Dielectric Properties of Silicothermic Reduction Chromite in the Microwave Field.
Ontology highlight
ABSTRACT:
SUBMITTER: Hu T
PROVIDER: S-EPMC7288365 | biostudies-literature | 2020 Jun
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Randomly distributed carbon fibers (CFs) reinforced epoxy resin composites are prepared by the pouring method, the dielectric properties of CF composites with different fiber content and length have been performed in the frequency range from 8.2 to 12.4 GHz. The complex permittivity of the composite increases with the fiber length, which is attributed to the decrease of depolarization field, and increases with the volume fraction, which is attributed to the increase of polarization. A formula, based on the theory of Reynolds-Hugh, is proposed to calculate the effective permittivity of CF composites, and validated by the experiments. The proposed formula is further applied to derive the axial permittivity of CF and analyze the effect of fiber length on the axial permittivity.
| S-EPMC4609955 | biostudies-other
Project description:Dielectric properties study is important in understanding the interaction between materials within electromagnetic field. By knowing and understanding the dielectric properties of materials, an efficient and effective microwave heating process and products can be designed. In this study, the dielectric properties of several encapsulation wall materials were measured using open-ended coaxial probe method. This method was selected due to its simplicity and high accuracy. All materials exhibited similar behavior. The result inferred that ?-cyclodextrin (BC), starch (S), Arabic (GA) and maltodextrin (M) with various dextrose equivalent exhibited effective encapsulation wall materials in microwave encapsulation-drying technique owing to loss tangent values which were higher than 0.1 at general application frequency of 2.45 GHz. Thus, these were found to be suitable as wall material to encapsulate the selected core material in this microwave encapsulation-drying method. On contrary, sodium caseinate showed an ineffective wall material to be used in microwave encapsulation-drying. The differences in the values of dielectric constant, loss factor and loss tangent were found to be contributed by frequency, composition and bulk density.
| S-EPMC6233465 | biostudies-literature
Project description:The GABA molecule is the major inhibitory neurotransmitter in the mammalian central nervous system. Through binding to post-synaptic neurons, GABA reduces the neuronal excitability by hyperpolarization. Correct binding between the GABA molecules and its receptors relies on molecular recognition. Earlier studies suggest that recognition is determined by the geometries of the molecule and its receptor. We employed dielectric relaxation spectroscopy (DRS) to study the conformation and dielectric properties of the GABA molecule under physiologically relevant laboratory conditions. The dielectric properties of GABA investigated have given us new insights about the GABA molecule, such as how they interact with each other and with water molecules at different temperatures (22°C and 37.5°C). Higher temperature leads to lower viscosity, thus lower relaxation time. The change in the GABA relaxation time due to concentration change is more associated with the solution viscosity than with the GABA dipole moment. A resonance behavior was observed with high GABA concentrations at physiological temperature, where there might be a phase transition at a certain temperature for a given GABA concentration that leads to a sudden change of the dielectric properties.
| S-EPMC8433407 | biostudies-literature
Project description:The role played by electronic polarization in the dielectric properties of liquid N-methyl acetamide (NMA) is examined using molecular dynamics simulations with a polarizable force field based on classical Drude oscillators. The model presented is the first force field shown to reproduce the anomalously large dielectric constant of liquid NMA. Details of the molecular polarizability are found to be important. For instance, all elements of the polarizability tensor, rather then just the trace, impact on the condensed phase properties. Two factors related to electronic polarizability are found to contribute to this large dielectric constant. First is the significant enhancement of the mean amide molecular dipole magnitude, which is 50% larger in the liquid than in the gas phase. Second is the consequent strong hydrogen bonding between molecular neighbors that enhances the orientational alignment of the molecular dipoles. Polarizable models of amide compounds that have two (acetamide) and zero (N,N-dimethyl acetamide) polar hydrogen-bond donor atoms are also investigated. Experimentally, the neat liquid dielectric constants at 373 K are 100 for NMA, 66 for acetamide and 26 for N,N-dimethyl acetamide. The polarizable models replicate this trend, predicting a dielectric constant of 92+/-5 for NMA, 66+/-3 for acetamide and 23+/-1 for N,N-dimethyl acetamide.
| S-EPMC4754998 | biostudies-literature
Project description:The frequency and temperature dependence of dielectric properties of CH3NH3PbI3 (MAPI) crystals have been studied and analyzed in connection with temperature-dependent structural studies. The obtained results bring arguments for the existence of ferroelectricity and aim to complete the current knowledge on the thermally activated conduction mechanisms, in dark equilibrium and in the presence of a small external a.c. electric field. The study correlates the frequency-dispersive dielectric spectra with the conduction mechanisms and their relaxation processes, as well as with the different transport regimes indicated by the Nyquist plots. The different energy barriers revealed by the impedance spectroscopy highlight the dominant transport mechanisms in different frequency and temperature ranges, being associated with the bulk of the grains, their boundaries, and/or the electrodes' interfaces.
| S-EPMC8348982 | biostudies-literature
Project description:This study discusses the production of microwave baked gluten-free cakes formulated by mixing buckwheat flour and rice flour at different concentrations. Three different ratios of buckwheat flour to rice flour (20:80%, 30:70%, 40:60%) and two different gum types (xanthan and guar gum) with a white layer cake recipe were employed. The batters were baked in microwave oven at different microwave powers (540 W, 450 W, 360 W) for different baking times (3 min, 3.5 min, 4 min). The effect of microwave power, baking time and buckwheat flour concentration on weight loss, color, specific volume, porosity, total phenolic content and dielectric properties were investigated. The optimum microwave power, baking time and buckwheat flour concentration were found as 432.77 W, 3 min, 40% for guar gum added cakes and 360 W, 3.70 min and 29.23% for xanthan gum added ones. It was found that weight loss and color values of the cakes that were baked at the optimal conditions were less than those of control cakes. On the other hand, total phenolic content, specific volume, porosity, dielectric constant and dielectric loss factor values were higher for guar gum added cakes compared to control samples. In addition, it was observed that the cakes prepared with guar gum had similar pore size distribution with control cakes. As a conclusion of the study, it can be declared that surface color and specific volume problems of microwave baking could be solved by addition of guar gum to the formulation which also enables the production of functional, phenolic rich microwave baked cakes.
| S-EPMC6423201 | biostudies-literature
Project description:Platinum-bearing chromitites in mafic-ultramafic intrusions such as the Bushveld Complex are key repositories of strategically important metals for human society. Basaltic melts saturated in chromite alone are crucial to their generation, but the origin of such melts is controversial. One concept holds that they are produced by processes operating within the magma chamber, whereas another argues that melts entering the chamber were already saturated in chromite. Here we address the problem by examining the pressure-related changes in the topology of a Mg2SiO4-CaAl2Si2O8-SiO2-MgCr2O4 quaternary system and by thermodynamic modelling of crystallisation sequences of basaltic melts at 1-10 kbar pressures. We show that basaltic melts located adjacent to a so-called chromite topological trough in deep-seated reservoirs become saturated in chromite alone upon their ascent towards the Earth's surface and subsequent cooling in shallow-level chambers. Large volumes of these chromite-only-saturated melts replenishing these chambers are responsible for monomineralic layers of massive chromitites with associated platinum-group elements.
| S-EPMC5792441 | biostudies-literature
Project description:NiMn₂O₄ prepared by conventional heating was irradiated with a microwave H-field using a single-mode cavity under air and magnetic properties of the microwave-irradiated material were investigated. X-ray diffraction and transmission electron microscopy demonstrated that the phase and microstructure are not affected by H-field irradiation. Measurements of the magnetization as a function of temperature revealed that the antiferromagnetic sublattice disappeared and electron spin resonance showed the existence of Mn2+, suggesting that Mn3+ is partially reduced. Moreover, the magnetization of NiMn₂O₄ was controlled from 35.3 to 18.2 emu/g and the coercivity from 140 to 750 Oe by changing the sample temperature during microwave irradiation. The reduction reaction of NiMn₂O₄ is controlled by microwave H-field irradiation, resulting in control over the magnetic properties.
| S-EPMC5456704 | biostudies-literature
Project description:Complex permittivity of conducting polypyrrole (PPy)-coated Nylon-Lycra textiles is measured using a free space transmission measurement technique over the frequency range of 1-18 GHz. The aging of microwave dielectric properties and reflection, transmission and absorption for a period of 18 months is demonstrated. PPy-coated fabrics are shown to be lossy over the full frequency range. The levels of absorption are shown to be higher than reflection in the tested samples. This is attributed to the relatively high resistivity of the PPy-coated fabrics. Both the dopant concentration and polymerisation time affect the total shielding effectiveness and microwave aging behaviour. Distinguishing either of these two factors as being exclusively the dominant mechanism of shielding effectiveness is shown to be difficult. It is observed that the PPy-coated Nylon-Lycra samples with a p-toluene sulfonic acid (pTSA) concentration of 0.015 M and polymerisation times of 60 min and 180 min have 37% and 26% decrease in total transmission loss, respectively, upon aging for 72 weeks at room temperature (20 °C, 65% Relative humidity (RH)). The concentration of the dopant also influences the microwave aging behaviour of the PPy-coated fabrics. The samples with a higher dopant concentration of 0.027 mol/L pTSA are shown to have a transmission loss of 32.6% and 16.5% for short and long polymerisation times, respectively, when aged for 72 weeks. The microwave properties exhibit better stability with high dopant concentration and/or longer polymerization times. High pTSA dopant concentrations and/or longer polymerisation times result in high microwave insertion loss and are more effective in reducing the transmission and also increasing the longevity of the electrical properties.
| S-EPMC5456856 | biostudies-other
Project description:Microwave-assisted processes have recognized advantages over more conventional heating techniques. However, the effects on the materials' microstructure are still a matter of study, due to the complexity of the interaction between microwaves and matter, especially at high temperatures. Recently developed advanced microwave instrumentation allows the study of high temperature microwave heating processes in a way that was not possible before. In this paper, different materials and thermal processes induced by microwaves have been studied through the in situ characterization of their dielectric properties with temperature. This knowledge is crucial in several aspects: to analyze the effects of the microwave field on the reaction pathways; to design and optimize microwave-assisted processes, and to predict the behavior of materials leading to repeatable and reliable heating processes, etc.
| S-EPMC5503012 | biostudies-other