ABSTRACT: Pigments with nanoscale dimensions are added to exterior coatings to achieve desirable color and gloss properties. The present study compared the performance, degradation, and release behavior of an acrylic coating that was pigmented by a nanoform of Cu-phthalocyanine after both natural (i.e., outdoor) and accelerated weathering. Samples were weathered outdoors in three geographically distinct locations across the United States (Arizona, Colorado, Maryland) continuously for 15 months. Identically prepared samples were also artificially weathered under accelerated conditions (increased ultraviolet (UV) light intensity and elevated temperatures) for three months, in one-month increments. After exposure, both sets of samples were characterized with color, gloss, and infrared spectroscopy measurements, and selectively with surface roughness measurements. Results indicated that UV-driven coating oxidation was the principal degradation pathway for both natural and accelerated weathering samples, with accelerated weathering leading to an increased rate of oxidation without altering the fundamental degradation pathway. The inclusion of the nanoform pigment reduced the rate of coating oxidation, via UV absorption by the pigment, leading to improved coating integrity compared to non-pigmented samples. Release measurements collected during natural weathering studies indicated there was never a period of weathering, in any location, that led to copper material release above background copper measurements. Lab-based release experiments performed on samples weathered naturally and under accelerated conditions found that the release of degraded coating material after each type of exposure was diminished by the inclusion of the nanoform pigment. Release measurements also indicated that the nanoform pigment remained embedded within the coating and did not release after weathering.

SUBMITTER: Lankone R

PROVIDER: S-EPMC7537477 | biostudies-literature | 2020 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Nano-fillers are increasingly incorporated into polymeric materials to improve the mechanical, barrier or other matrix properties of nanocomposites used for consumer and industrial applications. However, over the life cycle, these nanocomposites could degrade due to exposure to environmental conditions, resulting in the release of embedded nanomaterials from the polymer matrix into the environment. This paper presents a rigorous study on the degradation and the release of nanomaterials from food packaging composites. Films of nano-clay-loaded low-density polyethylene (LDPE) composite for food packaging applications were prepared with the spherilene technology and exposed to accelerated weathering of ultraviolet (UV) irradiation or low concentration of ozone at 40 °C. The changes in the structural, surface morphology, chemical and physical properties of the films during accelerated weathering were investigated. Qualitative and quantitative changes in properties of pristine and aged materials and the release of nano-clay proceeded slowly until 130 hr irradiation and then accelerated afterward resulting complete degradation. Although nano-clay increased the stability of LDPE and improved thermal and barrier properties, they accelerated the UV oxidation of LDPE. With increasing exposure to UV, the surface roughness, chemiluminescence index, and carbonyl index of the samples increased while decreasing the intensity of the wide-angle X-ray diffraction pattern. Nano-clay particles with sizes ranging from 2-8 nm were released from UV and ozone weathered composite. The concentrations of released nanoparticles increased with an increase in aging time. Various toxicity tests, including reactive oxygen species generation and cell activity/viability were also performed on the released nano-clay and clay polymer. The released nano-clays basically did not show toxicity. Our combined results demonstrated the degradation properties of nano-clay particle-embedded LDPE composites toxicity of released nano-clay particles to A594 adenocarcinomic human alveolar basal epithelial cells was observed, which will help with future risk based-formulations of exposure.

Project description:Developing materials for use in photovoltaic (PV) systems requires knowledge of their performance over the warranted lifetime of the PV system. Poly(ethylene-terephthalate) (PET) is a critical component of PV module backsheets due to its dielectric properties and low cost. However, PET is susceptible to environmental stressors and degrades over time. Changes in the physical properties of nine PET grades were modeled after outdoor and accelerated weathering exposures to characterize the degradation process of PET and assess the influence of stabilizing additives and weathering factors. Multivariate multiple regression (MMR) models were developed to quantify changes in color, gloss, and haze of the materials. Natural splines were used to capture the non-linear relationship between predictors and responses. Model performance was evaluated via adjusted-R2 and root mean squared error values from leave-one-out cross validation analysis. All models described over 85% of the variation in the data with low relative error. Model coefficients were used to assess the influence of weathering stressors and material additives on the property changes of films. Photodose was found to be the primary degradation stressor and moisture was found to increase the degradation rate of PET. Direct moisture contact was found to impose more stress on the material than airbone moisture (humidity). Increasing the concentration of TiO2 was found to generally decrease the degradation rate of PET and mitigate hydrolytic degradation. MMR models were compared to physics-based models and agreement was found between the two modeling approaches. Cross-correlation of accelerated exposures to outdoor exposures was achieved via determination of cross-correlation scale factors. Cross-correlation revealed that direct moisture contact is a key factor for reliable accelerated weathering testing and provided a quantitative method to determine when accelerated exposure results can be made more aggressive to better approximate outdoor exposure conditions.

Dataset Information

Evaluating performance, degradation, and release behavior of a nanoform pigmented coating after natural and accelerated weathering

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets