Adhesion Improvement of Solvent-Free Pressure-Sensitive Adhesives by Semi-IPN Using Polyurethanes and Acrylic Polymers.

ABSTRACT: To improve the peel strength and holding time of polypropylene glycol (PPG)-based pressure-sensitive adhesives (PSAs), a semi-interpenetrating polymer network (semi-IPN) was prepared using acrylic polymers. In addition, to prevent air pollution due to volatile organic compound emissions and avoid the degradation of physical properties due to a residual solvent, the PPG-based semi-IPN PSAs were fabricated by an eco-friendly solvent-free method using an acrylic monomer instead of an organic solvent. PPG-based semi-IPN PSAs with different hard segment contents (2.9-17.2%) were synthesized; their holding time was found to depend on the hard segment contents. The peel strength was improved because of the formation of the semi-IPN structure. Moreover, the high degree of hard domain formation in the semi-IPN PSA, derived from the increase in the hard segment content using a chain extender, resulted in a holding time improvement. We believe that the as-prepared PSAs can be used in various applications that require high creep resistance.

SUBMITTER: Park KH

PROVIDER: S-EPMC9571291 | biostudies-literature | 2022 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Adhesion Improvement of Solvent-Free Pressure-Sensitive Adhesives by Semi-IPN Using Polyurethanes and Acrylic Polymers.

Park Kwang Hun KH Lee Dong Yeob DY Yoon Sung Ha SH Kim Seong Hun SH Han Min Su MS Jeon Seungju S Kim Yejin Y Lim Yong Kwan YK Hwang Do-Hoon DH Jung Seo-Hyun SH Lim Bogyu B

Polymers 20220922 19

To improve the peel strength and holding time of polypropylene glycol (PPG)-based pressure-sensitive adhesives (PSAs), a semi-interpenetrating polymer network (semi-IPN) was prepared using acrylic polymers. In addition, to prevent air pollution due to volatile organic compound emissions and avoid the degradation of physical properties due to a residual solvent, the PPG-based semi-IPN PSAs were fabricated by an eco-friendly solvent-free method using an acrylic monomer instead of an organic solven ...[more]

PMID: 36235911

Similar Datasets

Project description:Pressure sensitive adhesives made with blends of thermoplastic polyurethanes (TPUs PSAs) with satisfactory tack, cohesion, and adhesion have been developed. A simple procedure consisting of the physical blending of methyl ethyl ketone (MEK) solutions of two thermoplastic polyurethanes (TPUs) with very different properties-TPU1 and TPU2-was used, and two different blending procedures have been employed. The TPUs were characterized by infra-red spectroscopy in attenuated total reflectance mode (ATR-IR spectroscopy), differential scanning calorimetry, thermal gravimetric analysis, and plate-plate rheology (temperature and frequency sweeps). The TPUs PSAs were characterized by tack measurement, creep test, and the 180° peel test at 25 °C. The procedure for preparing the blends of the TPUs determined differently their viscoelastic properties, and the properties of the TPUs PSAs as well, the blending of separate MEK solutions of the two TPUs imparted higher tack and 180° peel strength than the blending of the two TPUs in MEK. TPU1 + TPU2 blends showed somewhat similar contributions of the free and hydrogen-bonded urethane groups and they had an almost similar degree of phase separation, irrespective of the composition of the blend. Two main thermal decompositions at 308-317 °C due to the urethane hard domains and another at 363-373 °C due to the soft domains could be distinguished in the TPU1 + TPU2 blends, the weight loss of the hard domains increased and the one of the soft domains decreased by increasing the amount of TPU2 in the blends. The storage moduli of the TPU1 + TPU2 blends were similar for temperatures lower than 20 °C and the moduli at the cross over of the moduli were lower than in the parent TPUs. The improved properties of the TPU1 + TPU2 blends derived from the creation of a higher number of hydrogen bonds upon removal of the MEK solvent, which lead to a lower degree of phase separation between the soft and the hard domains than in the parent TPUs. As a consequence, the properties of the TPU1 + TPU2 PSAs were improved because good tack, high 180° peel strength, and sufficient cohesion were obtained, particularly in 70 wt% TPU1 + 30 wt% TPU2 PSA.

Project description:For polyacrylate latex pressure-sensitive adhesives (PSAs), high peel strength is of crucial significance. It is not only a key factor for ensuring the long-lasting and effective adhesive force of polyacrylate latex PSAs but also can significantly expand their application scope in many vital fields, such as packaging, electronics, and medical high-performance composite materials. High peel strength can guarantee that the products maintain stable and reliable adhesive performance under complex and variable environmental conditions. However, at present, the peel strength capacity of polyacrylate latex PSAs is conspicuously insufficient, making it difficult to fully meet the urgent market demand for high peel strength, and severely restricting their application in many cutting-edge fields. Therefore, based on previous experimental studies, and deeply inspired by the adhesion mechanism of natural marine mussels, in this study, a traditional polyacrylate latex PSA was ingeniously graft-modified with 3,4-dihydroxybenzaldehyde (DHBA) through the method of monomer-starved seeded semi-continuous emulsion polymerization, successfully synthesizing novel high-peel-strength polyacrylate latex pressure-sensitive adhesives (HPSAs) with outstanding strong adhesion properties, and the influence of DHBA content on the properties of the HPSAs was comprehensively studied. The research results indicated that the properties of the modified HPSAs were comprehensively enhanced. Regarding the water resistance of the adhesive film, the minimum water absorption rate was 4.33%. In terms of the heat resistance of the adhesive tape, it could withstand heat at 90 °C for 1 h without leaving residue upon tape peeling. Notably, the adhesive properties were significantly improved, and when the DHBA content reached 4.0%, the loop tack and 180° peel strength of HPSA4 significantly increased to 5.75 N and 825.4 gf/25 mm, respectively, which were 2.5 times and 2 times those of the unmodified PSA, respectively. Such superior adhesive performance of HPSAs, on the one hand, should be attributed to the introduction of the bonding functional monomer DHBA with a rich polyphenol structure; on the other hand, the acetal structure formed by the grafting reaction of DHBA with the PSA effectively enhanced the spatial network and crosslink density of the HPSAs. In summary, in this study, the natural biological adhesion phenomenon was ingeniously utilized to increase the peel strength of pressure-sensitive adhesives, providing a highly forward-looking and feasible direct strategy for the development of environmentally friendly polyacrylate latex pressure-sensitive adhesives.

Dataset Information

Adhesion Improvement of Solvent-Free Pressure-Sensitive Adhesives by Semi-IPN Using Polyurethanes and Acrylic Polymers.

Publications

Adhesion Improvement of Solvent-Free Pressure-Sensitive Adhesives by Semi-IPN Using Polyurethanes and Acrylic Polymers.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets