Adsorption of Fibrinogen on Silica Surfaces-The Effect of Attached Nanoparticles.

ABSTRACT: When a biomaterial is inserted into the body, proteins rapidly adsorb onto its surface, creating a conditioning protein film that functions as a link between the implant and adhering cells. Depending on the nano-roughness of the surface, proteins will adsorb in different amounts, with different conformations and orientations, possibly affecting the subsequent attachment of cells to the surface. Thus, modifications of the surface nanotopography of an implant may prevent biomaterial-associated infections. Fibrinogen is of particular importance since it contains adhesion epitopes that are recognized by both eukaryotic and prokaryotic cells, and can therefore influence the adhesion of bacteria. The aim of this study was to model adsorption of fibrinogen to smooth or nanostructured silica surfaces in an attempt to further understand how surface nanotopography may affect the orientation of the adsorbed fibrinogen molecule. We used a coarse-grained model, where the main body of fibrinogen (visible in the crystal structure) was modeled as rigid and the flexible ? C-chains (not visible in the crystal structure) were modeled as completely disordered. We found that the elongated fibrinogen molecule preferably adsorbs in such a way that it protrudes further into solution on a nanostructured surface compared to a flat one. This implicates that the orientation on the flat surface increases its bio-availability.

SUBMITTER: Hyltegren K

PROVIDER: S-EPMC7175343 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Adsorption of Fibrinogen on Silica Surfaces-The Effect of Attached Nanoparticles.

Hyltegren Kristin K Hulander Mats M Andersson Martin M Skepö Marie M

Biomolecules 20200306 3

When a biomaterial is inserted into the body, proteins rapidly adsorb onto its surface, creating a conditioning protein film that functions as a link between the implant and adhering cells. Depending on the nano-roughness of the surface, proteins will adsorb in different amounts, with different conformations and orientations, possibly affecting the subsequent attachment of cells to the surface. Thus, modifications of the surface nanotopography of an implant may prevent biomaterial-associated inf ...[more]

PMID: 32155964

Similar Datasets

Project description:Silicon (Si) is suggested to be an important/essential nutrient for bone and connective tissue health. Silicon-substituted hydroxyapatite (Si-HA) has silicate ions incorporated into its lattice structure and was developed to improve attachment to bone and increase new bone formation. Here we investigated the direct adsorption of silicate species onto an HA coated surface as a cost effective method of incorporating silicon on to HA surfaces for improved implant osseointegration, and determined changes in surface characteristics and osteoblast cell adhesion. Plasma-sprayed HA-coated stainless steel discs were incubated in silica dispersions of different concentrations (0-42 mM Si), at neutral pH for 12 h. Adsorbed Si was confirmed by XPS analysis and quantified by ICP-OES analysis following release from the HA surface. Changes in surface characteristics were determined by AFM and measurement of surface wettability. Osteoblast cell adhesion was determined by vinculin plaque staining. Maximum Si adsorption to the HA coated disc occurred after incubation in the 6 mM silica dispersion and decreased progressively with higher silica concentrations, while no adsorption was observed with dispersions below 6 mM Si. Comparison of the Si dispersions that produced the highest and lowest Si adsorption to the HA surface, by TEM-based analysis, revealed an abundance of small amorphous nanosilica species (NSP) of ~1.5 nm in diameter in the 6 mM Si dispersion, with much fewer and larger NSP in the 42 mM Si dispersions. 29Si-NMR confirmed that the NSPs in the 6 mM silica dispersion were polymeric and similar in composition to the larger NSPs in the 42 mM Si dispersion, suggesting that the latter were aggregates of the former. Amorphous NSP adsorbed from the 6 mM dispersion on to a HA-coated disc surface increased the surface's water contact angle by 53°, whereas that adsorbed from the 42 mM dispersion decreased the contact angle by 18°, indicating increased and decreased hydrophobicity, respectively. AFM showed an increase in surface roughness of the 6 mM Si treated surface, which correlated well with an increase in number of vinculin plaques. These findings suggest that NSP of the right size (relative to charge) adsorb readily to the HA surface, changing the surface characteristics and, thus, improving osteoblast cell adhesion. This treatment provides a simple way to modify plasma-coated HA surfaces that may enable improved osseointegration of bone implants.

Project description:Biomaterials, once inserted in the oral cavity, become immediately covered by a layer of adsorbed proteins that consists mostly of salivary proteins but also of plasma proteins if the biomaterial is placed close to the gingival margin or if it becomes implanted into tissue and bone. It is often this protein layer, rather than the pristine biomaterial surface, that is subsequently encountered by colonizing bacteria or attaching tissue cells. Thus, to study this important initial protein adsorption from human saliva and serum and how it might be influenced through chemical modification of the biomaterial surface, we have measured the amount of protein adsorbed and analyzed the composition of the adsorbed protein layer using gel electrophoresis and western blotting. Here, we have developed an in vitro model system based on silica surfaces, chemically modified with 7 silane-based self-assembled monolayers that span a broad range of physicochemical properties, from hydrophilic to hydrophobic surfaces (water contact angles from 15° to 115°), low to high surface free energy (12 to 57 mN/m), and negative to positive surface charge (zeta potentials from -120 to +40 mV at physiologic pH). We found that the chemical surface functionalities exerted a substantial effect on the total amounts of proteins adsorbed; however, no linear correlation of the adsorbed amounts with the physicochemical surface parameters was observed. Only the adsorption behavior of a few singular protein components, from which physicochemical data are available, seems to follow physicochemical expectations. Examples are albumin in serum and lysozyme in saliva; in both, adsorption was favored on countercharged surfaces. We conclude from these findings that in complex biofluids such as saliva and serum, adsorption behavior is dominated by the overall protein-binding capacity of the surface rather than by specific physicochemical interactions of single protein entities with the surface.

Dataset Information

Adsorption of Fibrinogen on Silica Surfaces-The Effect of Attached Nanoparticles.

Publications

Adsorption of Fibrinogen on Silica Surfaces-The Effect of Attached Nanoparticles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets