changes of six types of 3D printed resins and computer-aided design/computer-aided manufacturing (CAD/CAM) materials after artificial toothbrushing. The average surface roughness height (Ra) change of Formlabs denture teeth A2 resin (FMLB) was not significant between after artificial toothbrushing (0.17 ± 0.02 μm and 0.17 ± 0.05 μm, respectively; mean ± standard deviation). However, the Ra value increased significantly in all remaining groups. Regarding waviness, polymethylmethacrylate (PMMA) had the largest increases in average waviness height (Wa) and maximum surface waviness height (Wz) between, before (0.43 ± 0.23 μm and 0.08 ± 0.02 μm), and after (8.67 ± 4.03 μm, 1.30 ± 0.58 μm) toothbrushing. There were no significant changes in Wa for Formlabs denture teeth A2 resin (FMLB) and NextDent C&B (NXT). After artificial toothbrushing, the dispersed-filler composite (DFC) group had the largest color difference (ΔE, of 2.4 ± 0.9), and the remaining materials had smaller changes than the clinical acceptance threshold of ΔE = 2.25. The VHN of FMLB and NXT were 9.1 ± 0.4 and 15.5 ± 0.4, respectively, and were not affected by artificial toothbrushing. The flexural strengths of the 3D printed materials were 139.4 ± 40.5 MPa and 163.9 ± 14.0 MPa for FMLB and NXT, respectively, which were similar to those of the polycarbonate and PMMA groups (155.2 ± 23.6 MPa and 108.0 ± 8.1 MPa, respectively). This study found that the evaluated 3D printed materials had mechanical and optical properties comparable to those of CAD/CAM materials and were stable even after artificial toothbrushing and hydrothermal aging.

SUBMITTER: Nam NE

PROVIDER: S-EPMC8540203 | biostudies-literature | 2021 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effects of Artificial Tooth Brushing and Hydrothermal Aging on the Mechanical Properties and Color Stability of Dental 3D Printed and CAD/CAM Materials.

Nam Na-Eun NE Shin Seung-Ho SH Lim Jung-Hwa JH Shim June-Sung JS Kim Jong-Eun JE

Materials (Basel, Switzerland) 20211019 20

This study analyzed the surface roughness and waviness, Vickers hardness (VHN), and color changes of six types of 3D printed resins and computer-aided design/computer-aided manufacturing (CAD/CAM) materials after artificial toothbrushing. The average surface roughness height (Ra) change of Formlabs denture teeth A2 resin (FMLB) was not significant between after artificial toothbrushing (0.17 ± 0.02 μm and 0.17 ± 0.05 μm, respectively; mean ± standard deviation). However, the Ra value increased s ...[more]

PMID: 34683798

Similar Datasets

Project description:BackgroundThe effect of an immune-boosting beverage (SAM) containing Sambucus Nigra, an energy beverage (ENE), an in-office bleaching (BLE) agent with 25% hydrogen peroxide superior, glazing (GLA) or polishing (POL) methods, and professional dental prophylaxis (PDP) on the color of CAD-CAM restorative materials is unknown.MethodsIn total 210 specimens were prepared, consisting of CAD-CAM feldspathic (FC), zirconia-reinforced lithium disilicate ceramic (ZLS) and hybrid ceramic (HC). The ceramic specimens were divided according to the polishing methods of glazing (GLA) and mechanical polishing (POL). All materials were divided into two groups: with and without BLE. A 25% hydrogen peroxide superior (HPS) gel was used for BLE. After the baseline (BAS) measurement, the specimens were immersed in 3 different beverages (distilled water (DIS), SAM, ENE). After 28 days, a fine-grained (RDA 7) prophylaxis paste was applied. Statistical analysis of ∆E00 color difference values was performed by 3-way ANOVA and Bonferroni test (α = 0.05).ResultsThe effect of all other actions except material-BLE-beverage on color for BAS-Day 28 was statistically different (p < 0.05). The effect of material, material-BLE, beverage on color for Day 28-PDP was statistically different (p < 0.05). After 28 days, the lowest color change was found in FC-GLA and HC immersed in DIS (p = 0.0001) and the highest in FC-POL immersed in ENE (p = 0.0002). PDP was efficient in color recovery in HC immersed to DIS, ENE and SAM (p = 0.0010). For FC, HC and ZLS, BLE caused a higher color change (p < 0.0001). Regardless of the material, the highest color change for BLE-beverage was found in BLE-treated specimens immersed in ENE (p = 0.0496) and the lowest color change was found in non-BLE-treated specimens immersed in SAM (p = 0.0074).ConclusionsIn materials pre-exposed to 25% HPS, the effect of PDP on color recovery was lower than in unexposed materials. After 28 days, mechanical polishing produced higher color change in FC than glazing, however, in ZLS effects of glazing and mechanical polishing on color were similar. For material/polishing method, HC was the most effective. ENE caused higher color change than DIS and SAM. PDP was more effective than ENE in restoring color to DIS- and SAM-immersed specimens.

Project description:ObjectivesTo evaluate and compare fracture resistance, translucency, and color reproducibility, as well as the effect of aging on the fracture load and color stability of novel monolithic CAD/CAM ceramics.Materials and methodsOne hundred crowns of uniform thickness were milled from five ceramic blocks (n = 20): partially crystallized lithium disilicate (PLD) and fully crystallized lithium disilicate (FLD), lithium metasilicate (LMS), 4Y-TZP (SMZ), and 5Y-TZP (UMZ) monolithic zirconia. PLD crowns were glazed, LMS was fired, and FLD was polished. SMZ and UMZ crowns were sintered and polished. Crowns were adhesively cemented to epoxy dies. Half of the crowns (n = 10) were subjected to 1.200.000 load cycles with thermal cycling. Color space values L, a, b defined by the Commission Internationale de l´Eclairage (CIELAB) were measured before and after aging, and (∆E) was calculated. Both aged and non-aged specimens were loaded until fracture in a universal testing machine and the fracture load was recorded. X-ray diffraction (XRD) and scanning electron microscope (SEM) fractographic analysis were carried out on fractured fragments of representative samples. For translucency and color reproducibility, 50 rectangular-shaped specimens were fabricated and processed as described previously. Color values were measured over black and white backgrounds, and the translucency parameter (TP) was computed. Using the shade verification mode, (∆E) to shade A3 was calculated. Data were statistically analyzed using one-way and two-way ANOVA, and t-test.ResultsAging did not affect fracture resistance significantly (p > 0.05). The highest mean fracture load was obtained for the SMZ and UMZ. A significant color change was observed after aging in all groups. The highest TP was noted for FLD. SMZ and UMZ had the best shade match.ConclusionsZirconia showed higher fracture resistance and color stability than lithium silicate ceramics. Lithium silicate ceramics were more translucent. The experimental FLD demonstrated high translucency.Clinical relevanceTested ceramics showed sufficient stability to withstand masticatory forces. Characterization of final restorations might be mandatory for better color match.

Dataset Information

Effects of Artificial Tooth Brushing and Hydrothermal Aging on the Mechanical Properties and Color Stability of Dental 3D Printed and CAD/CAM Materials.

Publications

Effects of Artificial Tooth Brushing and Hydrothermal Aging on the Mechanical Properties and Color Stability of Dental 3D Printed and CAD/CAM Materials.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets