Change of Characterization and Film Morphology Based on Acrylic Pressure Sensitive Adhesives by Hydrophilic Derivative Ratio.

ABSTRACT: Hydrophilic acrylic pressure-sensitive adhesives (PSAs) were synthesized by controlling the contents of 2-ethylhexyl acrylate (EHA), isobornyl acrylate (IBOA), and 2-hydroxyethyl acrylate (HEA); especially, the characteristic change of the HEA content was analyzed. Surface contact angle of acrylic PSA film decreased from 77.87° to 70.23° in the case of Acryl-2 to Acryl-8 (below HEA 10 wt %). However, the surface contact angle of Acryl-10 to Acryl-40 (HEA 10 wt % to 40 wt %) increased up to 92.29°, indicating hydrophobicity. All acrylic PSA films showed high adhesive force above 1800 gf/25 mm. According to X-ray diffraction (XRD) measurement, hydrophilic acrylic PSAs exhibited amorphous property and it was confirmed that the morphology of acrylic PSA film was significantly affected by the flexibility of the polymer chain and the strength of hydrogen bonding. The affinity with hydrophilic materials for acrylic PSA films was evaluated by T-type peel test, confirming that the affinity with hydrophilic materials is determined by the hydrophilicity of the acrylic PSA film. The synthesized acrylic PSA film is non-toxic regardless of the hydrophilicity.

SUBMITTER: Seok WC

PROVIDER: S-EPMC7408043 | biostudies-literature | 2020 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Change of Characterization and Film Morphology Based on Acrylic Pressure Sensitive Adhesives by Hydrophilic Derivative Ratio.

Seok Woong Cheol WC Leem Jong Tae JT Kang Ju Hui JH Kim Young Jun YJ Lee Sangkug S Song Ho Jun HJ

Polymers 20200707 7

Hydrophilic acrylic pressure-sensitive adhesives (PSAs) were synthesized by controlling the contents of 2-ethylhexyl acrylate (EHA), isobornyl acrylate (IBOA), and 2-hydroxyethyl acrylate (HEA); especially, the characteristic change of the HEA content was analyzed. Surface contact angle of acrylic PSA film decreased from 77.87° to 70.23° in the case of Acryl-2 to Acryl-8 (below HEA 10 wt %). However, the surface contact angle of Acryl-10 to Acryl-40 (HEA 10 wt % to 40 wt %) increased up to 92.29 ...[more]

PMID: 32645817

Similar Datasets

Project description:Pressure-sensitive adhesives (PSAs) are usually made from viscoelastic, high-molecular-weight copolymers, which are fine-tuned by adjusting the comonomer ratios, molecular weights, and cross-link densities to optimize the adhesion properties for the desired end-use. To create a lightly cross-linked network, an ultraviolet (UV) photoinitiator can be incorporated. Here, we present the first use of perfluorophenylazide chemistry to control precisely a polyacrylate network for application as a PSA. Upon UV irradiation, the highly reactive nitrene from the azide moiety reacts with nearby molecules through a C-H insertion reaction, resulting in cross-linking via covalent bonding. This approach offers three benefits: (1) a means to optimize adhesive properties without the addition of an external photoinitiator; (2) the ability to switch off the tack adhesion on demand via a high cross-linking density; and (3) a platform for additional chemical modification. A series of poly(n-butyl acrylate-co-2,3,4,5,6-pentafluorobenzyl acrylate) or poly(PFBA-co-BA) copolymers were synthesized and modified post-polymerization into the photo-reactive poly(n-butyl acrylate-co-4-azido-2,3,5,6-tetrafluorobenzyl acrylate) [azide-modified poly(PFBA-co-BA)] with various molar contents. When cast into films, the azide-modified copolymers with a high azide content achieved a very high shear resistance after UV irradiation, whereas the tack and peel adhesion decreased strongly with the increase in azide content, indicating that excessive cross-linking occurred. These materials are thus photo-switchable. However, in the low range of azide content, an optimum probe tack adhesion energy was obtained in films with a 0.3 mol % azide content, where a long stress plateau (indicating good fibrillation) with a high plateau stress was observed. An optimum peel adhesion strength was achieved with 0.5 mol % azide. Thus, the adhesion was finely controlled by the degree of cross-linking of the PSA, as determined by the azide content of the copolymer chain. Finally, as a demonstration of the versatility and advantages of the material platform, we show an azide-aldehyde-amine multicomponent modification of the azide copolymer to make a dye-functionalized film that retains its adhesive properties. This first demonstration of using azide functionality has enormous potential for functional PSA design.

Dataset Information

Change of Characterization and Film Morphology Based on Acrylic Pressure Sensitive Adhesives by Hydrophilic Derivative Ratio.

Publications

Change of Characterization and Film Morphology Based on Acrylic Pressure Sensitive Adhesives by Hydrophilic Derivative Ratio.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets