Biocomposites of Bio-Polyethylene Reinforced with a Hydrothermal-Alkaline Sugarcane Bagasse Pulp and Coupled with a Bio-Based Compatibilizer.

ABSTRACT: Bio-polyethylene (BioPE, derived from sugarcane), sugarcane bagasse pulp, and two compatibilizers (fossil and bio-based), were used to manufacture biocomposite filaments for 3D printing. Biocomposite filaments were manufactured and characterized in detail, including measurement of water absorption, mechanical properties, thermal stability and decomposition temperature (thermo-gravimetric analysis (TGA)). Differential scanning calorimetry (DSC) was performed to measure the glass transition temperature (Tg). Scanning electron microscopy (SEM) was applied to assess the fracture area of the filaments after mechanical testing. Increases of up to 10% in water absorption were measured for the samples with 40 wt% fibers and the fossil compatibilizer. The mechanical properties were improved by increasing the fraction of bagasse fibers from 0% to 20% and 40%. The suitability of the biocomposite filaments was tested for 3D printing, and some shapes were printed as demonstrators. Importantly, in a cradle-to-gate life cycle analysis of the biocomposites, we demonstrated that replacing fossil compatibilizer with a bio-based compatibilizer contributes to a reduction in CO2-eq emissions, and an increase in CO2 capture, achieving a CO2-eq storage of 2.12 kg CO2 eq/kg for the biocomposite containing 40% bagasse fibers and 6% bio-based compatibilizer.

SUBMITTER: Ehman NV

PROVIDER: S-EPMC7249044 | biostudies-literature | 2020 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Biocomposites of Bio-Polyethylene Reinforced with a Hydrothermal-Alkaline Sugarcane Bagasse Pulp and Coupled with a Bio-Based Compatibilizer.

Ehman Nanci Vanesa NV Ita-Nagy Diana D Felissia Fernando Esteban FE Vallejos María Evangelina ME Quispe Isabel I Area María Cristina MC Chinga-Carrasco Gary G

Molecules (Basel, Switzerland) 20200505 9

Bio-polyethylene (BioPE, derived from sugarcane), sugarcane bagasse pulp, and two compatibilizers (fossil and bio-based), were used to manufacture biocomposite filaments for 3D printing. Biocomposite filaments were manufactured and characterized in detail, including measurement of water absorption, mechanical properties, thermal stability and decomposition temperature (thermo-gravimetric analysis (TGA)). Differential scanning calorimetry (DSC) was performed to measure the glass transition temper ...[more]

PMID: 32380693

Similar Datasets

Project description:BackgroundPreparing multiple products from lignocellulosic biomass feedstock enhances the profit and sustainability of future biorefineries. Grasses are suitable feedstocks for biorefineries as they permit a variety of possible by-products due to their particular chemical characteristics and morphology. Elucidating the fate of p-hydroxycinnamates (ferulates-FAs and p-coumarates-pCAs) and major structural components during bioprocessing helps to discriminate the sources of recalcitrance in grasses and paves the way for the recovery of p-hydroxycinnamates, which have multiple applications. To address these subjects, we assessed sugarcane bagasse biorefining under alkaline-sulfite chemithermomechanical (AS-CTM) pretreatment and enzymatic saccharification.ResultsThe mass balances of the major bagasse components were combined with 2D-NMR structural evaluation of process solids to advance our understanding of sugarcane bagasse changes during biorefining. AS-CTM pretreatment provided a high yield and thoroughly digestible substrates. The pretreated material was depleted in acetyl groups, but retained 62 and 79% of the original lignin and xylan, respectively. Forty percent of the total FAs and pCAs were also retained in pretreated material. After pretreatment and enzymatic hydrolysis, the residual solids contained mostly lignin and ester-linked pCAs, with minor amounts of FAs and non-digested polysaccharides. Saponification of the residual solids, at a higher alkali load, cleaved all the ester linkages in the pCAs; nevertheless, a significant fraction of the pCAs remained attached to the saponified solids, probably to lignin, through 4-O ether-linkages.ConclusionAS-CTM pretreatment provided soundly digestible substrates, which retain substantial amounts of xylans and lignin. Acetyl groups were depleted, but 40% of the total FAs and pCAs remained in pretreated material. Ester-linked pCAs detected in pretreated material also resisted to the enzymatic hydrolysis step. Only a more severe saponification reaction cleaved ester linkages of pCAs from residual solids; nevertheless, pCAs remained attached to the core lignin through 4-O ether-linkages, suggesting the occurrence of an alkali-stable fraction of pCAs in sugarcane bagasse.

Project description:Brazil is the world’s second largest producer of ethanol. Increasing demand for this biofuel has called for investment in new technologies. One example of such technologies is the second-generation (2G) ethanol production. Lignocellulose comprises mainly cellulose and hemicellulose, which consist of high-energy sugars that can be converted into ethanol. Aspergillus sp play an important role in the recycling of lignocellulosic biomass. These species have been investigated as a cell factory to produce industrial enzymes. To improve our understanding of the mechanisms used by Aspergillus sp during degradation of plant biomass and to identify the hydrolytic enzymes secreted by these fungi, we have analyzed the transcriptome and secretome of an Aspergillus species grown on sugarcane bagasse (SEB). A. fumigatus was cultivated in the presence of fructose or SEB. Its cellulolytic and xylanolytic activities depended on time. The maximum activities of endoglucanase and xylanase from the fungus grown on SEB were 0.0029 and 10.82 U mL-1, respectively. Characterization of the transcriptome by RNAseq technology helped to identify genes that participated in the degradation of the biomass demonstrating potential application in the process of enzymatic hydrolysis. The RNAseq data revealed that 2287 genes were differentially expressed in the fungus grown on SEB; 1181 and 1046 of these genes were up- and down-regulated, respectively. There were several CAZymes among the up-regulated genes. Most of these enzymes belonged to the GH family, which includes important hydrolytic and accessory enzymes involved in the degradation of lignocellulose. Similarly, proteomic studies showed that a total of 130 proteins existed in the fungus grown on SEB. These proteins were classified into several groups of secreted extracellular enzymes, and their functional classification demonstrated that 59% of the proteins were CAZymes such as GH45-endoglucanases, GH6 and GH7-cellobiohydrolases, GH3-β-glucosidases, GH10-xylanases, and AA9-LPMO. Data obtained by transcriptome and secretome analyses indicated that A. fumigatus produces a considerable number of CAZymes that participate in the hydrolysis of biomass. These CAZymes are valuable for the lignocellulosic bioenergy industry, provide information for future studies on the degradation of biomass, and improve understanding of the role genes and enzymes play in the degradation process.

Dataset Information

Biocomposites of Bio-Polyethylene Reinforced with a Hydrothermal-Alkaline Sugarcane Bagasse Pulp and Coupled with a Bio-Based Compatibilizer.

Publications

Biocomposites of Bio-Polyethylene Reinforced with a Hydrothermal-Alkaline Sugarcane Bagasse Pulp and Coupled with a Bio-Based Compatibilizer.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure