Cu/CuO Composite Track-Etched Membranes for Catalytic Decomposition of Nitrophenols and Removal of As(III).

ABSTRACT: One of the promising applications of nanomaterials is to use them as catalysts and sorbents to remove toxic pollutants such as nitroaromatic compounds and heavy metal ions for environmental protection. This work reports the synthesis of Cu/CuO-deposited composite track-etched membranes through low-temperature annealing and their application in catalysis and sorption. The synthesized Cu/CuO/poly(ethylene terephthalate) (PET) composites presented efficient catalytic activity with high conversion yield in the reduction of nitro aryl compounds to their corresponding amino derivatives. It has been found that increasing the time of annealing raises the ratio of the copper(II) oxide (CuO) tenorite phase in the structure, which leads to a significant increase in the catalytic activity of the composites. The samples presented maximum catalytic activity after 5 h of annealing, where the ratio of CuO phase and the degree of crystallinity were 64.3% and 62.7%, respectively. The catalytic activity of pristine and annealed composites was tested in the reduction of 4-nitroaniline and was shown to remain practically unchanged for five consecutive test cycles. Composites annealed at 140 °C were also tested for their capacity to absorb arsenic(III) ions in cross-flow mode. It was observed that the sorption capacity of composite membranes increased by 48.7% compared to the pristine sample and reached its maximum after 10 h of annealing, then gradually decreased by 24% with further annealing.

SUBMITTER: Mashentseva AA

PROVIDER: S-EPMC7466412 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Cu/CuO Composite Track-Etched Membranes for Catalytic Decomposition of Nitrophenols and Removal of As(III).

Mashentseva Anastassiya A AA Barsbay Murat M Zdorovets Maxim V MV Zheltov Dmitriy A DA Güven Olgun O

Nanomaterials (Basel, Switzerland) 20200807 8

One of the promising applications of nanomaterials is to use them as catalysts and sorbents to remove toxic pollutants such as nitroaromatic compounds and heavy metal ions for environmental protection. This work reports the synthesis of Cu/CuO-deposited composite track-etched membranes through low-temperature annealing and their application in catalysis and sorption. The synthesized Cu/CuO/poly(ethylene terephthalate) (PET) composites presented efficient catalytic activity with high conversion y ...[more]

PMID: 32784726

Similar Datasets

Project description:The synthesis of optoelectrically enhanced nanomaterials should be continuously improved by employing time- and energy-saving techniques. The porous zinc oxide (ZnO) and copper-doped ZnO nanocomposites (NCs) were synthesized by the time- and energy-efficient solution combustion synthesis (SCS) approach. In this SCS approach, once the precursor-surfactant complex ignition point is reached, the reaction starts and ends within a short time without the need for any external energy. The TGA-DTA analysis confirmed that 500 °C was the point at which stable metal oxide was obtained. The doping and heterojunction strategy improved the optoelectric properties of the NCs more than the individual constituents, which then enhanced the materials' charge transfer and optical absorption capabilities. The porosity, nanoscale crystallite size (15-50 nm), and formation of Cu/CuO-ZnO NCs materials were confirmed from the XRD, SEM, and TEM/HRTEM analyses. The obtained d-spacing values of 0.275 and 0.234 nm confirm the formation of ZnO and CuO crystals, respectively. The decrease in photoluminescence intensity for the doped NCs corroborates a reduction in electron-hole recombination. On the Mott-Schottky analysis, the positive slope for ZnO confirms the n-type character, while the negative and positive slopes of the NCs confirm the p- and n-type characters, respectively. A diffusion-controlled type of charge transfer process on the electrode surface was confirmed from the cyclic voltammetric analysis. Thus, the overall analysis shows the applicability of the less expensive and more efficient SCS for several applications, such as catalysis and sensors. To confirm this, an organic catalytic reduction reaction of 4-nitrophenol to 4-aminophenol was tested. Within three and a half minutes, the catalytic reduction result showed the great potential of NCs over ZnO NPs. Thus, the energy- and time-saving SCS approach has a great future outlook as an industrial pollutant catalytic reduction application.

Dataset Information

Cu/CuO Composite Track-Etched Membranes for Catalytic Decomposition of Nitrophenols and Removal of As(III).

Publications

Cu/CuO Composite Track-Etched Membranes for Catalytic Decomposition of Nitrophenols and Removal of As(III).

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets