Methacrylamide-methacrylate hybrid monomers for dental applications.

ABSTRACT:

Objectives

The susceptibility of methacrylates to hydrolytic and enzymatic degradation may be a contributing factor limiting the clinical lifespan of resin composite restorations. The elimination of labile ester bonds is a potential advantage of methacrylamides, which have been shown to produce more stable restorative interfaces. The rationale of this study is to design hydrolytically and enzymatically stable adhesive monomers, with the added benefit of being able to form crosslinked networks. The objective of this study was to synthesize difunctional, hybrid methacrylate-methacrylamide monomers, and evaluate them as potential monomers for dental adhesives.

Materials and methods

HEMA, TEGDMA (controls) or secondary methacrylamides (HEMAM - commercially available, 2EM and 2dMM - newly synthesized) either bearing a hydroxyl group or a methacrylate functionality (Hybrids-Hy), were added at 40mass% to bisGMA. The photoinitiator system consisted of 2-dimethoxyphenyl acetophenone (DMPA) and diphenyl iodonium hexafluorophosphate (DPI-PF6) at 0.2 and 0.4mass%, respectively. Polymerization kinetics were followed in real-time by near-IR spectroscopy during light activation at 630mW/cm² for 300s. Water sorption and solubility (WS, SL) were measured according to ISO 4049. Storage modulus in shear (G') for 300s was obtained by oscillatory rheometry. For the microtensile bond strength (μTBS), fully formulated adhesives containing 40vol% ethanol were used to restore caries-free human third molars. Bonded specimens with 1mm² cross-sectional area were tested after 48h and 6 months storage in water at 37°C. Single bond (SB) was tested as a commercial control. Data were analysed with one-way ANOVA and Tukey's test and Student's t-test (α=0.05).

Results

In general, hybrid versions showed lower polymerization rate and degree of conversion, whereas the methacrylate controls, HEMA and TEGDMA, showed the highest values. The hybrid versions showed lower values of WS and SL than their monofunctional versions. HEMAM Hy showed the highest values of G' and TEGDMA, 2EM, and 2dMM-Hy the lowest. The μTBS values between 48h and 6 months were statistically reduced only for the HEMA and both 2dMM materials. The formulation containing the monofunctional methacrylamide (HEMAM) showed only 9% reduction in μTBS after 6 months of aging, while the other groups showed a decrease ranging between 18% and 33%.

Conclusion

Overall, hybrid monomers showed lower reactivity than their analogous monofunctional versions, but had markedly lower water sorption. Shear storage modulus was affected differently by the addition of the second functionality. HEMAM-containing systems were able to maintain stable long-term dentin bond strength, which demonstrates that bonding stability is a result of the complex interplay among the factors studied.

Clinical significance

The novel monomers showed here are potential alternatives to the current methacrylate adhesives, with selected formulations presenting greater bond stability.

SUBMITTER: Fugolin AP

PROVIDER: S-EPMC7363560 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Investigation of polymerisation kinetics using ATR-FTIR systems is common in many dental studies. However, peak selection methods to calculate monomer-polymer conversion can vary, consequently affecting final results. Thus, the aim of this study is to experimentally confirm which method is less prone to systematic errors. Three commercial restorative materials were tested-Vertise Flow (VF), Constic and Activa Bioactive Restorative Kids. Firstly, Attenuated Total Reflectance Fourier Transform Infra-Red (ATR-FTIR) (Spectrum One, Perkin-Elmer, UK) spectra of monomers were acquired-10-methacryloyloxy decyl dihydrogen phosphate (10-MDP), bisphenol-A glycidyl dimethacrylate (Bis-GMA), 2-hydroxyethyl methacrylate (HEMA), triethyelene glycol dimethacrylate (TEGDMA) and urethane dimethacrylate (UDMA) to investigate proportionality of methacrylate peak heights versus concentration. Spectral changes upon light exposure of 2 mm discs of the restorative materials (irradiated for 20 s, LED curing unit 1100-1330 mW/cm2) were assessed to study polymerisation kinetics (n = 3), with continuous acquisition of spectra, before, during and after light exposure. Peak differences and degrees of conversion (DC %) were calculated using 1320/1336, 1320/1350 and 1636/1648 cm-1 as reaction/reference peaks. Inferential statistics included a MANOVA and within-subjects repeated measures ANOVA design (5% significance level). Proportionality of methacrylate peak height to concentration was confirmed, with the 1320/1352 cm-1 peak combination showing the lowest coefficient of variation (8%). Difference spectra of the polymerisation reaction showed noise interference around the 1500-1800 cm-1 region. Across the different materials, DC % results are highly dependent upon peak selection (p<0.001), with higher variability associated to the 1636 cm-1. Significant differences in the materials were only detected when the 1320 cm-1 peak was used (p<0.05). Within the same materials, methods were significantly different for Constic and Activa (p<0.05). It is possible to conclude that the 1320 cm-1 peak is more adequate to assess polymerisation of methacrylates and is therefore recommended.

Project description:OBJECTIVES:Methacrylamides are proposed as components for dental adhesive systems with enhanced resistance to hydrolytic and enzymatic degradation. The specific objective of this study was to evaluate the polymerization kinetics, water sorption and solubility, pH-derived degradation and microtensile bond strength of various monofunctional acrylamides and meth(acrylamides) when copolymerized with dimethacrylates. METHODS:Base monomers were added at 60?wt%, and included either BisGMA or UDMA. Monofunctional monomers were added at 40?wt%, including one (meth)acrylate as the control, two secondary methacrylamides and two tertiary acrylamides. DMPA (0.2?wt%) and DPI-PF6 (0.4?wt%)/BHT (0.1?wt%) were added as initiators/inhibitor. Polymerization kinetics wwere followed with near-IR spectroscopy in real time. Water sorption (WS) and solubility (SL) were measured following ISO 4049. Monomer degradation at different pH levels was assessed with 1H NMR. Microtensile bond strength (MTBS) was assessed in caries-free human third molars 48?h and 3 weeks after restorations were placed using solvated BisGMA-based adhesives (40?vol% ethanol). Data were analyzed with one-way ANOVA/Tukey's test (??=?0.05). RESULTS:As expected, rate of polymerization and final degree of conversion (DC) were higher for the acryl versions of each monomer, and decreased with increasing steric hindrance around the vinyl group for each molecule. In general, UDMA copolymerizations were more rapid and extensive than for BisGMA, but this was dependent upon the specific monofunctional monomer added. WS/SL were in general higher for the (meth)acrylamides compared to the (meth)acrylates, except for the tertiary acrylamide, which showed the lowest values. One of the secondary methacrylamides was significantly more stable than the methacrylate control, but the alpha substitutions decreased stability to degradation in acid pH. MTBS in general was higher for the (meth)acrylates. While for all materials the MTBS values at 3 weeks decreased in relation to the 24?h results, the tertiary acrylamide showed no reduction in bond strength. SIGNIFICANCE:This study highlights the importance of considering steric and electronic factors when designing monomers for applications where rapid polymerizations are needed, especially when co-polymerizations with other base monomers are required to balance mechanical properties, as is the case with dental adhesives. The results of this investigation will be used to design fully formulated adhesives to be tested in clinically-relevant conditions.