Efficient Removal of Cr(VI) Ions by a Novel Magnetic 4-Vinyl Pyridine Grafted Ni3Si2O5(OH)4 Multiwalled Nanotube.

ABSTRACT: The contamination of water systems by heavy metals greatly threatens human health and ecological safety. An efficient adsorbent is critical for the removal of these contaminants. In this work, magnetic Ni3Si2O5(OH)4 nanotubes (NTs) have been synthesized via in situ hydrothermal reduction and further functionalized by grafting poly(4-vinyl pyridine) (P4VP) brushes on its surface via atom transfer radical polymerization. Characterizations by Fourier transform infrared, X-ray diffraction, thermogravimetric analysis, transmission electron microscopy, and X-ray photoelectron spectroscopy proved that P4VP was successfully grafted on the surface of magnetic Ni3Si2O5(OH)4 NTs. The resultant Ni3Si2O5(OH)4-g-P4VP NTs are efficient nanosorbents for removing Cr(VI) anions from water. The Cr(VI) adsorption capacity of Ni3Si2O5(OH)4-g-P4VP NTs reaches 1.49 mmol/g at a pH of 3. The pseudo-second-order kinetic model and the Freundlich isothermal model are suitable to describe the adsorption process. The analysis using Weber-Morris and Boyd models indicates that both intraparticle diffusion and external film diffusion affect the Cr(VI) adsorption process. The adsorption enthalpy is estimated to be 18.37 kJ/mol. More than 90% of the Cr(VI) adsorption capacity of the Ni3Si2O5(OH)4-g-P4VP NTs remains after eight adsorption and desorption cycles.

SUBMITTER: Xiao C

PROVIDER: S-EPMC7495723 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Efficient Removal of Cr(VI) Ions by a Novel Magnetic 4-Vinyl Pyridine Grafted Ni3Si2O5(OH)4 Multiwalled Nanotube.

Xiao Chunmei C Lin Jianming J

ACS omega 20200903 36

The contamination of water systems by heavy metals greatly threatens human health and ecological safety. An efficient adsorbent is critical for the removal of these contaminants. In this work, magnetic Ni3Si2O5(OH)4 nanotubes (NTs) have been synthesized via in situ hydrothermal reduction and further functionalized by grafting poly(4-vinyl pyridine) (P4VP) brushes on its surface via atom transfer radical polymerization. Characterizations by Fourier tran ...[more]

PMID: 32954160

Similar Datasets

Project description:Heavy metal ions in water refer to significant risks to the biological system due to their high toxicity. Therefore, the decontamination of water polluted by heavy metal ions attracts significant interest of researchers. Adsorption by nanomaterials has been a widely used technique for removing heavy metal ions from water. Chitosan was extracted from shrimp shellfish and mixed with laboratory-prepared AgNPs/GO in the ratio of 3 : 1. A series of tests evaluates the best condition of pH, amount of adsorbent, retention time, stirring speed, temp, and initial concentration. The research was conducted under various conditions. Langmuir, Freundlich, Tempkin, and Dubinin-Radushkevich isotherms were also tested. Also, the column adsorption experiment was carried out on industrial wastewater at different flow rates and column bed heights. The optimal values of the contact time, pH, and adsorbent dose of Cr(vi) were found to be 80 min, 4, and 0.1 g 100 mL-1, respectively, at room temperature (30 °C), agitation at 150 rpm, and initial concentration of 50 ppm. On the other hand, the optimal value of contact time, pH, and adsorbent dose of Fe(iii) were found to be 30 min, 6, and 0.02 g 100 mL-1, respectively, at room temp (30 °C) with a stirring speed of 250 rpm and an initial concentration of 40 ppm. For Cr(vi) and Fe(iii), equilibrium studies show that the data fit the Freundlich isotherm well (correlation coefficient, R 2 = 0.98) (III). A link between the pseudo-second order active model and data fitting the pseudo-first order active models were made. Within the intraparticle diffusion model, there are four stages that the mechanism must go through before it is at equilibrium. The adsorbent was tested in an industrial adsorbent column. This test proves that the nanocomposite's adsorption capacity can be restored by washing it with 0.1 M HCl, as shown by the periodicity test. After four cycles, the amount of Cr(vi) adsorbed on AgNPs/GO/chitosan was just 20%, which is insufficient for further adsorption experiments. Cr(vi) removal rates (%R) decreased slightly.

Dataset Information

Efficient Removal of Cr(VI) Ions by a Novel Magnetic 4-Vinyl Pyridine Grafted Ni3Si2O5(OH)4 Multiwalled Nanotube.

Publications

Efficient Removal of Cr(VI) Ions by a Novel Magnetic 4-Vinyl Pyridine Grafted Ni<sub>3</sub>Si<sub>2</sub>O<sub>5</sub>(OH)<sub>4</sub> Multiwalled Nanotube.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets