Time-Dependent Effect of Chitosan Nanoparticles as Final Irrigation on the Apical Sealing Ability and Push-Out Bond Strength of Root Canal Obturation.

ABSTRACT: Materials and Methods:Fifty-six premolars were used in this study and divided by two evaluations: 28 teeth for apical sealing ability and 28 others for bond strength. Each study was assigned randomly into two groups of fourteen teeth: Group-1, final irrigation with 17% EDTA; Group-2, with 0.5% chitosan nanoparticles. Each group was further divided into two groups of 7 each: Group-A, final irrigation was applied for 1 minute; Group-B, for 3 minutes. All teeth were obturated with epoxy resin-based sealer and gutta-percha. In the apical sealing ability study, the obturated teeth were immersed in 2% methylene blue and observed under a stereomicroscope (8x magnification). In the bond strength study, the teeth were tested using the push-out technique and observed under a stereomicroscope (40x magnification) to determine the failure type. Data from each evaluation were analysed with two-way ANOVA followed by the LSD test. Results:Final irrigation using 0.5% chitosan nanoparticles produced the same apical sealing ability and bond strength as 17% EDTA (p > 0.05). A significant difference occurred between application times (p < 0.05). The failure type was observed predominantly as cohesive, and the least was adhesive. Conclusion:Regardless of the final irrigation solution used, 3-minute application time produced greater apical sealing ability and push-out bond strength than 1-minute application time.

SUBMITTER: Ratih DN

PROVIDER: S-EPMC7378618 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Time-Dependent Effect of Chitosan Nanoparticles as Final Irrigation on the Apical Sealing Ability and Push-Out Bond Strength of Root Canal Obturation.

Ratih Diatri Nari DN Sari Nikita Ika NI Santosa Pribadi P Kaswati Nofa Mardia Ningsih NMN

International journal of dentistry 20200715

<h4>Materials and methods</h4>Fifty-six premolars were used in this study and divided by two evaluations: 28 teeth for apical sealing ability and 28 others for bond strength. Each study was assigned randomly into two groups of fourteen teeth: Group-1, final irrigation with 17% EDTA; Group-2, with 0.5% chitosan nanoparticles. Each group was further divided into two groups of 7 each: Group-A, final irrigation was applied for 1 minute; Group-B, for 3 minutes. All teeth were obturated with epoxy res ...[more]

PMID: 32733565

Similar Datasets

Project description:IntroductionRoot canal sealing materials play a crucial role in an endodontic procedure by forming a bond between the dentinal walls and the gutta-percha. The current study aims to analyse the dentinal tubule penetration and adhesive pattern, including the push-out bond strength of six commercially available root canal sealers.MethodologyEighty-four mandibular first premolars were split into seven groups (and n = 12), Group 1: Dia-Root, Group 2: One-Fil, Group 3: BioRoot RCS, Group 4: AH Plus, Group 5: CeraSeal, Group 6: iRoot SP, Group 7: GP without sealer (control). Two groups were made, one for dentinal tubule penetration and the other for push-out bond strength; the total sample size was one hundred sixty-eight. Root canal treatment was performed using a method called the crown down technique, and for obturation, the single cone technique was used. A confocal laser scanning microscope (Leica, Microsystem Heidel GmbH, Version 2.00 build 0585, Germany) was used to evaluate dentinal tubule penetration, and Universal Testing Machine was utilised to measure the push-out bond strength (Shimadzu, Japan) using a plunger size of 0.4 mm and speed of 1mm/min. Finally, the adhesive pattern of the sealers was analysed by HIROX digital microscope (KH-7700). Statistical analysis was carried out by a one-way Anova test, Dunnet's T3 test, and Chi-square test.ResultsHighest dentinal tubule penetration was noticed with One-Fil (p<0.05), followed by iRoot SP, CeraSeal, AH Plus, Dia-Root also, the most negligible value was recorded for BioRoot RCS. Meanwhile, BioRoot RCS (p<0.05) demonstrated the greater value of mean push-out bond strength, followed by One-fil, iRoot SP, CeraSeal, AH Plus and Dia-Root. Regarding adhesive pattern, most of the samples were classified as type 3 and type 4 which implies greater sealing ability and better adherence to the dentinal wall. However, BioRoot RCS revealed the most type 4 (p<0.05), followed by AH Plus, One-Fil, CeraSeal and Dia-Root.ConclusionThe highest dentinal tubule penetration was shown by One-Fil compared to other groups. Meanwhile, BioRoot RCS had greater push-out bond strength and more adhesive pattern than other tested materials.

Project description:BackgroundThere are few studies in the literature about the effect of obturation techniques on postoperative pain. Besides, GuttaFlow2 was used for the first time in this study regarding postoperative pain. This study aimed to compare the postoperative pain levels and incidence following single-visit root canal treatment with different canal filling techniques; cold lateral compaction (CLC), thermoplasticised solid-core carrier (GuttaCore) based filling and cold free-flow compaction (GuttaFlow2) technique.MethodsThe patients (n = 93) having single-rooted teeth with a single canal diagnosed with asymptomatic irreversible pulpitis or single-rooted vital teeth with a single canal requiring endodontic treatment because of prosthetic reasons were enrolled in this study. Patients were randomized into three groups (n = 31) according to the obturation technique. A single operator performed all the treatments in a single visit. Data on obturation levels, postoperative pain and analgesic intake frequency were recorded at postoperative 6, 12 and 24 h and daily afterward until the 7th day. Postoperative pain was measured by visual analogue scale (VAS). The date were statistically analyzed with chi-squared tests (for the analyses of the categorical data), the nonparametric Kruskal-Wallis test (for the comparisons of VAS score) and with the Friedman test (for the assessments of the changes in VAS scores over time).ResultsThe GuttaCore group recorded the higher pain levels, except first 12 h, on the other hand, the GuttaFlow2 group recorded the lower pain levels at all time periods. Significant differences occurred among the groups during the first 4 days (p < 0.05), except at 12 h (p = 0.054). The patients in the CLC and GuttaFlow2 groups did not need to use the prescribed analgesic; however, one patient in the GuttaCore group used it once.ConclusionsPostoperative pain levels following root canal therapy were affected by the obturation technique especially first 4 days following obturation.

Dataset Information

Time-Dependent Effect of Chitosan Nanoparticles as Final Irrigation on the Apical Sealing Ability and Push-Out Bond Strength of Root Canal Obturation.

Publications

Time-Dependent Effect of Chitosan Nanoparticles as Final Irrigation on the Apical Sealing Ability and Push-Out Bond Strength of Root Canal Obturation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets