Effect of the photoinitiator system on the polymerization of secondary methacrylamides of systematically varied structure for dental adhesive applications.

ABSTRACT: OBJECTIVE:The aim of this study was to investigate the influence of the photoinitiator system on the polymerization kinetics of methacrylamide-based monomers as alternatives to methacrylates in adhesives dental-based materials. METHODS:In total, 16 groups were tested. Monofunctional monomers (2-hydroxyethyl methacrylate) - HEMA; (2-hydroxy-1-ethyl methacrylate) -2EMATE, (2-hydroxyethyl methacrylamide) - HEMAM; and (N-(1-hydroxybutan-2-yl) methacrylamide) -2EM; were combined with bifunctional monomers containing the same polymerizing moieties as the monofunctional counterparts (HEMA-BDI; 2EMATE-BDI; HEMAM-BDI; and 2EM-BDI) at 50/50 M ratios. BHT was used as inhibitor (0.1 wt%) and the photoinitiators used were: CQ + EDMAB (0.2/0.8), BAPO (0.2), IVOCERIN (0.2), and DMPA (0.2), in wt%. The polymerization kinetics were monitored using Near-IR spectroscopy (?6165 cm-1) in real-time while the specimens were photoactivated with a mercury arc lamp (Acticure 2; 320-500 nm, 300 mW/cm2) for 5 min, and maximum rate of polymerization (Rpmax, in %.s-?1), degree of conversion at Rpmax (DC@Rpmax, in %), and the final degree of conversion (Final DC, in %) were calculated (n = 3). Initial viscosity was measured with an oscillating rheometer (n = 3). Data were analyzed using Two-way ANOVA for the polymerization kinetics and one-way ANOVA for the viscosity. Multiple comparisons were made using the Tukey's test (? = 0.05). RESULTS:There was statistically significant interaction between monomer and photoinitiator (p < 0.001). For the methacrylates groups, the highest Rpmax was observed for HEMA + DMPA and 2EMATE + BAPO. For methacrylamides groups, the highest Rpmax were observed for HEMAM and 2EM, both with DMPA. Final DC was higher for the methacrylate groups, in comparison with methacrylamide groups, independent of the photoinitiators. However, for the methacrylamide groups, the association with BAPO led to the lowest values of DC. In terms of DC@Rpmax, methacrylate-based systems showed significantly higher values than methacrylamide formulations. DMPA and Ivocerin led to higher values than CQ/EDMAB and BAPO in methacrylamide-based compounds. BAPO systems showed de lowest values for both HEMA and HEMAM formulations. For the viscosity (Pa.s), only 2EM had higher values (1.60 ± 0.15) in comparison with all monomers. In conclusion, polymerization kinetics was affected by the photoinitiators for both monomers. Viscosity was significantly increased with the use of secondary methacrylamide. SIGNIFICANCE:this work demonstrated the feasibility of using newly-synthesized methacrylamide monomers in conjunction with a series of initiator systems already used in commercial materials.

SUBMITTER: Barcelos LM

PROVIDER: S-EPMC7200046 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of the photoinitiator system on the polymerization of secondary methacrylamides of systematically varied structure for dental adhesive applications.

Barcelos L M LM Borges M G MG Soares C J CJ Menezes M S MS Huynh V V Logan M G MG Fugolin A P P APP Pfeifer C S CS

Dental materials : official publication of the Academy of Dental Materials 20200128 3

<h4>Objective</h4>The aim of this study was to investigate the influence of the photoinitiator system on the polymerization kinetics of methacrylamide-based monomers as alternatives to methacrylates in adhesives dental-based materials.<h4>Methods</h4>In total, 16 groups were tested. Monofunctional monomers (2-hydroxyethyl methacrylate) - HEMA; (2-hydroxy-1-ethyl methacrylate) -2EMATE, (2-hydroxyethyl methacrylamide) - HEMAM; and (N-(1-hydroxybutan-2-yl) methacrylamide) -2EM; were combined with b ...[more]

PMID: 32005546

Similar Datasets

Project description:A self-strengthening methacrylate-based dental adhesive system was developed by introducing an epoxy cyclohexyl trimethoxysilane (TS) which contains both epoxy and methoxysilyl functional groups. The experimental formulation, HEMA/BisGMA/TS (22.5/27.5/50, wt%), was polymerized by visible-light. Real-time Fourier transform infrared spectroscopy (FTIR) was used to investigate in situ the free radical polymerization of methacrylate, ring-opening cationic polymerization of epoxy, and photoacid-induced sol-gel reactions. Among the three simultaneous reactions, the reaction rate of the free radical polymerization was the highest and the hydrolysis/condensation rate was the lowest. With 40s-irradiation, the degrees of conversion of the double bond and epoxy groups at 600 s were 73.2±1.2%, 87.9±2.4%, respectively. Hydrolysis of the methoxysilyl group was initially <5%, and increased gradually to about 50% after 48 h dark storage. Photoacids generated through the visible-light-induced reaction were effective in catalyzing both epoxy ring-opening polymerization and methoxysilyl sol-gel reaction. The mechanical properties of copolymers made with TS concentrations from 5 to 35 wt% were obtained using dynamic mechanical analysis (DMA). In wet conditions, the storage moduli at 70 °C and glass transition temperature were significantly higher than that of the control (p<0.05); these properties increased with TS concentration and storage time. The post reaction of hydrolysis/condensation of alkoxysilane could provide persistent strengthening whether in a neutral or acidic environment and these characteristics could lead to enhanced mechanical properties in the oral environment. The cumulative amount of leached species decreased significantly in the TS-containing copolymers. These results provide valuable information for the development of dental adhesives with reduced leaching of methacrylate monomers and enhanced mechanical properties under the wet, oral environment.

Project description:ObjectiveAssess the ability of an antimicrobial drug-releasing resin adhesive, containing octenidine dihydrochloride (OCT)-silica co-assembled particles (DSPs), to enhance the biostability and preserve the interfacial fracture toughness (FT) of composite restorations bonded to dentin. Enzyme-catalyzed degradation compromises the dental restoration-tooth interface, increasing cariogenic bacterial infiltration. In addition to bacterial ingress inhibition, antimicrobial-releasing adhesives may exhibit direct interfacial biodegradation inhibition as an additional benefit.MethodsMini short-rod restoration bonding specimens with total-etch adhesive with/without 10% wt. DSPs were made. Interfacial fracture toughness (FT) was measured as-manufactured or post-incubation in simulated human salivary esterase (SHSE) for up to 6-months. Effect of OCT on SHSE and whole saliva/bacterial enzyme activity was assessed. Release of OCT outside the restoration interface was assessed.ResultsNo deleterious effect of DSPs on initial bonding capacity was observed. Aging specimens in SHSE reduced FT of control but not DSP-adhesive-bonded specimens. OCT inhibited SHSE degradation of adhesive monomer and may inhibit endogenous proteases. OCT inhibited bacterial esterase and collagenase. No endogenous collagen breakdown was detected in the present study. OCT increased human saliva degradative esterase activity below its minimum inhibitory concentration towards S. mutans (MIC), but inhibited degradation above MIC. OCT release outside restoration margins was below detection.SignificanceDSP-adhesive preserves the restoration bond through a secondary enzyme-inhibitory effect of released OCT, which is virtually confined to the restoration interface microgap. Enzyme activity modulation may produce a positive-to-negative feedback switch, by increasing OCT concentration via biodegradation-triggered release to an effective dose, then subsequently slowing degradation and degradation-triggered release.

Dataset Information

Effect of the photoinitiator system on the polymerization of secondary methacrylamides of systematically varied structure for dental adhesive applications.

Publications

Effect of the photoinitiator system on the polymerization of secondary methacrylamides of systematically varied structure for dental adhesive applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets