Sustainable PHBV/Cellulose Acetate Blends: Effect of a Chain Extender and a Plasticizer.

ABSTRACT: Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and cellulose acetate (CA) were blended in the presence of a plasticizer, i.e., triethyl citrate (TEC), and a chain extender, i.e., poly(styrene-acrylic-co-glycidyl methacrylate). To increase the ductility and impact properties of PHBV and to investigate a new biodegradable PHBV-based blend for sustainable packaging, CA was compatibilized with TEC. PHBV and plasticized CA (pCA) blends showed complete immiscibility through separate glass transition and melting peak temperatures in differential scanning calorimetry (DSC), despite the similar Hansen solubility parameters of PHBV, CA, and TEC, indicating partial miscibility. Phase separation between PHBV and pCA was clearly observed by scanning electron microscopy (SEM). PHBV/pCA (70:30) blends had improved impact strength, exceeding that of neat PHBV and pCA, which is attributed to PHBV porosity induced by degradation from the high processing temperature. During processing, the plasticizer migrated from CA to PHBV and partially plasticized it, as evidenced through DSC analysis. The melt temperature of PHBV was reduced, which was confirmed by double melting peaks, representing the formation of secondary crystallites at a lower temperature. Due to processing at high temperatures (210-220 °C), significant porosity was observed in the PHBV/pCA 30:70 blend in SEM analysis. Consequently, the impact strength was improved by 110% as compared to that of virgin PHBV. The addition of CE had no effect on the mechanical properties but did make the PHBV/pCA blends morphologically uniform.

SUBMITTER: Meereboer KW

PROVIDER: S-EPMC7315424 | biostudies-literature | 2020 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Sustainable PHBV/Cellulose Acetate Blends: Effect of a Chain Extender and a Plasticizer.

Meereboer Kjeld W KW Pal Akhilesh K AK Misra Manjusri M Mohanty Amar K AK

ACS omega 20200611 24

Poly(3-hydroxybutyrate-<i>co</i>-3-hydroxyvalerate) (PHBV) and cellulose acetate (CA) were blended in the presence of a plasticizer, i.e., triethyl citrate (TEC), and a chain extender, i.e., poly(styrene-acrylic-<i>co</i>-glycidyl methacrylate). To increase the ductility and impact properties of PHBV and to investigate a new biodegradable PHBV-based blend for sustainable packaging, CA was compatibilized with TEC. PHBV and plasticized CA (pCA) blends showed complete immiscibility through separate ...[more]

PMID: 32596558

Similar Datasets

Project description:A recently developed cellulose hybrid chemical treatment consists of two steps: solvent exchange (with ethanol or hexane) and chemical grafting of maleic anhydride (MA) on the surface of fibers. It induces a significant decrease in cellulose moisture content and causes some changes in the thermal resistance of analyzed blend samples, as well as surface properties. The thermal characteristics of ethylene-norbornene copolymer (TOPAS) blends filled with hybrid chemically modified cellulose fibers (UFC100) have been widely described on the basis of differential scanning calorimetry and thermogravimetric analysis. Higher thermal stability is observed for the materials filled with the fibers which were dried before any of the treatments carried out. Dried cellulose filled samples start to degrade at approximately 330 °C while undried UFC100 specimens begin to degrade around 320 °C. Interestingly, the most elevated thermal resistance was detected for samples filled with cellulose altered only with solvents (both ethanol and hexane). In order to support the supposed thermal resistance trends of prepared blend materials, apparent activation energies assigned to cellulose degradation (EA1) and polymer matrix decomposition (EA2) have been calculated and presented in the article. It may be evidenced that apparent activation energies assigned to the first decomposition step are higher in case of the systems filled with UFC100 dried prior to the modification process. Moreover, the results have been enriched using surface free energy analysis of the polymer blends. The surface free energy polar part (Ep) raises considering samples filled with not dried UFC100. On the other hand, when cellulose fibers are dried prior to the modification process, then the blend sample's dispersive part of surface free energy is increased with respect to that containing unmodified fiber. As polymer blend Ep exhibits higher values reflecting enhanced material degradation potential, the cellulose fibers employment leads to more eco-friendly production and responsible waste management. This is in accordance with the rules of sustainable development.

Dataset Information

Sustainable PHBV/Cellulose Acetate Blends: Effect of a Chain Extender and a Plasticizer.

Publications

Sustainable PHBV/Cellulose Acetate Blends: Effect of a Chain Extender and a Plasticizer.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets