Effect of surface sealant on the surface roughness of different composites and evaluation of their microhardness.

ABSTRACT: Purpose:The aim of this study was to evaluate the effect of a surface sealant on the surface roughness of different composites and compare their microhardness values. Materials and methods:Sixty disc-shaped specimens were prepared and assigned to 6 groups (n =10). Groups were prepared as follows; Group 1 (Herculite XRV Ultra), Group 2 (Beautifil Bulk Restorative) and Group 3 (Filtek Bulk Fill Posterior Restorative). Groups 4, 5, and 6 were prepared by applying a surface sealant (BisCover LV) on the specimens in groups 1, 2 and 3. Surface hardness of the discs in group 1, 2, and 3 and surface roughness of the discs in all groups were measured using the Vickers hardness test and a profilometer, respectively. One-way ANOVA was used to test for differences among the groups. Results:No significant differences were observed in the microhardness and roughness between the experimental and control groups for each restorative materials. Group 3 showed the highest surface hardness and group 4 showed the lowest surface roughness values. Conclusion:Using the BisCover LV resin after the polishing step has no significant effect on the surface roughness. The highest hardness values were obtained for the Filtek Bulk Fill Posterior Restorative after the polishing step. The smoothest surfaces were obtained for all experimental groups using the BisCover LV resin after the polishing step, Herculite XRV Ultra showed lower average roughness values than the other materials.

SUBMITTER: Gurbuz O

PROVIDER: S-EPMC7252534 | biostudies-literature | 2020 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of surface sealant on the surface roughness of different composites and evaluation of their microhardness.

Gurbuz Ozge O Cilingir Aylin A Dikmen Benin B Ozsoy Alev A Mert Eren Meltem M

European oral research 20200101 1

<h4>Purpose</h4>The aim of this study was to evaluate the effect of a surface sealant on the surface roughness of different composites and compare their microhardness values.<h4>Materials and methods</h4>Sixty disc-shaped specimens were prepared and assigned to 6 groups (n =10). Groups were prepared as follows; Group 1 (Herculite XRV Ultra), Group 2 (Beautifil Bulk Restorative) and Group 3 (Filtek Bulk Fill Posterior Restorative). Groups 4, 5, and 6 were prepared by applying a surface sealant (B ...[more]

PMID: 32518904

Similar Datasets

Project description:BACKGROUND:Increased composite roughness enhances bacterial adhesion and discoloration, thus increasing the risk of gingival inflammation and secondary caries. Concerns about detrimental effects of sodium bicarbonate on surface roughness influenced the development of less abrasive powders: a glycine-based powder and an erythritol-based powder, additionally - sodium bicarbonate-based powder of reduced grain size. However, there is limited evidence on effects of these materials on the surface of dental fillings. The aim of the present study was to compare the effects of three air-polishing powders (of a reduced abrasiveness) on surface roughness of microhybrid restorative composite material. MATERIAL AND METHODS:Microhybrid light-cure resin composite samples were placed on 64 plaster cubes and light-cured through polyester strips. Surface roughness was measured using laser confocal microscope (magnification 2160x). The specimens were randomly divided into three groups (n = 20, 20 and 24) and air-polished with: sodium bicarbonate (40 μm), glycine (25 μm) and erythritol (14 μm), respectively. Then surface roughness was remeasured, keeping the same field of observation. Specialized 3D analysis software was used for data processing. Parameters according to ISO 25178: Sa, Sq, Sku, Sp, Sv, Sz, Ssk were used to describe surface roughness. RESULTS:Sa, Sq, Sp, Sv, Sz increased significantly following air polishing. Ssk was significantly higher, whereas Sku was significantly lower in sodium bicarbonate and erythritol groups than before air polishing. Comparison between the three powders revealed that Sa was significantly higher in sodium bicarbonate group than in glycine group. Sku was significantly higher in glycine and erythritol groups than in sodium bicarbonate group. CONCLUSIONS:Sodium bicarbonate has a stronger detrimental effect on composite surface than glycine or erythritol. No advantage of erythritol comparing to glycine could be found.

Project description:Fabricating method may affect the surface properties and biological characteristics of provisional restorations. This study aimed to evaluate the surface roughness, plaque accumulation, and cytotoxicity of provisional restorative materials fabricated by the conventional, digital subtractive and additive methods. Sixty-six bar-shaped specimens (2×4×10 mm) were fabricated by using provisional restorative materials through the conventional, digital subtractive and additive methods (n = 22 per group). Ten specimens of each group were used for surface roughness and plaque accumulation tests, 10 specimens for cytotoxicity assay, and 2 specimens of each group were used for qualitative assessment by scanning electron microscopy. The Ra (roughness average) and Rz (roughness height) values (μm) were measured via profilometer, and visual inspection was performed through scanning electron microscopy. Plaque accumulation of Streptococcus mutans and cytotoxicity on human gingival fibroblast-like cells were evaluated. The data were analyzed with one-way ANOVA and Tukey's post hoc test (α = 0.05). Surface roughness, biofilm accumulation and cytotoxicity were significantly different among the groups (P<0.05). Surface roughness was significantly higher in the conventional group (P<0.05); however, the two other groups were not significantly different (P>0.05). Significantly higher bacterial attachment was observed in the additive group than the subtractive (P<0.001) and conventional group (P = 0.025); while, the conventional and subtractive groups were statistically similar (P = 0.111). Regarding the cytotoxicity, the additive group had significantly higher cell viability than the subtractive group (P = 0.006); yet, the conventional group was not significantly different from the additive (P = 0.354) and subtractive group (P = 0.101). Surface roughness was the highest in conventionally cured group; but, the additive group had the most plaque accumulation and lowest cytotoxicity.

Dataset Information

Effect of surface sealant on the surface roughness of different composites and evaluation of their microhardness.

Publications

Effect of surface sealant on the surface roughness of different composites and evaluation of their microhardness.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets