Effect of Polishing on Electrochemical Behavior and Passive Layer Composition of Different Stainless Steels.

ABSTRACT: In the present paper, the effect of different polishing methods (mechanical and electrochemical) on passive layer chemistry and the corrosion behavior of stainless steels is investigated. It was found that CrNiMo austenites have a substantially better corrosion behavior than CrMnN ones. The nickel is enriched underneath the passive layer, while manganese tends to be enriched in the passive layer. It was also noted that immersion of manganese into an electrolyte preferentially causes its dissolution. It was found that high amounts of chromium (27.4%), molybdenum (3.3%), nickel (29.4%), with the addition of manganese (2.8%) after mechanical grinding, generates a better corrosion resistance than after electrochemical polishing. This is most likely because of the introduction of phosphates and sulfates into its structure, which is known for steels with a high amount of manganese. For highly alloyed CrNiMo steels, which do not contain a high amount of manganese, the addition of phosphates and/or sulphates via the electropolishing process results in a decrease in pitting corrosion resistance, which is also observed for high manganese steels. Electropolished samples show detrimental corrosion properties when compared to mechanically polished samples. This is attributed to substantial amounts of sulfate and phosphate from the electropolishing electrolyte present in the surface of the passive layer.

SUBMITTER: Rokosz K

PROVIDER: S-EPMC7435799 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of Polishing on Electrochemical Behavior and Passive Layer Composition of Different Stainless Steels.

Rokosz Krzysztof K Solecki Grzegorz G Mori Gregor G Fluch Rainer R Kapp Marianne M Lahtinen Jouko J

Materials (Basel, Switzerland) 20200801 15

In the present paper, the effect of different polishing methods (mechanical and electrochemical) on passive layer chemistry and the corrosion behavior of stainless steels is investigated. It was found that CrNiMo austenites have a substantially better corrosion behavior than CrMnN ones. The nickel is enriched underneath the passive layer, while manganese tends to be enriched in the passive layer. It was also noted that immersion of manganese into an electrolyte preferentially causes its dissolut ...[more]

PMID: 32752187

Similar Datasets

Project description:BACKGROUND:Increased composite roughness enhances bacterial adhesion and discoloration, thus increasing the risk of gingival inflammation and secondary caries. Concerns about detrimental effects of sodium bicarbonate on surface roughness influenced the development of less abrasive powders: a glycine-based powder and an erythritol-based powder, additionally - sodium bicarbonate-based powder of reduced grain size. However, there is limited evidence on effects of these materials on the surface of dental fillings. The aim of the present study was to compare the effects of three air-polishing powders (of a reduced abrasiveness) on surface roughness of microhybrid restorative composite material. MATERIAL AND METHODS:Microhybrid light-cure resin composite samples were placed on 64 plaster cubes and light-cured through polyester strips. Surface roughness was measured using laser confocal microscope (magnification 2160x). The specimens were randomly divided into three groups (n = 20, 20 and 24) and air-polished with: sodium bicarbonate (40 μm), glycine (25 μm) and erythritol (14 μm), respectively. Then surface roughness was remeasured, keeping the same field of observation. Specialized 3D analysis software was used for data processing. Parameters according to ISO 25178: Sa, Sq, Sku, Sp, Sv, Sz, Ssk were used to describe surface roughness. RESULTS:Sa, Sq, Sp, Sv, Sz increased significantly following air polishing. Ssk was significantly higher, whereas Sku was significantly lower in sodium bicarbonate and erythritol groups than before air polishing. Comparison between the three powders revealed that Sa was significantly higher in sodium bicarbonate group than in glycine group. Sku was significantly higher in glycine and erythritol groups than in sodium bicarbonate group. CONCLUSIONS:Sodium bicarbonate has a stronger detrimental effect on composite surface than glycine or erythritol. No advantage of erythritol comparing to glycine could be found.

Dataset Information

Effect of Polishing on Electrochemical Behavior and Passive Layer Composition of Different Stainless Steels.

Publications

Effect of Polishing on Electrochemical Behavior and Passive Layer Composition of Different Stainless Steels.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets