Studies of the early stages of the dynamic setting process of chemically activated restorative glass-ionomer cements.

ABSTRACT:

Objective

To evaluate the early stages of the setting process of chemically activated restorative glass-ionomer cements (GICs).

Material and methods

Five GICs were evaluated (n = 5): Equia Forte (GC), Equia Forte HT (GC), Ketac Universal (3M ESPE), Maxxion R (FGM) and Riva Self Cure (SDI) by Thermography, Fourier Transform Infrared Attenuated Total Reflectance Spectroscopy (FTIR-ATR) and Gillmore needle indentation mechanical testing. The FTIR-ATR spectra showed the formation of metal carboxylates within the cements and enabled the stabilization time (ST) to be determined and the thermographic camera measured the temperature field images in the sample. Data were statistically analyzed by ANOVA and Tukey-Kramer (α = 5%).

Results

The Gillmore needle test showed that the order of hardening was opposite to the order of ST values determined by FTIR. The results with the thermographic camera showed two stages of temperature variation, which coincided with the evolution of specific infrared bands. The exception was Maxxion R, which showed only a single step change in temperature.

Conclusion

The early stages of the GIC setting reaction show temperature changes, both endothermic and exothermic, at specific times, confirming the occurrence of individual chemical reactions. The early setting involves reactions other than carboxylate formation.Significance: This study gives further detail of the early stages of the setting of GICs, and past research regarding the setting reaction of GIC.

SUBMITTER: Tsuzuki FM

PROVIDER: S-EPMC8018555 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:ObjectivesAddition of chlorhexidine has enhanced the antimicrobial effect of glass ionomer cement (GIC) indicated to Atraumatic Restorative Treatment (ART); however, the impact of this mixture on the properties of these materials and on the longevity of restorations must be investigated. The aim of this study was to evaluate the effects of incorporating chlorhexidine (CHX) in the in vitro biological and chemical-mechanical properties of GIC and in vivo clinical/ microbiological follow-up of the ART with GIC containing or not CHX.Material and methodsFor in vitro studies, groups were divided into GIC, GIC with 1.25% CHX, and GIC with 2.5% CHX. Antimicrobial activity of GIC was analyzed using agar diffusion and anti-biofilm assays. Cytotoxic effects, compressive tensile strength, microhardness and fluoride (F) release were also evaluated. A randomized controlled trial was conducted on 36 children that received ART either with GIC or GIC with CHX. Saliva and biofilm were collected for mutans streptococci (MS) counts and the survival rate of restorations was checked after 7 days, 3 months and one year after ART. ANOVA/Tukey or Kruskal-Wallis/ Mann-Whitney tests were performed for in vitro tests and in vivo microbiological analysis. The Kaplan-Meier method and Log rank tests were applied to estimate survival percentages of restorations (p<0.05).ResultsIncorporation of 1.25% and 2.5% CHX improved the antimicrobial/anti-biofilm activity of GIC, without affecting F release and mechanical characteristics, but 2.5% CHX was cytotoxic. Survival rate of restorations using GIC with 1.25% CHX was similar to GIC. A significant reduction of MS levels was observed for KM+CHX group in children saliva and biofilm 7 days after treatment.ConclusionsThe incorporation of 1.25% CHX increased the in vitro antimicrobial activity, without changing chemical-mechanical properties of GIC and odontoblast-like cell viability. This combination improved the in vivo short-term microbiological effect without affecting clinical performance of ART restorations.

Project description:IntroductionDevelopment of white spot lesions (WSLs) during orthodontic treatment is a common risk factor. Fixation of the orthodontic appliances with glass ionomer cements could reduce the prevalence of WSL's due to their fluoride release capacities. The purpose of this study was to evaluate differences of fluoride release properties from resin-modified and conventional glass ionomer cements (GICs).MethodsThe resin-modified GICs Fuji ORTHO LC (GC Orthodontics), Meron Plus QM (VOCO), as well as the conventional GICs Fuji ORTHO (GC Orthodontics), Meron (VOCO) and Ketac Cem Easymix (3M ESPE) were tested in this study. The different types of GICs were applied to hydroxyapatite discs according to the manufacturer's instructions and stored in a solution of TISAB III (Total Ionic Strength Adjustment Buffer III) and fluoride-free water at 37°C. Fluoride measurements were made after 5 minutes, 2 hours, 24 hours, 14 days, 28 days, 2 months, 3 months and 6 months. One factor analysis of variance (ANOVA) was used for the overall comparison of the cumulative fluoride release (from measurement times of 5 minutes to 6 months) between the different materials with the overall level of significance set to 0.05. Tukey's post hoc test was used for post hoc pairwise comparisons in the cumulative fluoride release between the different materials.ResultsThe cumulative fluoride release (mean ± sd) in descending order was: Fuji ORTHO LC (221.7 ± 10.29 ppm), Fuji ORTHO (191.5 ± 15.03 ppm), Meron Plus QM (173.0 ± 5.89 ppm), Meron (161.3 ± 7.84 ppm) and Ketac Cem Easymix (154.6 ± 6.09 ppm) within 6 months. Analysis of variance detected a significant difference in the cumulative fluoride release between at least two of the materials (rounded p-value < 0.001). Pairwise analysis with Tukey's post hoc test showed a significant difference in the cumulative fluoride release for all the comparisons except M and MPQM (p = 0.061) and KCE and M (p = 0.517).ConclusionFluoride ions were released cumulatively over the entire test period for all products. When comparing the two products from the same company (Fuji ORTHO LC vs. Fuji ORTHO from GC Orthodontics Europe GmbH and Meron Plus QM vs. Meron from VOCO GmbH, Mannheim, Germany), it can be said that the resin-modified GICs have a higher release than conventional GICs. The highest individual fluoride release of all GICs was at 24 hours. A general statement, whether resin-modified or conventional GICs have a higher release of fluoride cannot be made.