Kinetic and Isotherm Study of As(III) Removal from Aqueous Solution by PET Track-Etched Membranes Loaded with Copper Microtubes.

ABSTRACT: This paper reports on the synthesis and structure elucidation of track-etched membranes (TeMs) with electrolessly deposited copper microtubes (prepared in etched-only and oxidized polyethylene terephthalate (PET) TeMs), as well as on the comparative testing of arsenic (III) ion removal capacities through bath adsorption experiments. The structure and composition of composites were investigated by X-ray diffraction technique and scanning electron and atomic force microscopies. It was determined that adsorption followed pseudo-second-order kinetics, and the adsorption rate constants were calculated. A comparative study of the applicability of the adsorption models of Langmuir, Freundlich, and Dubinin-Radushkevich was carried out in order to describe the experimental isotherms of the prepared composite TeMs. The constants and parameters of all of the above equations were determined. By comparing the regression coefficients R², it was shown that the Freundlich model describes the experimental data on the adsorption of arsenic through the studied samples better than others. Free energy of As(III) adsorption on the samples was determined using the Dubinin-Radushkevich isotherm model and was found to be 17.2 and 31.6 kJ/mol for Cu/PET and Cu/Ox_PET samples, respectively. The high EDr value observed for the Cu/Ox_PET composite indicates that the interaction between the adsorbate and the composite is based on chemisorption.

SUBMITTER: Russakova AV

PROVIDER: S-EPMC7914724 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Kinetic and Isotherm Study of As(III) Removal from Aqueous Solution by PET Track-Etched Membranes Loaded with Copper Microtubes.

Russakova Alyona V AV Altynbaeva Liliya Sh LS Barsbay Murat M Zheltov Dmitriy A DA Zdorovets Maxim V MV Mashentseva Anastassiya A AA

Membranes 20210206 2

This paper reports on the synthesis and structure elucidation of track-etched membranes (TeMs) with electrolessly deposited copper microtubes (prepared in etched-only and oxidized polyethylene terephthalate (PET) TeMs), as well as on the comparative testing of arsenic (III) ion removal capacities through bath adsorption experiments. The structure and composition of composites were investigated by X-ray diffraction technique and scanning electron and atomic force microscopies. It was determined t ...[more]

PMID: 33562130

Similar Datasets

Project description:Oil palm trunk (OPT) represents one of the five main oil palm biomass wastes with high carbon content that can be economically converted to a large surface area, porous activated carbon (AC) adsorbent to treat palm oil mill effluent wastewater in Indonesia and Malaysia. In the first portion of this work, the design of the experiment was used to determine the optimum set of synthesis parameters required to maximize the iodine number of AC [i.e., Brunauer-Emmett-Teller (BET) specific surface area indicator] prepared from OPT via chemical activation route using H3PO4. The iodine numbers of AC and AC yield were probed as the impregnation ratio, the activation time, and the activation temperature were varied in the range of 0.28-3.47, 5.68-69.32 min, and 379-521 °C, respectively. An impregnation ratio of 2.29, an activation time of 6 min, and an activation temperature of 450 °C were identified as the optimum set of synthesis parameters. In the second portion of the work, the AC synthesized using the optimum parameters were then characterized and tested as an adsorbent for tannin. N2 sorption results revealed that the AC exhibits type IV isotherm, that is, contains micropores and mesopores and displays a relatively high BET specific surface area of 1657 m2 g-1. Adsorption equilibria isotherms for tannin adsorption onto the AC were collected at three different pH of 2, 4, and 6 and were nonlinearly fitted using Langmuir and Freundlich isotherm models, where the Langmuir isotherm gave better fitting than Freundlich. The higher adsorption capacity at lower pH can be explained in terms of the absence of electrostatic repulsion interaction between the AC surface and the tannic acid species as suggested by the point of zero charges (pHpzc) of 4.8 and an increasing ionization of tannic acid with pH rise between 4 and 7. Adsorption kinetics data were also obtained at four different pH of 2, 4, 6, and 8 where the nonlinear pseudo-first-order model best fitted the kinetic at pH of 2 and the nonlinear pseudo-second-order model represented the kinetic best at the remaining higher pH, which suggests that tannin adsorption onto AC occurred by physisorption at pH of 2 and by chemisorption at pH of 4, 6, and 8.

Dataset Information

Kinetic and Isotherm Study of As(III) Removal from Aqueous Solution by PET Track-Etched Membranes Loaded with Copper Microtubes.

Publications

Kinetic and Isotherm Study of As(III) Removal from Aqueous Solution by PET Track-Etched Membranes Loaded with Copper Microtubes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets