Evaluation of the antimicrobial activity of novel composite plastics containing two silver (I) additives, acyl pyrazolonate and acyl pyrazolone.

ABSTRACT: BACKGROUND:Public health systems today face the dual challenges of controlling infections and curbing the increase in antimicrobial resistance manifested in drug-resistant microorganisms in hospitals and elsewhere. In the last ten years, research has been conducted to develop new materials with antimicrobial properties to be used in medical devices, increasingly found to harbour critical nosocomial infections. METHODS:Two next-generation composites using the antimicrobial qualities of silver were tested against Escherichia coli, Staphylococcus aureus and Candida albicans with the purpose of evaluating their antimicrobial and antifungal activity. These tests applied the standardized method according to ISO-2216: Plastics-Measurement of Antibacterial Activity on Plastics Surfaces. Testing was carried out using polyethylene (PE) enriched with AgNO3 as a positive control and PE as a negative control. RESULTS:The antimicrobial activity of the composites proved to be between medium (bacteriostatic) and very good (bactericidal). In particular, PE2 showed the highest scores against all microorganisms, with values ranging from good to very good. Instead, PE1 had lower scores, with a value of medium for Escherichia coli and slight for Candida albicans. Statistical analysis carried out with the t-test for unpaired data showed a statistically significant difference between the positive control and the other polymers (p< .0001). CONCLUSIONS:Based on our findings, we conclude that the test, conducted to ISO-2216 standards, could be extended to include fungal strains and that the new composites could be used to produce antimicrobial surfaces for medical devices, for example, intubation tubes, urinary catheters, vascular prostheses, and mechanical heart valves. This would reduce the risk of microbial contamination and biofilm formation, ensuring better health outcomes for patients treated with these devices. Further testing should be done to evaluate potential future applications of these composites and the possibility of adding fungal strains to the IS0-2216 standard.

SUBMITTER: Scuri S

PROVIDER: S-EPMC7233731 | biostudies-literature | 2019 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Evaluation of the antimicrobial activity of novel composite plastics containing two silver (I) additives, acyl pyrazolonate and acyl pyrazolone.

Scuri Stefania S Petrelli Fabio F Grappasonni Iolanda I Idemudia Loveth L Marchetti Fabio F Di Nicola Corrado C

Acta bio-medica : Atenei Parmensis 20190906 3

<h4>Background</h4>Public health systems today face the dual challenges of controlling infections and curbing the increase in antimicrobial resistance manifested in drug-resistant microorganisms in hospitals and elsewhere. In the last ten years, research has been conducted to develop new materials with antimicrobial properties to be used in medical devices, increasingly found to harbour critical nosocomial infections.<h4>Methods</h4>Two next-generation composites using the antimicrobial qualitie ...[more]

PMID: 31580329

Similar Datasets

Project description:Objective:To compare the elastic modulus, flexural strength, and hardness of an experimental resin based composite (RBC) with and without containing silver nanoparticles (AgNPs) and bioactive glass (BAG) with a commercially available RBC. Methods:This study was conducted, during the period August 2016-May 2018, at the Department of Dental Materials, Peshawar Dental College, Peshawar (Pakistan) and Department of Chemistry, University of Montreal, Canada. Test specimens made in the commercial RBC acted as Group-1 (G1). An experimental RBC containing 70 wt % filler content was synthesized. It was first used as such to prepare test specimens to act as the experimental control group (G2). This RBC was then modified by adding various amounts of BAG (5%, 10% and 15%) and a fixed amount of 0.009% AgNPs to use the so modified RBCs for preparing the test specimens to belong to three groups (G3, G4 & G5). The AgNPs had been synthesized in situ by reduction of salt during photo-polymerization. Flexural strength (FS), elastic modulus (EM) and Vickers hardness were determined using universal testing machine and hardness tester respectively. Data were analyzed using one-way ANOVA and Tukey post-hoc test. Results:Except for G3 restorations showing significantly lower mean FS value, the FS for those in the other groups were not significantly different (p>0.05). Elastic modulus of the experimental RBC restorations was though higher than those of the others but the difference was statistically insignificant (p>0.05). Reduced Vickers hardness values were documented for the restorations in the G4 and G5 compared to those in the G3 but again the difference was insignificant (p>0.05). Flexural strength and hardness values of the test specimens in the experimental RBCs were significantly lower than those made in the commercial hybrid RBC (p<0.05). Conclusion:BAG and AgNPs addition to the experimental RBC in the mentioned concentration adversely affected the tested mechanical properties.

Dataset Information

Evaluation of the antimicrobial activity of novel composite plastics containing two silver (I) additives, acyl pyrazolonate and acyl pyrazolone.

Publications

Evaluation of the antimicrobial activity of novel composite plastics containing two silver (I) additives, acyl pyrazolonate and acyl pyrazolone.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets