Micro Push-out Bond Strength and Bioactivity Analysis of a Bioceramic Root Canal Sealer.

ABSTRACT: Bioactive endodontic sealers have been developed to improve the quality of root canal obturation. EndoSequence Bioceramic (BC) Sealer is amongst calcium silicate-based materials recently developed for permanent root canal filling. The objective of this study was to evaluate the bioactivity of BC Sealer and its micro push-out bond strength to dentin compared to AH-Plus (AH) sealer.To perform the micro push-out test, 24 root canals of mandibular premolars were instrumented and divided into two groups (n=12). Each root was cut into 4 slices and lumens of the canals were filled with the sealers and submitted to micro push-out test. Failure mode was assessed using scanning electron microscopy (SEM). Bioactivity of BC sealer was investigated with scanning electron microscopy/energy-dispersive X-ray (SEM/EDS) and X-ray diffraction (XRD). Bioactivity assessments were reported descriptively. Bond strength data were analyzed by parametric t-test (α=5%).In micro push-out test AH had higher bond strength mean values (16.29 MPa) than BC sealer (9.48 MPa) (P<0.05). Both groups had low amount of adhesive failure. SEM showed the presence of a mineral precipitate after 30 days and EDS analysis showed that those precipitates have high proportion of Ca. XRD showed peaks of crystalline phases of calcium carbonate compatible with the bioactivity.BC sealer showed indications of bioactivity and lower bond strength to dentine compared to AH.

SUBMITTER: Carvalho CN

PROVIDER: S-EPMC5527212 | biostudies-other | 2017

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:IntroductionRoot canal sealing materials play a crucial role in an endodontic procedure by forming a bond between the dentinal walls and the gutta-percha. The current study aims to analyse the dentinal tubule penetration and adhesive pattern, including the push-out bond strength of six commercially available root canal sealers.MethodologyEighty-four mandibular first premolars were split into seven groups (and n = 12), Group 1: Dia-Root, Group 2: One-Fil, Group 3: BioRoot RCS, Group 4: AH Plus, Group 5: CeraSeal, Group 6: iRoot SP, Group 7: GP without sealer (control). Two groups were made, one for dentinal tubule penetration and the other for push-out bond strength; the total sample size was one hundred sixty-eight. Root canal treatment was performed using a method called the crown down technique, and for obturation, the single cone technique was used. A confocal laser scanning microscope (Leica, Microsystem Heidel GmbH, Version 2.00 build 0585, Germany) was used to evaluate dentinal tubule penetration, and Universal Testing Machine was utilised to measure the push-out bond strength (Shimadzu, Japan) using a plunger size of 0.4 mm and speed of 1mm/min. Finally, the adhesive pattern of the sealers was analysed by HIROX digital microscope (KH-7700). Statistical analysis was carried out by a one-way Anova test, Dunnet's T3 test, and Chi-square test.ResultsHighest dentinal tubule penetration was noticed with One-Fil (p<0.05), followed by iRoot SP, CeraSeal, AH Plus, Dia-Root also, the most negligible value was recorded for BioRoot RCS. Meanwhile, BioRoot RCS (p<0.05) demonstrated the greater value of mean push-out bond strength, followed by One-fil, iRoot SP, CeraSeal, AH Plus and Dia-Root. Regarding adhesive pattern, most of the samples were classified as type 3 and type 4 which implies greater sealing ability and better adherence to the dentinal wall. However, BioRoot RCS revealed the most type 4 (p<0.05), followed by AH Plus, One-Fil, CeraSeal and Dia-Root.ConclusionThe highest dentinal tubule penetration was shown by One-Fil compared to other groups. Meanwhile, BioRoot RCS had greater push-out bond strength and more adhesive pattern than other tested materials.

Dataset Information

Micro Push-out Bond Strength and Bioactivity Analysis of a Bioceramic Root Canal Sealer.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets