Lignin Refinery Using Organosolv Process for Nanoporous Carbon Synthesis.

ABSTRACT: Porous carbon has been widely used for many applications e.g., adsorbents, catalysts, catalyst supports, energy storage and gas storage due to its outstanding properties. In this paper, characteristics of porous carbon prepared by carbonization of lignin from various biomasses are presented. Various biomasses, i.e., mangosteen peel, corncob and coconut shell, were processed using ethanol as an organosolv solvent. The obtained lignin was characterized using a Fourier transform infrared (FTIR) spectrophotometer and a viscosimeter to investigate the success of extraction and lignin properties. The results showed that high temperature is favorable for the extraction of lignin using the organosolv process. The FTIR spectra show the success of lignin extraction using the organosolv process because of its similarity to the standard lignin spectra. The carbonization process of lignin was performed at 600 and 850 °C to produce carbon from lignin, as well as to investigate the effect of temperature. A higher pyrolysis temperature will produce a porous carbon with a high specific surface area, but it will lower the yield of the produced carbon. At 850 °C temperature, the highest surface area up to 974 m2/g was achieved.

SUBMITTER: Prasetyo I

PROVIDER: S-EPMC7435991 | biostudies-literature | 2020 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Lignin Refinery Using Organosolv Process for Nanoporous Carbon Synthesis.

Prasetyo Imam I Permatasari Puspita Rahayu PR Laksmana William Teja WT Rochmadi Rochmadi R Oh Won-Chun WC Ariyanto Teguh T

Molecules (Basel, Switzerland) 20200728 15

Porous carbon has been widely used for many applications e.g., adsorbents, catalysts, catalyst supports, energy storage and gas storage due to its outstanding properties. In this paper, characteristics of porous carbon prepared by carbonization of lignin from various biomasses are presented. Various biomasses, i.e., mangosteen peel, corncob and coconut shell, were processed using ethanol as an organosolv solvent. The obtained lignin was characterized using a Fourier transform infrared (FTIR) spe ...[more]

PMID: 32731572

Similar Datasets

Project description:Lignin, being one of the main structural components of lignocellulosic biomass, is considered the most abundant natural source of phenolics and aromatics. Efforts for its valorisation were recently explored as it is mostly treated as waste from heat/energy production via combustion. Among them, polymer-based lignin composites are a promising approach to both valorise lignin and to fine tune the properties of polymers. In this work, organosolv lignin, from beech wood, was used as fillers in a poly (lactic acid) (PLA) matrix. The PLA/lignin composites were prepared using melt mixing of masterbatches with neat PLA in three different lignin contents: 0.5, 1.0 and 2.5 wt%. Lignin was used as-isolated, via the organosolv biomass pretreatment/fractionation process and after 8 h of ball milling. The composites were characterised with Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR) spectroscopy, X-ray Diffraction (XRD), and Differential Scanning Calorimetry (DSC). Additionally, their antioxidant activity was assessed with the 2,2-Diphenyil-1-picrylhydrazyl (DPPH) method, the colour was measured with a colorimeter and the mechanical properties were evaluated with tensile testing. Ball milling, at least under the conditions applied in this study, did not induce a further substantial decrease in the already relatively small organosolv lignin primary particles of ~1 μm. All the produced PLA/lignin composites had a uniform dispersion of lignin. Compression-moulded films were successfully prepared, and they were coloured brown, with ball-milled lignin, giving a slightly lighter colour in comparison with the as-received lignin. Hydrogen bonding was detected between the components of the composites, and crystallization of the PLA was suppressed by both lignin, with the suppression being less pronounced by the ball-milled lignin. All composites showed a significantly improved antioxidant activity, and their mechanical properties were maintained for filler content 1 wt%.

Dataset Information

Lignin Refinery Using Organosolv Process for Nanoporous Carbon Synthesis.

Publications

Lignin Refinery Using Organosolv Process for Nanoporous Carbon Synthesis.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets