High-speed femtosecond laser plasmonic lithography and reduction of graphene oxide for anisotropic photoresponse.

ABSTRACT: Micro/nanoprocessing of graphene surfaces has attracted significant interest for both science and applications due to its effective modulation of material properties, which, however, is usually restricted by the disadvantages of the current fabrication methods. Here, by exploiting cylindrical focusing of a femtosecond laser on graphene oxide (GO) films, we successfully produce uniform subwavelength grating structures at high speed along with a simultaneous in situ photoreduction process. Strikingly, the well-defined structures feature orientations parallel to the laser polarization and significant robustness against distinct perturbations. The proposed model and simulations reveal that the structure formation is based on the transverse electric (TE) surface plasmons triggered by the gradient reduction of the GO film from its surface to the interior, which eventually results in interference intensity fringes and spatially periodic interactions. Further experiments prove that such a regular structured surface can cause enhanced optical absorption (>20%) and an anisotropic photoresponse (~0.46 ratio) for the reduced GO film. Our work not only provides new insights into understanding the laser-GO interaction but also lays a solid foundation for practical usage of femtosecond laser plasmonic lithography, with the prospect of expansion to other two-dimensional materials for novel device applications.

SUBMITTER: Zou T

PROVIDER: S-EPMC7183510 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Femtosecond laser-assisted synthesis of silver nanoparticles and reduced graphene oxide hybrid for optical limiting.

Project description:Reduced graphene oxide (rGO) functionalized with silver nanoparticles (Ag NPs) is prepared using a femtosecond laser ablation in liquids method. By ablating the mixed aqueous solutions of silver nitrate and graphene oxide (GO) using femtosecond laser pulses, Ag ions and GO are simultaneously reduced and well-dispersed Ag NPs supported on rGO are obtained. The effect of laser power, irritation time and Ag ion concentration on the optical property and morphology of the products are systematically studied. The nonlinear optical responses of the functionalized graphene are studied using a nanosecond Z-scan technique. The rGO hybrid shows an enhanced nonlinear absorption (NLA) effect compared with GO and rGO, and thus exhibits an excellent optical limiting (OL) property with very low activating threshold, which is estimated to be about 0.38 J cm-2. The enhanced NLA effect in rGO hybrids makes it possible to fabricate solid-state optical limiter, improving the practicality of graphene materials in the OL area.

| S-EPMC6083672 | biostudies-literature

Anisotropic Plasmonic Gold Nanorod-Indocyanine Green@Reduced Graphene Oxide-Doxorubicin Nanohybrids for Image-Guided Enhanced Tumor Theranostics.

Project description:The unique physicochemical and localized surface plasmon resonance assets of gold nanorods (GNRs) have offered combined cancer treatments with real-time diagnosis by integrating diverse theragnostic modalities into a single nanoplatform. In this work, a unique multifunctional nanohybrid material based on GNRs was designed for in vitro and in vivo tumor imaging along with synergistic and combinatorial therapy of tumor. The hybrid material with size less than 100 nm was achieved by embedding indocyanine green (ICG) on mesoporous silica-coated GNRs with further wrapping of reduced graphene oxide (rGO) and then attached with doxorubicin (DOX) and polyethylene glycol. The nanohybrid unveiled noteworthy stability and competently protected the embedded ICG from further aggregation, photobleaching, and nucleophilic attack by encapsulation of GNRs-ICG with rGO. Such combination of GNRs-ICG with rGO and DOX served as a real-time near-infrared (NIR) contrast imaging agent for cancer diagnosis. The hybrid material exhibits high NIR absorption property along with three destined capabilities, such as, nanozymatic activity, photothermal activity, and an excellent drug carrier for drug delivery. The integrated properties of the nanohybrid were then utilized for the triple mode of combined therapeutics of tumor cells, through synergistic catalytic therapy and chemotherapy with combinatorial photothermal therapy to achieve the maximum cancer killing efficiency. It is assumed that the assimilated multimodal imaging and therapeutic capability in single nanoparticle platform is advantageous for future practical applications in cancer diagnosis, therapy, and molecular imaging.

| S-EPMC9089692 | biostudies-literature

The primary structural photoresponse of phytochrome proteins captured by a femtosecond X-ray laser.

Project description:Phytochrome proteins control the growth, reproduction, and photosynthesis of plants, fungi, and bacteria. Light is detected by a bilin cofactor, but it remains elusive how this leads to activation of the protein through structural changes. We present serial femtosecond X-ray crystallographic data of the chromophore-binding domains of a bacterial phytochrome at delay times of 1 ps and 10 ps after photoexcitation. The data reveal a twist of the D-ring, which leads to partial detachment of the chromophore from the protein. Unexpectedly, the conserved so-called pyrrole water is photodissociated from the chromophore, concomitant with movement of the A-ring and a key signaling aspartate. The changes are wired together by ultrafast backbone and water movements around the chromophore, channeling them into signal transduction towards the output domains. We suggest that the observed collective changes are important for the phytochrome photoresponse, explaining the earliest steps of how plants, fungi and bacteria sense red light.

| S-EPMC7164956 | biostudies-literature

Raman spectroscopy data related to the laser induced reduction of graphene oxide.

Project description:This data paper reports data obtained from the fitting of Raman spectra obtained during a laser reduction process for graphene oxide under different processing and material conditions. In particular, we show examples of fitting curves of three different representative reduced graphene oxide spectra, as well as fitting curves for a graphene oxide spectrum. Moreover, we show and compare cumulative distributions of the ID/IG values (intensity ratio of peaks D and G) obtained from spectra acquired from different samples. Fittings and distributions were obtained using the OriginPro 8.5 software package. Such data may be the starting point of further experiments on the laser induced reduction of graphene oxide.

| S-EPMC8385394 | biostudies-literature

Controllable Plasmonic Nanostructures induced by Dual-wavelength Femtosecond Laser Irradiation.

Project description:We demonstrated an abnormal double-peak (annular shaped) energy deposition through dual-wavelength synthesis of the fundamental frequency (ω) and the second-harmonic frequency (2ω) of a femtosecond (fs) Ti:sapphire laser. The annular shaped distribution of the dual-wavelength fs laser was confirmed through real beam shape detection. This uniquely simple and flexible technique enables the formation of functional plasmonic nanostructures. We applied this double-peak fs-laser-induced dewetting effect to the controlled fabrication and precise deposition of Au nanostructures, by using a simple, lithography-free, and single-step process. In this process, the double-peak energy-shaped fs laser pulse induces surface patterning of a thin film followed by nanoscale hydrodynamic instability, which is highly controllable under specific irradiation conditions. Nanostructure morphology (shape, size, and distribution) modulation can be achieved by adjusting the laser irradiation parameters, and the subsequent ion-beam polishing enables further dimensional reduction and removal of the surrounding film. The unique optical properties of the resulting nanostructure are highly sensitive to the shape and size of the nanostructure. In contrast to a nanoparticle, the resonance-scattering spectrum of an Au nanobump exhibites two resonance peaks. These suggest that the dual-wavelength fs laser-based dewetting of thin films can be an effective means for the scalable manufacturing of patterned-functional nanostructures.

| S-EPMC5725531 | biostudies-literature

Anisotropic optical transmission of femtosecond laser induced periodic surface nanostructures on indium-tin-oxide films.

Project description:Two types of periodic nanostructures, self-organized nanodots and nanolines, were fabricated on the surfaces of indium-tin-oxide (ITO) films using femtosecond laser pulse irradiation. Multiple periodicities (approximately 800 nm and 400 nm) were clearly observed on the ITO films with nanodot and nanoline structures and were identified using two-dimensional Fourier transformation patterns. Both nanostructures show the anisotropic transmission characteristics in the visible range, which are strongly correlated with the geometry and the metallic content of the laser-induced nanostructures.

| S-EPMC3448592 | biostudies-other

UV-Laser Interference Lithography for Local Functionalization of Plasmonic Nanostructures with Responsive Hydrogel.

Project description:A novel approach to local functionalization of plasmonic hotspots at gold nanoparticles with biofunctional moieties is reported. It relies on photocrosslinking and attachment of a responsive hydrogel binding matrix by the use of a UV interference field. A thermoresponsive poly(N-isopropylacrylamide)-based (pNIPAAm) hydrogel with photocrosslinkable benzophenone groups and carboxylic groups for its postmodification was employed. UV-laser interference lithography with a phase mask configuration allowed for the generation of a high-contrast interference field that was used for the recording of periodic arrays of pNIPAAm-based hydrogel features with the size as small as 170 nm. These hydrogel arrays were overlaid and attached on the top of periodic arrays of gold nanoparticles, exhibiting a diameter of 130 nm and employed as a three-dimensional binding matrix in a plasmonic biosensor. Such a hybrid material was postmodified with ligand biomolecules and utilized for plasmon-enhanced fluorescence readout of an immunoassay. Additional enhancement of the fluorescence sensor signal by the collapse of the responsive hydrogel binding matrix that compacts the target analyte at the plasmonic hotspot is demonstrated.

| S-EPMC7032879 | biostudies-literature

Crack reduction in laser powder bed fusion of MnAl(C) using graphene oxide coated powders.

Project description:MnAl(C) is a promising candidate as a rare earth free magnet. When processing MnAl(C) in laser powder bed fusion (L-PBF) the high cooling rates can retain the high temperature ε-phase which can then be annealed at low temperatures to yield the ferromagnetic τ-phase. However, MnAl(C) has been shown to be difficult to print using L-PBF and the material is prone to severe cracking. In this study, we have investigated how the addition of a graphene oxide (GO) coating on the powders can affect the processability of MnAl(C) and properties of the printed parts. MnAl(C) powders were coated with 0.2 wt.% GO using a wet-chemical process. The addition of GO reduced crack formation in the printed parts, and also influenced the degree of [Formula: see text] texture along the build direction. After printing, densities of 93% and 87% could be achieved for the reference and 0.2 wt.% GO, respectively. Furthermore, a 35% reduction of cracking was calculated from image analysis, comparing printed samples produced from coated and non-coated powders. Both powders formed mostly the ε-phase but some two-phase regions with a mix of γ- and ε-phase could be observed in the as-printed parts, but seemed to be more prominent in the uncoated reference samples and could also be linked to cracks. The τ-phase together with smaller amounts of secondary phases was obtained after heat treatment at 560 °C for 5 min for both samples. Vibrating sample magnetometry was used to measure the magnetic properties, the reference had a remanence of 33 Am2/kg and a coercivity of 139 kA/m, and the 0.2 wt.% GO sample showed a similar remanence of 30 Am2/kg and coercivity of 130 kA/m. These results show that GO coating is a viable method to reduce detrimental cracking in L-PBF MnAl without reducing the magnetic performance of the material.

| S-EPMC10784453 | biostudies-literature

Femtosecond Laser Fabrication of Anisotropic Structures in Phosphorus- and Boron-Doped Amorphous Silicon Films.

Project description:Femtosecond laser-modified amorphous silicon (a-Si) films with optical and electrical anisotropy have perspective polarization-sensitive applications in optics, photovoltaics, and sensors. We demonstrate the formation of one-dimensional femtosecond laser-induced periodic surface structures (LIPSS) on the surface of phosphorus- (n-a-Si) and boron-doped (p-a-Si) amorphous silicon films. The LIPSS are orthogonal to the laser polarization, and their period decreases from 1.1 ± 0.1 µm to 0.84 ± 0.07 µm for p-a-Si and from 1.06 ± 0.03 to 0.98 ± 0.01 for n-a-Si when the number of laser pulses per unit area increases from 30 to 120. Raman spectra analysis indicates nonuniform nanocrystallization of the irradiated films, with the nanocrystalline Si phase volume fraction decreasing with depth from ~80 to ~40% for p-a-Si and from ~20 to ~10% for n-a-Si. LIPSS' depolarizing effect, excessive ablation of the film between LIPSS ridges, as well as anisotropic crystalline phase distribution within the film lead to the emergence of conductivity anisotropy of up to 1 order for irradiated films. Current-voltage characteristic nonlinearity observed for modified p-a-Si samples may be associated with the presence of both the crystalline and amorphous phases, resulting in the formation of potential barriers for the in-plane carrier transport and Schottky barriers at the electric contacts.

| S-EPMC9654927 | biostudies-literature

High-Speed Imaging of Second-Harmonic Generation in MoS2 Bilayer under Femtosecond Laser Ablation.

Project description:We report an in situ characterization of transition-metal dichalcogenide (TMD) monolayers and twisted bilayers using a high-speed second-harmonic generation (SHG) imaging technique. High-frequency laser modulation and galvano scanning in the SHG imaging enabled a rapid identification of the crystallinity in the TMD, including the orientation and homogeneity with a speed of 1 frame/s. For a twisted bilayer MoS2, we studied the SHG peak intensity and angles as a function of the twist angle under a strong interlayer coupling. In addition, rapid SHG imaging can be used to visualize laser-induced ablation of monolayer and bilayer MoS2 in situ under illumination by a strong femtosecond laser. Importantly, we observed a characteristic threshold behavior; the ablation process occurred for a very short time duration once the preheating condition was reached. We investigated the laser thinning of the bilayer MoS2 with different twist angles. When the twist angle was 0°, the SHG decreased by approximately one-fourth of the initial intensity when one layer was removed. Conversely, when the twist angle was approximately 60° (the SHG intensity was suppressed), the SHG increased abruptly close to that of the nearby monolayer when one layer was removed. Precise layer-by-layer control was possible because of the unique threshold behavior of the laser-induced ablation.

| S-EPMC8308356 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data