A Two-Year Evaluation of Corrosion-Induced Damage to Hot Galvanized Reinforcing Steel B500SP in Chloride Contaminated Concrete.

ABSTRACT: Corrosion-induced damage to concrete reinforced with bars is a serious problem regarding technical and economic aspects and strongly depends on used materials, corrosion environment, and service life. Tests described in this paper refer to a two-year evaluation of the effectiveness of protection provided by zinc-coated low-carbon reinforcing steel of grade B500SP in concrete against chloride corrosion. Performed tests were comparative and included measurements conducted on four groups of concrete test elements with dimensions of 40 mm × 40 mm × 140 mm reinforced with a bar having a diameter of ?8 mm. Particular groups were a combination of different types of concrete with or without chloride additives, with galvanized or black steel. Chlorides as CaCl2 were added to the concrete mix in the amount of 3% of cement weight in concrete. Reinforced concrete specimens were periodically monitored within two years using the following techniques: linear polarization resistance (LPR) and electrochemical impedance spectroscopy (EIS). Polarization measurements were conducted in a three-electrode arrangement, in which a rebar in concrete served as a working electrode, stainless steel sheet was used as an auxiliary electrode, and Cl-/AgCl,Ag was a reference electrode. Comparative tests of changes in the density of corrosion current in concrete specimens without chloride additives basically demonstrated no development of corrosion, and possible passivation was expected in case of black steel. Higher densities of corrosion current were observed for galvanized steel during first days of testing. The reason was the dissolution of zinc after the contact with initially high pH of concrete pore solution. Six-month measurements demonstrated a higher density of corrosion current in concrete specimens with high concentration of chlorides, which unambiguously indicated corrosion in concrete reinforced with galvanized or black steel. Densities of corrosion current determined for selected specimens dramatically decreased after an 18-month interval in measurements. Corrosion was even inhibited on black steel as an insulating barrier of corrosion products was formed. The above observations were confirmed with structural studies using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) techniques. Results obtained from corrosion (LPR, EIS) and structural (SEM, EDS) tests on specimens of concrete reinforced with steel B500SP demonstrated a very favorable impact of zinc coating on steel by providing two-year protection against corrosion in the environment with very high chloride content.

SUBMITTER: Jasniok M

PROVIDER: S-EPMC7435989 | biostudies-literature | 2020 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

A Two-Year Evaluation of Corrosion-Induced Damage to Hot Galvanized Reinforcing Steel B500SP in Chloride Contaminated Concrete.

Jaśniok Mariusz M Sozańska Maria M Kołodziej Jacek J Chmiela Bartosz B

Materials (Basel, Switzerland) 20200725 15

Corrosion-induced damage to concrete reinforced with bars is a serious problem regarding technical and economic aspects and strongly depends on used materials, corrosion environment, and service life. Tests described in this paper refer to a two-year evaluation of the effectiveness of protection provided by zinc-coated low-carbon reinforcing steel of grade B500SP in concrete against chloride corrosion. Performed tests were comparative and included measurements conducted on four groups of concret ...[more]

PMID: 32722437

Similar Datasets

Project description:IntroductionCorrosion-induced deterioration of infrastructure is a growing global concern. The development and application of corrosion inhibitors are one of the most effective approaches to protect steel rebar from corrosion. Hence, this study focuses on a novel hydrazone derivative, (E)-N'-(4-(dimethylamino)benzylidene)-2-(5-methoxy-2-methyl-1H-indol-3-yl)aceto-hydrazide (HIND), and its potential application to mitigate corrosion in steel rebar exposed to chloride-contaminated concrete pore solutions (ClSCPS).ObjectivesThe research aims to evaluate the anti-corrosion capabilities of HIND on steel rebar within a simulated corrosive environment, focusing on the mechanisms of its inhibitory effect.MethodsThe corrosion of steel rebar exposed to the ClSCPS was studied through weight loss and electrochemical methods. The surface morphology of steel rebar surface was characterized by FE-SEM-EDS, AFM; oxidation states of the steel rebar and crystal structures were examined using X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) methods. Further, experimental findings were complemented by theoretical studies using self-consistent-charge density-functional tight-binding (SCC-DFTB) simulations. The performance of HIND was monitored at an optimal concentration over a period of 30 days.ResultsThe results indicated a significant reduction in steel rebar corrosion upon introducing HIND. The inhibitor molecules adhered to the steel surface, preventing further deterioration and achieving an inhibition efficiency of 88.4% at 0.5 mmol/L concentration. The surface morphology analysis confirmed the positive effect of HIND on the rebar surface, showing a decrease in the surface roughness of the steel rebar from 183.5 in uninhibited to 50 nm in inhibited solutions. Furthermore, SCC-DFTB simulations revealed the presence of coordination between iron atoms and HIND active sites.ConclusionThe findings demonstrate the potential of HIND as an effective anti-corrosion agent in chloride-contaminated environments. Its primary adsorption mechanism involves charge transfer from the inhibitor molecules to iron atoms. Therefore, applying HIND could be an effective strategy to address corrosion-related challenges in reinforced infrastructure.

Dataset Information

A Two-Year Evaluation of Corrosion-Induced Damage to Hot Galvanized Reinforcing Steel B500SP in Chloride Contaminated Concrete.

Publications

A Two-Year Evaluation of Corrosion-Induced Damage to Hot Galvanized Reinforcing Steel B500SP in Chloride Contaminated Concrete.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets