Sucrose-Triggered, Self-Sustained Combustive Synthesis of Magnetic Nickel Oxide Nanoparticles and Efficient Removal of Malachite Green from Water.

ABSTRACT: Dye-containing industrial effluents create major concern nowadays. To address the problem, magnetic nickel oxide nanoparticles (NONPs) were synthesized using the autopropagator combustion technique assisted by sucrose as fuel and used for the removal of toxic malachite green (MG) from water. The material was characterized by scanning electron microscopy (SEM-EDS), Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), vibrating sample magnetism (VSM), point of zero charge (pHZPC), and Brunauer-Emmet-Teller surface area analysis. SEM images show flowerlike texture with the presence of multiple pores. VSM reveals a well-defined hysteresis at room temperature, confirming a permanent magnetic nature of the material. pHZPC was found to be 6.63, which enables dye separation in the drinking water pH range. MG removal from water was carried out in the batch mode with optimized physicochemical parameters such as contact time, pH, temperature, and dose. Langmuir adsorption capacity was estimated to be 87.72 mg/g. Pseudo-second order kinetics (R 2 = 0.999) and Langmuir isotherm model (R 2 = 0.997) were found to best fit. The magnetic nature facilitates fast and quantitative separation of NONPs from solution using a hand-held magnet. Dye-loaded NONPs can be easily regenerated up to 89% and reused up to five cycles without significant loss of activity. The mechanism of adsorption is proposed to be a combination of electrostatic attraction and weak hydrogen bonding. Strategically designed straightforward synthetic protocol, low cost, high uptake capacity, and sustainable use render NONPs an ideal alternative for future dye treatment.

SUBMITTER: Mohanta J

PROVIDER: S-EPMC7364633 | biostudies-literature | 2020 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Sucrose-Triggered, Self-Sustained Combustive Synthesis of Magnetic Nickel Oxide Nanoparticles and Efficient Removal of Malachite Green from Water.

Mohanta Jhilirani J Dey Banashree B Dey Soumen S

ACS omega 20200702 27

Dye-containing industrial effluents create major concern nowadays. To address the problem, magnetic nickel oxide nanoparticles (NONPs) were synthesized using the autopropagator combustion technique assisted by sucrose as fuel and used for the removal of toxic malachite green (MG) from water. The material was characterized by scanning electron microscopy (SEM-EDS), Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), vibrating sample magnetism (VSM), point of zero charge (pH<s ...[more]

PMID: 32685815

Similar Datasets

Project description:Aurivillius oxides ferroelectric layered materials are formed by bismuth oxide and pseu-do-perovskite layers. They have a good ionic conductivity, which is beneficial for various photo-catalyzed reactions. Here, we synthesized ultra-thin nanosheets of two different Aurivillius oxides, Bi2WO6 (BWO) and Bi2MoO6 (BMO), by using a hard-template process. All materials were characterized through XRD, TEM, FTIR, TGA/DSC, DLS/ELS, DRS, UV-Vis. Band gap material (Eg) and potential of the valence band (EVB) were calculated for BWO and BMO. In contrast to previous reports on the use of multi composite materials, a new procedure for photocatalytic efficient BMO nanosheets was developed. The procedure, with an additional step only, avoids the use of composite materials, improves crystal structure, and strongly reduces impurities. BWO and BMO were used as photocatalysts for the degradation of the water pollutant dye malachite green (MG). MG removal kinetics was fitted with Langmuir-Hinshelwood model obtaining a kinetic constant k = 7.81 × 10-2 min-1 for BWO and k = 9.27 × 10-2 min-1 for BMO. Photocatalytic dye degradation was highly effective, reaching 89% and 91% MG removal for BWO and BMO, respectively. A control experiment, carried out in the absence of light, allowed to quantify the contribution of adsorption to MG removal process. Adsorption contributed to MG removal by a 51% for BWO and only by a 19% for BMO, suggesting a different degradation mechanism for the two photocatalysts. The advanced MG degradation process due to BMO is likely caused by the high crystallinity of the material synthetized with the new procedure. Reuse tests demonstrated that both photocatalysts are highly active and stable reaching a MG removal up to 95% at the 10th reaction cycle. These results demonstrate that BMO nanosheets, synthesized with an easy additional step, achieved the best degradation performance, and can be successfully used for environmental remediation applications.

Project description:Phytogenic magnetic nanoparticles (PMNPs) were fabricated using plant leaves' extract of Fraxinus chinensis Roxb. and then, the surfaces of the PMNPs were functionalized by 3-mercaptopropionic acid (3-MPA) to investigate the adsorptive removal of the toxic dye malachite green (MG) from aqueous solutions. The preparation and coating of 3-MPA on the surface of the PMNPs was confirmed and characterized using different techniques, which are UV-visible spectroscopy, Fourier transform infrared spectroscopy (FTIR), X-ray diffractometry (XRD), scanning electron microscopy with integrated energy dispersive X-ray analysis (SEM-EDX), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), vibrating sample magnetometry (VSM), Brunauer-Emmett-Teller (BET) analysis and thermogravimetric analysis (TGA). The hysteresis loops of 3-MPA@PMNPs depicted an excellent superparamagnetic nature with saturation magnetization values of 50.95 emu g-1. The prepared material showed the highest adsorptive rate (98.57% MG removal within 120 min) and an estimated comparable adsorptive capacity of 81.2 mg g-1 at 25 °C. The experimental data were well fitted to the Langmuir isotherm, indicating the monolayer adsorption of MG onto 3-MPA@PMNPs. Furthermore, the kinetic data agreed well with the pseudo-second-order model, indicating the removal of MG by chemisorption and/or ion-exchange mechanism. Thermodynamic study confirmed that the adsorption of MG was exothermic and spontaneous. The high adsorptive removal of the dye not only persisted over a wide pH range (6-12), but the material also demonstrated high selectivity in the presence of co-existing ions (i.e. Pd2+ and Cd2+) along with the fastest separation times (35 s) from aqueous solutions. The recovered adsorbent (3-MPA@PMNPs) was reused five times and maintained a removal efficiency of more than 85%. Therefore, the prepared novel 3-MPA@PMNPs can be employed as an alternative low-cost sorbent material for the removal cationic dyes from textile wastewater. In addition, this green nanotechnology/strategy can easily be implemented in low-economy countries for wastewater treatment.

Dataset Information

Sucrose-Triggered, Self-Sustained Combustive Synthesis of Magnetic Nickel Oxide Nanoparticles and Efficient Removal of Malachite Green from Water.

Publications

Sucrose-Triggered, Self-Sustained Combustive Synthesis of Magnetic Nickel Oxide Nanoparticles and Efficient Removal of Malachite Green from Water.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets