Solid-State Li-Ion Batteries Operating at Room Temperature Using New Borohydride Argyrodite Electrolytes.

ABSTRACT: Using a new class of (BH4)- substituted argyrodite Li6PS5Z0.83(BH4)0.17, (Z = Cl, I) solid electrolyte, Li-metal solid-state batteries operating at room temperature have been developed. The cells were made by combining the modified argyrodite with an In-Li anode and two types of cathode: an oxide, LixMO2 (M = ? Ni, ? Mn, ? Co; so called NMC) and a titanium disulfide, TiS2. The performance of the cells was evaluated through galvanostatic cycling and Alternating Current AC electrochemical impedance measurements. Reversible capacities were observed for both cathodes for at least tens of cycles. However, the high-voltage oxide cathode cell shows lower reversible capacity and larger fading upon cycling than the sulfide one. The AC impedance measurements revealed an increasing interfacial resistance at the cathode side for the oxide cathode inducing the capacity fading. This resistance was attributed to the intrinsic poor conductivity of NMC and interfacial reactions between the oxide material and the argyrodite electrolyte. On the contrary, the low interfacial resistance of the TiS2 cell during cycling evidences a better chemical compatibility between this active material and substituted argyrodites, allowing full cycling of the cathode material, 240 mAhg-1, for at least 35 cycles with a coulombic efficiency above 97%.

SUBMITTER: Dao AH

PROVIDER: S-EPMC7558157 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Solid-State Li-Ion Batteries Operating at Room Temperature Using New Borohydride Argyrodite Electrolytes.

Dao Anh Ha AH López-Aranguren Pedro P Zhang Junxian J Cuevas Fermín F Latroche Michel M

Materials (Basel, Switzerland) 20200911 18

Using a new class of (BH4)- substituted argyrodite Li6PS5Z0.83(BH4)0.17, (Z = Cl, I) solid electrolyte, Li-metal solid-state batteries operating at room temperature have been developed. The cells were made by combining the modified argyrodite with an In-Li anode and two types of cathode: an oxide, LixMO2 (M = ⅓ Ni, ⅓ Mn, ⅓ Co; so called NMC) and a titanium disulfi ...[more]

PMID: 32932863

Similar Datasets

Project description:Fluorinated electrolytes based on fluoroethylene carbonate (FEC) have been considered as promising alternative electrolytes for high-voltage and high-energy capacity lithium-ion batteries (LIBs). However, the compatibility of the fluorinated electrolytes with graphite negative electrodes is unclear. In this paper, we have systematically investigated, for the first time, the stability of fluorinated electrolytes with graphite negative electrodes, and the result shows that unlike the ethylene carbonate (EC)-based electrolyte, the FEC-based electrolyte (EC was totally replaced by FEC) is incapable of forming a protective and effective solid electrolyte interphase (SEI) that protects the electrolyte from runaway reduction on the graphite surface. The reason is that the lowest unoccupied molecular orbital energy levels are also lowered by the introduction of fluorine into the solvent, and the FEC solvent has poorer resistance against reduction, leading to instability on the graphite negative electrode. To tackle this problem, two lithium salts of lithium bis(oxalato)borate and lithium difluoro(oxalato)borate (LiDFOB) have been investigated as negative-electrode film-forming additives. Incorporation of only 0.5 wt % LiDFOB to a FEC-based electrolyte [1.0 M LiPF6 in 3:7 (FEC-ethyl methyl carbonate)] results in excellent cycling performance of the graphite negative electrode. This improved property originates from the generation of a thinner and better quality SEI film with little LiF by the sacrificial reduction of the LiDFOB additive on the graphite negative electrode surface. On the other hand, this additive can stabilize the electrolyte by scavenging HF. Meanwhile, the incorporated LiDFOB additive has positive influence on the interphase layer on the positive electrode surface and significantly decreases the amount of HF formation, finally leading to improved cycling stability and rate capability of LiNi0.5Mn1.5O4 electrodes at a high cutoff voltage of 5 V. The data demonstrate that the LiDFOB additive not only exhibits a superior compatibility with graphite but also improves the electrochemical properties of high-voltage spinel LiNi0.5Mn1.5O4 positive electrodes considerably, confirming its potential as a prospective, multifunctional additive for 5 V fluorinated electrolytes in high-energy capacity lithium-ion batteries (LIBs).

Dataset Information

Solid-State Li-Ion Batteries Operating at Room Temperature Using New Borohydride Argyrodite Electrolytes.

Publications

Solid-State Li-Ion Batteries Operating at Room Temperature Using New Borohydride Argyrodite Electrolytes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets