Accelerated Weathering Effects on Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and PHBV/TiO2 Nanocomposites.

ABSTRACT: The effect of accelerated weathering on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and PHBV-based nanocomposites with rutile titanium (IV) dioxide (PHBV/TiO2) was investigated. The accelerated weathering test applied consecutive steps of UV irradiation (at 340 nm and 0.76 W m-2 irradiance) and moisture at 50 °C following the ASTM D4329 standard for up to 2000 h of exposure time. The morphology, chemical structure, crystallization, as well as the mechanical and thermal properties were studied. Samples were characterized after 500, 1000, and 2000 h of exposure time. Different degradation mechanisms were proposed to occur during the weathering exposure and were confirmed based on the experimental data. The PHBV surface revealed cracks and increasing roughness with the increasing exposure time, whereas the PHBV/TiO2 nanocomposites showed surface changes only after 2000 h of accelerated weathering. The degradation of neat PHBV under moisture and UV exposure occurred preferentially in the amorphous phase. In contrast, the presence of TiO2 in the nanocomposites retarded this process, but the degradation would occur simultaneously in both the amorphous and crystalline segments of the polymer after long exposure times. The thermal stability, as well as the temperature and rate of crystallization, decreased in the absence of TiO2. TiO2 not only provided UV protection, but also restricted the physical mobility of the polymer chains, acting as a nucleating agent during the crystallization process. It also slowed down the decrease in mechanical properties. The mechanical properties were shown to gradually decrease for the PHBV/TiO2 nanocomposites, whereas a sharp drop was observed for the neat PHBV after an accelerated weathering exposure. Atomic force microscopy (AFM), using the amplitude modulation-frequency modulation (AM-FM) tool, also confirmed the mechanical changes in the surface area of the PHBV and PHBV/TiO2 samples after accelerated weathering exposure. The changes in the physical and chemical properties of PHBV/TiO2 confirm the barrier activity of TiO2 for weathering attack and its retardation of the degradation process.

SUBMITTER: Antunes A

PROVIDER: S-EPMC7464598 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Accelerated Weathering Effects on Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and PHBV/TiO2 Nanocomposites.

Antunes Ana A Popelka Anton A Aljarod Omar O Hassan Mohammad K MK Kasak Peter P Luyt Adriaan S AS

Polymers 20200805 8

The effect of accelerated weathering on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and PHBV-based nanocomposites with rutile titanium (IV) dioxide (PHBV/TiO2) was investigated. The accelerated weathering test applied consecutive steps of UV irradiation (at 340 nm and 0.76 W m-2 irradiance) and moisture at 50 °C following the ASTM D4329 standard for up to 2000 h of exposure time. The morphology, chemical structure, crystallization, as well as the mechanical and ther ...[more]

PMID: 32764247

Similar Datasets

Project description:Poly(hydroxybutyrate-co-hydroxyhexanoate) [P(HB-co-HHx)] and poly(hydroxybutyrate-co-hydroxyvalerate-co-hydroxyhexanoate) [P(HB-co-HV-co-HHx)] demonstrate interesting mechanical and thermal properties as well as excellent biocompatibility, making them suitable for multiple applications and notably biomedical purposes. The production of such polymers was described in Rhodospirillum rubrum, a purple nonsulfur bacteria in a nutrient-lacking environment where the HHx synthesis is triggered by the presence of hexanoate in the medium. However, the production of P(HB-co-HHx) under nutrient-balanced growth conditions in R. rubrum has not been described so far, and the assimilation of hexanoate is poorly documented. In this study, we used proteomic analysis and a mutant fitness assay to demonstrate that hexanoate assimilation involve β-oxidation and the ethylmalonyl-coenzyme A (CoA) (EMC) and methylbutanoyl-CoA (MBC) pathways, both being anaplerotic pathways already described in R. rubrum. Polyhydroxyalkanoate (PHA) production is likely to involve the de novo fatty acid synthesis pathway. Concerning the polymer composition, HB is the main component of the polymer, probably as acetyl-CoA and butyryl-CoA are intermediates of hexanoate assimilation pathways. When no essential nutrient is lacking in the medium, the synthesis of PHA seems to help maintain the redox balance of the cell. In this framework, we showed that the fixation of CO2 is required to sustain the growth. An increase in the proportion of HHx in the polymer was observed when redox stress was engendered in the cell under bicarbonate-limiting growth conditions. The addition of isoleucine or valerate in the medium also increased the HHx content of the polymer and allowed the production of a terpolymer of P(HB-co-HV-co-HHx). IMPORTANCE The use of purple bacteria, which can assimilate volatile fatty acids, for biotechnological applications has increased, since they reduce the production costs of added-value compounds such as PHA. P(HB-co-HHx) and P(HB-co-HV-co-HHx) have demonstrated interesting properties, notably for biomedical applications. In a nutrient-lacking environment, R. rubrum is known to synthesize such polymers when hexanoate is used as the carbon source. However, their production in R. rubrum in non-nutrient-lacking growth conditions has not been described so far, and the assimilation of hexanoate is poorly documented. As the carbon source and its assimilation directly impact the polymer composition, we studied under non-nutrient-lacking growth conditions the assimilation pathway of hexanoate and PHA production in R. rubrum. Proteomic analysis and mutant fitness assays allowed us to explain PHA production and composition. An increase in HHx content of the polymer and production of P(HB-co-HV-co-HHx) was possible using the knowledge gained on metabolism under hexanoate growth conditions.

Dataset Information

Accelerated Weathering Effects on Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and PHBV/TiO2 Nanocomposites.

Publications

Accelerated Weathering Effects on Poly(3-hydroxybutyrate-<i>co</i>-3-hydroxyvalerate) (PHBV) and PHBV/TiO<sub>2</sub> Nanocomposites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets