Synthesis of di- and triacrylamides with tertiary amine cores and their evaluation as monomers in dental adhesive interfaces.

ABSTRACT:

Purpose/aim

In an attempt to increase the service life of dental adhesive interfaces, more hydrolytically and enzymatically-stable methacrylate alternatives, such as methacrylamides, have been proposed. The aim of this study was to investigate polymerization behavior, as well as mechanical and biological properties of experimental adhesives containing multi-functional acrylamides.

Materials and methods

Multi-functional acrylamides (N,N-Bis[(3-methylaminoacryl)propyl]methylamine - BMAAPMA, Tris[(2-methylaminoacryl)ethyl]amine - TMAAEA, N,N'-bis(acrylamido) 1,4-diazepane - BAADA, N,N-Diethyl-1,3-bis(acrylamido)propane - DEBAAP) or HEMA (2-Hydroxyethyl methacrylate - control) were added at 40 wt% to UDMA. 0.2 wt% DMPA and 0.4 wt% DPI-PF6 were used as initiators. Polymerization kinetics was followed in real-time in near-IR during photoactivation (320-500 nm, at 630 mW/cm²). Water sorption/solubility and flexural strength/modulus were measured according to ISO 4049. ¹H NMR was used to assess monomer degradation kinetics. MTT assay was used to assess cytotoxicity against OD-21 and DPSC cells. Biofilm formation and adhesion were assessed by Luciferase Assay and Impingement technique, respectively. Solvated adhesives (40 vol% ethanol) were used to test interfacial adhesion strength. The results were analyzed by ANOVA/Tukey's test (α = 0.05).

Results

In general, the pure methacrylate mixture had higher rate of polymerization (Rp_max), degree of conversion (DC) at Rp_max, and final DC than the acrylamides. Flexural properties after water storage decreased between 11 and 65%, more markedly for acrylamides. Interfacial bond strength was greater and more stable long-term for the newly synthesized acrylamide formulations (less than 4% reduction at 6 months) compared to the methacrylate experimental control (42% reduction at 6 months). HEMA degraded by almost 90%, while the acrylamides showed no degradation in acidic conditions. Cytotoxicity and biofilm formation, in general, were similar for all groups.

Conclusions

Despite demonstrating high water sorption, the acrylamide-containing materials had similar mechanical and biological properties and enhanced interfacial bond strength stability compared to the methacrylate control.

SUBMITTER: Fugolin APP

PROVIDER: S-EPMC7530076 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:ObjectivesMethacrylamides are proposed as components for dental adhesive systems with enhanced resistance to hydrolytic and enzymatic degradation. The specific objective of this study was to evaluate the polymerization kinetics, water sorption and solubility, pH-derived degradation and microtensile bond strength of various monofunctional acrylamides and meth(acrylamides) when copolymerized with dimethacrylates.MethodsBase monomers were added at 60 wt%, and included either BisGMA or UDMA. Monofunctional monomers were added at 40 wt%, including one (meth)acrylate as the control, two secondary methacrylamides and two tertiary acrylamides. DMPA (0.2 wt%) and DPI-PF6 (0.4 wt%)/BHT (0.1 wt%) were added as initiators/inhibitor. Polymerization kinetics wwere followed with near-IR spectroscopy in real time. Water sorption (WS) and solubility (SL) were measured following ISO 4049. Monomer degradation at different pH levels was assessed with 1H NMR. Microtensile bond strength (MTBS) was assessed in caries-free human third molars 48 h and 3 weeks after restorations were placed using solvated BisGMA-based adhesives (40 vol% ethanol). Data were analyzed with one-way ANOVA/Tukey's test (α = 0.05).ResultsAs expected, rate of polymerization and final degree of conversion (DC) were higher for the acryl versions of each monomer, and decreased with increasing steric hindrance around the vinyl group for each molecule. In general, UDMA copolymerizations were more rapid and extensive than for BisGMA, but this was dependent upon the specific monofunctional monomer added. WS/SL were in general higher for the (meth)acrylamides compared to the (meth)acrylates, except for the tertiary acrylamide, which showed the lowest values. One of the secondary methacrylamides was significantly more stable than the methacrylate control, but the alpha substitutions decreased stability to degradation in acid pH. MTBS in general was higher for the (meth)acrylates. While for all materials the MTBS values at 3 weeks decreased in relation to the 24 h results, the tertiary acrylamide showed no reduction in bond strength.SignificanceThis study highlights the importance of considering steric and electronic factors when designing monomers for applications where rapid polymerizations are needed, especially when co-polymerizations with other base monomers are required to balance mechanical properties, as is the case with dental adhesives. The results of this investigation will be used to design fully formulated adhesives to be tested in clinically-relevant conditions.

Project description:ObjectivesThe susceptibility of methacrylates to hydrolytic and enzymatic degradation may be a contributing factor limiting the clinical lifespan of resin composite restorations. The elimination of labile ester bonds is a potential advantage of methacrylamides, which have been shown to produce more stable restorative interfaces. The rationale of this study is to design hydrolytically and enzymatically stable adhesive monomers, with the added benefit of being able to form crosslinked networks. The objective of this study was to synthesize difunctional, hybrid methacrylate-methacrylamide monomers, and evaluate them as potential monomers for dental adhesives.Materials and methodsHEMA, TEGDMA (controls) or secondary methacrylamides (HEMAM - commercially available, 2EM and 2dMM - newly synthesized) either bearing a hydroxyl group or a methacrylate functionality (Hybrids-Hy), were added at 40mass% to bisGMA. The photoinitiator system consisted of 2-dimethoxyphenyl acetophenone (DMPA) and diphenyl iodonium hexafluorophosphate (DPI-PF6) at 0.2 and 0.4mass%, respectively. Polymerization kinetics were followed in real-time by near-IR spectroscopy during light activation at 630mW/cm2 for 300s. Water sorption and solubility (WS, SL) were measured according to ISO 4049. Storage modulus in shear (G') for 300s was obtained by oscillatory rheometry. For the microtensile bond strength (μTBS), fully formulated adhesives containing 40vol% ethanol were used to restore caries-free human third molars. Bonded specimens with 1mm2 cross-sectional area were tested after 48h and 6 months storage in water at 37°C. Single bond (SB) was tested as a commercial control. Data were analysed with one-way ANOVA and Tukey's test and Student's t-test (α=0.05).ResultsIn general, hybrid versions showed lower polymerization rate and degree of conversion, whereas the methacrylate controls, HEMA and TEGDMA, showed the highest values. The hybrid versions showed lower values of WS and SL than their monofunctional versions. HEMAM Hy showed the highest values of G' and TEGDMA, 2EM, and 2dMM-Hy the lowest. The μTBS values between 48h and 6 months were statistically reduced only for the HEMA and both 2dMM materials. The formulation containing the monofunctional methacrylamide (HEMAM) showed only 9% reduction in μTBS after 6 months of aging, while the other groups showed a decrease ranging between 18% and 33%.ConclusionOverall, hybrid monomers showed lower reactivity than their analogous monofunctional versions, but had markedly lower water sorption. Shear storage modulus was affected differently by the addition of the second functionality. HEMAM-containing systems were able to maintain stable long-term dentin bond strength, which demonstrates that bonding stability is a result of the complex interplay among the factors studied.Clinical significanceThe novel monomers showed here are potential alternatives to the current methacrylate adhesives, with selected formulations presenting greater bond stability.