Experimental data for extrusion processing and tensile properties of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) polymer and wood fibre reinforced PHBV biocomposites.

ABSTRACT: This article features a large database on different extrusion processing conditions and the resulting tensile properties of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) and wood fibre reinforced biocomposites. The data presented here corresponds to a comprehensive design of experiments conducted separately for both neat PHBV polymer and wood-PHBV composites, in which the effects of temperature profile, screw speed, feeding rate, feeding method, screw configuration, and wood contents (wood-PHBV composites only) of 10, 20, 30, and 40?wt% wood content were examined. For each processing condition, 5 specimens were tested under uniaxial tensile loading. Here we provide the complete set of extrusion parameters, including the observed screw torque, residence time and material output. Individual stress-strain curves for each specimens are provided, along with their calculated elastic modulus, strength, and strain at maximum load. The data is also provided as support material for the research article: "Extrusion of wood fibre reinforced Poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) biocomposites: statistical analysis of the effect of processing conditions on mechanical performance" (Vandi et al., 2018).

SUBMITTER: Vandi LJ

PROVIDER: S-EPMC6327731 | biostudies-literature | 2019 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Experimental data for extrusion processing and tensile properties of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) polymer and wood fibre reinforced PHBV biocomposites.

Vandi Luigi-Jules LJ Chan Clement Matthew CM Werker Alan A Richardson Des D Laycock Bronwyn B Pratt Steven S

Data in brief 20181229

This article features a large database on different extrusion processing conditions and the resulting tensile properties of poly(hydroxybutyrate-<i>co</i>-hydroxyvalerate) (PHBV) and wood fibre reinforced biocomposites. The data presented here corresponds to a comprehensive design of experiments conducted separately for both neat PHBV polymer and wood-PHBV composites, in which the effects of temperature profile, screw speed, feeding rate, feeding method, screw configuration, and wood contents (w ...[more]

PMID: 30671517

Similar Datasets

Project description:The effect of accelerated weathering on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and PHBV-based nanocomposites with rutile titanium (IV) dioxide (PHBV/TiO2) was investigated. The accelerated weathering test applied consecutive steps of UV irradiation (at 340 nm and 0.76 W m-2 irradiance) and moisture at 50 °C following the ASTM D4329 standard for up to 2000 h of exposure time. The morphology, chemical structure, crystallization, as well as the mechanical and thermal properties were studied. Samples were characterized after 500, 1000, and 2000 h of exposure time. Different degradation mechanisms were proposed to occur during the weathering exposure and were confirmed based on the experimental data. The PHBV surface revealed cracks and increasing roughness with the increasing exposure time, whereas the PHBV/TiO2 nanocomposites showed surface changes only after 2000 h of accelerated weathering. The degradation of neat PHBV under moisture and UV exposure occurred preferentially in the amorphous phase. In contrast, the presence of TiO2 in the nanocomposites retarded this process, but the degradation would occur simultaneously in both the amorphous and crystalline segments of the polymer after long exposure times. The thermal stability, as well as the temperature and rate of crystallization, decreased in the absence of TiO2. TiO2 not only provided UV protection, but also restricted the physical mobility of the polymer chains, acting as a nucleating agent during the crystallization process. It also slowed down the decrease in mechanical properties. The mechanical properties were shown to gradually decrease for the PHBV/TiO2 nanocomposites, whereas a sharp drop was observed for the neat PHBV after an accelerated weathering exposure. Atomic force microscopy (AFM), using the amplitude modulation-frequency modulation (AM-FM) tool, also confirmed the mechanical changes in the surface area of the PHBV and PHBV/TiO2 samples after accelerated weathering exposure. The changes in the physical and chemical properties of PHBV/TiO2 confirm the barrier activity of TiO2 for weathering attack and its retardation of the degradation process.

Dataset Information

Experimental data for extrusion processing and tensile properties of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) polymer and wood fibre reinforced PHBV biocomposites.

Publications

Experimental data for extrusion processing and tensile properties of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) polymer and wood fibre reinforced PHBV biocomposites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure