Enhancing the Mechanical Properties of Glass-Ionomer Dental Cements: A Review.

ABSTRACT: This paper reviews the strategies that have been reported in the literature to attempt to reinforce glass-ionomer dental cements, both conventional and resin-modified. These cements are widely used in current clinical practice, but their use is limited to regions where loading is not high. Reinforcement might extend these applications, particularly to the posterior dentition. A variety of strategies have been identified, including the use of fibres, nanoparticles, and larger particle additives. One problem revealed by the literature survey is the limited extent to which researchers have used International Standard test methods. This makes comparison of results very difficult. However, it does seem possible to draw conclusions from this substantial body of work and these are (1) that powders with conventional particle sizes do not reinforce glass-ionomer cements, (2) certain fibres and certain nanoparticles give distinct improvements in strength, and (3) in the case of the nanoparticles these improvements are associated with differences in the morphology of the cement matrix, in particular, a reduction in the porosity. Despite these improvements, none of the developments has yet been translated into clinical use.

SUBMITTER: Nicholson JW

PROVIDER: S-EPMC7321445 | biostudies-literature | 2020 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Enhancing the Mechanical Properties of Glass-Ionomer Dental Cements: A Review.

Nicholson John W JW Sidhu Sharanbir K SK Czarnecka Beata B

Materials (Basel, Switzerland) 20200531 11

This paper reviews the strategies that have been reported in the literature to attempt to reinforce glass-ionomer dental cements, both conventional and resin-modified. These cements are widely used in current clinical practice, but their use is limited to regions where loading is not high. Reinforcement might extend these applications, particularly to the posterior dentition. A variety of strategies have been identified, including the use of fibres, nanoparticles, and larger particle additives. ...[more]

PMID: 32486416

Similar Datasets

Project description:IntroductionDevelopment of white spot lesions (WSLs) during orthodontic treatment is a common risk factor. Fixation of the orthodontic appliances with glass ionomer cements could reduce the prevalence of WSL's due to their fluoride release capacities. The purpose of this study was to evaluate differences of fluoride release properties from resin-modified and conventional glass ionomer cements (GICs).MethodsThe resin-modified GICs Fuji ORTHO LC (GC Orthodontics), Meron Plus QM (VOCO), as well as the conventional GICs Fuji ORTHO (GC Orthodontics), Meron (VOCO) and Ketac Cem Easymix (3M ESPE) were tested in this study. The different types of GICs were applied to hydroxyapatite discs according to the manufacturer's instructions and stored in a solution of TISAB III (Total Ionic Strength Adjustment Buffer III) and fluoride-free water at 37°C. Fluoride measurements were made after 5 minutes, 2 hours, 24 hours, 14 days, 28 days, 2 months, 3 months and 6 months. One factor analysis of variance (ANOVA) was used for the overall comparison of the cumulative fluoride release (from measurement times of 5 minutes to 6 months) between the different materials with the overall level of significance set to 0.05. Tukey's post hoc test was used for post hoc pairwise comparisons in the cumulative fluoride release between the different materials.ResultsThe cumulative fluoride release (mean ± sd) in descending order was: Fuji ORTHO LC (221.7 ± 10.29 ppm), Fuji ORTHO (191.5 ± 15.03 ppm), Meron Plus QM (173.0 ± 5.89 ppm), Meron (161.3 ± 7.84 ppm) and Ketac Cem Easymix (154.6 ± 6.09 ppm) within 6 months. Analysis of variance detected a significant difference in the cumulative fluoride release between at least two of the materials (rounded p-value < 0.001). Pairwise analysis with Tukey's post hoc test showed a significant difference in the cumulative fluoride release for all the comparisons except M and MPQM (p = 0.061) and KCE and M (p = 0.517).ConclusionFluoride ions were released cumulatively over the entire test period for all products. When comparing the two products from the same company (Fuji ORTHO LC vs. Fuji ORTHO from GC Orthodontics Europe GmbH and Meron Plus QM vs. Meron from VOCO GmbH, Mannheim, Germany), it can be said that the resin-modified GICs have a higher release than conventional GICs. The highest individual fluoride release of all GICs was at 24 hours. A general statement, whether resin-modified or conventional GICs have a higher release of fluoride cannot be made.

Dataset Information

Enhancing the Mechanical Properties of Glass-Ionomer Dental Cements: A Review.

Publications

Enhancing the Mechanical Properties of Glass-Ionomer Dental Cements: A Review.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets