Analysis and Modeling of Viscosity for Aqueous Polyurethane Dispersion as a Function of Shear Rate, Temperature, and Solid Content.

ABSTRACT: Aqueous polyurethane dispersion (PUD) has attracted increasing attention in a wide range of industrial applications because of their versatile properties as well as ecofriendly nature. In this study, the aqueous PUD used in warp-knitted vamp printing was characterized by Fourier transform infrared spectra, dynamic light scattering, and laser Doppler electrophoresis. The mean diameter and zeta potential are 206.6 nm and -18.3 mV, respectively. The rheological behavior of aqueous PUD as a function of shear rate, temperature, and solid content was investigated experimentally. Besides, a new correlation model was proposed based on the Carreau equation and Arrhenius relation. The resulting model has high accuracy in viscosity estimation under complex conditions according to the prediction interval of 95%. Furthermore, the reasonable ranges of parameters were proposed theoretically for successful printing.

SUBMITTER: Liu Y

PROVIDER: S-EPMC7558001 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Analysis and Modeling of Viscosity for Aqueous Polyurethane Dispersion as a Function of Shear Rate, Temperature, and Solid Content.

Liu Yuegang Y Meng Zhuo Z Wang Yacheng Y Li Peibo P Sun Yize Y

ACS omega 20201001 40

Aqueous polyurethane dispersion (PUD) has attracted increasing attention in a wide range of industrial applications because of their versatile properties as well as ecofriendly nature. In this study, the aqueous PUD used in warp-knitted vamp printing was characterized by Fourier transform infrared spectra, dynamic light scattering, and laser Doppler electrophoresis. The mean diameter and zeta potential are 206.6 nm and -18.3 mV, respectively. The rheological behavior of aqueous PUD as a function ...[more]

PMID: 33073150

Similar Datasets

Project description:We report the synthesis of sterically-stabilized diblock copolymer particles at 20% w/w solids via reversible addition-fragmentation chain transfer (RAFT) aqueous dispersion polymerization of N,N'-dimethylacrylamide (DMAC) in highly salty media (2.0 M (NH4)2SO4). This is achieved by selecting a well-known zwitterionic water-soluble polymer, poly(2-(methacryloyloxy)ethyl phosphorylcholine) (PMPC), to act as the salt-tolerant soluble precursor block. A relatively high degree of polymerization (DP) can be targeted for the salt-insoluble PDMAC block, which leads to the formation of a turbid free-flowing dispersion of PDMAC-core particles by a steric stabilization mechanism. 1H NMR spectroscopy studies indicate that relatively high DMAC conversions (>99%) can be achieved within a few hours at 30 °C. Aqueous GPC analysis indicates high blocking efficiencies and unimodal molecular weight distributions, although dispersities increase monotonically as higher degrees of polymerization (DPs) are targeted for the PDMAC block. Particle characterization techniques include dynamic light scattering (DLS) and electrophoretic light scattering (ELS) using a state-of-the-art instrument that enables accurate ζ potential measurements in a concentrated salt solution. 1H NMR spectroscopy studies confirm that dilution of the as-synthesized dispersions using deionized water lowers the background salt concentration and hence causes in situ molecular dissolution of the salt-intolerant PDMAC chains, which leads to a substantial thickening effect and the formation of transparent gels. Thus, this new polymerization-induced self-assembly (PISA) formulation enables high molecular weight water-soluble polymers to be prepared in a highly convenient, low-viscosity form. In principle, such aqueous PISA formulations are highly attractive: there are various commercial applications for high molecular weight water-soluble polymers, while the well-known negative aspects of using a RAFT agent (i.e., its cost, color, and malodor) are minimized when targeting such high DPs.

Project description:RAFT solution polymerization of N-(2-(methacryoyloxy)ethyl)pyrrolidone (NMEP) in ethanol at 70 °C was conducted to produce a series of PNMEP homopolymers with mean degrees of polymerization (DP) varying from 31 to 467. Turbidimetry was used to assess their inverse temperature solubility behavior in dilute aqueous solution, with an LCST of approximately 55 °C being observed in the high molecular weight limit. Then a poly(glycerol monomethacylate) (PGMA) macro-CTA with a mean DP of 63 was chain-extended with NMEP using a RAFT aqueous dispersion polymerization formulation at 70 °C. The target PNMEP DP was systematically varied from 100 up to 6000 to generate a series of PGMA63-PNMEP x diblock copolymers. High conversions (≥92%) could be achieved when targeting up to x = 5000. GPC analysis confirmed high blocking efficiencies and a linear evolution in Mn with increasing PNMEP DP. A gradual increase in Mw/Mn was also observed when targeting higher DPs. However, this problem could be minimized (Mw/Mn < 1.50) by utilizing a higher purity grade of NMEP (98% vs 96%). This suggests that the broader molecular weight distributions observed at higher DPs are simply the result of a dimethacrylate impurity causing light branching, rather than an intrinsic side reaction such as chain transfer to polymer. Kinetic studies confirmed that the RAFT aqueous dispersion polymerization of NMEP was approximately four times faster than the RAFT solution polymerization of NMEP in ethanol when targeting the same DP in each case. This is perhaps surprising because both 1H NMR and SAXS studies indicate that the core-forming PNMEP chains remain relatively solvated at 70 °C in the latter formulation. Moreover, dissolution of the initial PGMA63-PNMEP x particles occurs on cooling from 70 to 20 °C as the PNMEP block passes through its LCST. Hence this RAFT aqueous dispersion polymerization formulation offers an efficient route to a high molecular weight water-soluble polymer in a rather convenient low-viscosity form. Finally, the relatively expensive PGMA macro-CTA was replaced with a poly(methacrylic acid) (PMAA) macro-CTA. High conversions were also achieved for PMAA85-PNMEP x diblock copolymers prepared via RAFT aqueous dispersion polymerization for x ≤ 4000. Again, better control was achieved when using the 98% purity NMEP monomer in such syntheses.

Dataset Information

Analysis and Modeling of Viscosity for Aqueous Polyurethane Dispersion as a Function of Shear Rate, Temperature, and Solid Content.

Publications

Analysis and Modeling of Viscosity for Aqueous Polyurethane Dispersion as a Function of Shear Rate, Temperature, and Solid Content.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets