Improved Removal Capacity and Equilibrium Time of Maghemite Nanoparticles Growth in Zeolite Type 5A for Pb(II) Adsorption.

ABSTRACT: Novel magnetic zeolite type 5A nanocomposites were synthesized by the co-precipitation method and applied to lead removal from aqueous ambient. Maghemite nanoparticles were mixed with zeolite and, by controlling its content, transmission electron microscopy results gave sizes of 5 to 15 nm and selected area electron diffraction patterns confirmed the presence of zeolite. The nanocomposites have high specific surface area with values up to 194 m2/g. Magnetization measurements proved superparamagnetic behavior with saturation values of ~35 emu/gFe. Kinetic adsorption experiments showed removal efficiencies of 99.9% and an enhanced equilibrium time of 5 min. The lead concentrations after adsorption experiments lay under the permissible levels of 10 ?g L-1, according to the World Health Organization. The maximum adsorption capacity, estimated by Sips model, was 265 mg L-1 at 300 K. The removal efficiency was significantly improved in the range of pH > 6, as well as in the presence of cation interferents such as Ca(II), Cu(II), and Cd(II). The adsorption mechanism was explained with cation exchange between Pb(II), the zeolite framework, and the protonated maghemite surface. Besides, our system revealed recyclability even after seven regeneration cycles. Thus, our synthesized materials have remarkable adsorption properties for lead water remediation processes.

SUBMITTER: Ramos-Guivar JA

PROVIDER: S-EPMC7558356 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Improved Removal Capacity and Equilibrium Time of Maghemite Nanoparticles Growth in Zeolite Type 5A for Pb(II) Adsorption.

Ramos-Guivar Juan A JA Taipe Katterine K Schettino Miguel Angelo MA Silva Eloi E Morales Torres Marco Antonio MA Passamani Edson Caetano EC Litterst Fred Jochen FJ

Nanomaterials (Basel, Switzerland) 20200826 9

Novel magnetic zeolite type 5A nanocomposites were synthesized by the co-precipitation method and applied to lead removal from aqueous ambient. Maghemite nanoparticles were mixed with zeolite and, by controlling its content, transmission electron microscopy results gave sizes of 5 to 15 nm and selected area electron diffraction patterns confirmed the presence of zeolite. The nanocomposites have high specific surface area with values up to 194 m<sup>2</sup>/g. Magnetization measurements proved su ...[more]

PMID: 32858820

Similar Datasets

Project description:Graphene oxide (GO) has shown remarkable performance in the multiple-equilibrium-route adsorption (MER) process, which is characterized by further activation of GO through an in-situ reduction process based on single-equilibrium-route adsorption (SER), generating new adsorption sites and achieving an adsorption capacity increase. However, the effect of GO on MER adsorption in lateral size and thickness is still unclear. Here, GO sheets were sonicated for different lengths of time, and the adsorption of MER and SER was investigated at three temperatures to remove the typical cationic dye, acridine orange (AO). After sonication, we found that freshly prepared GO was greatly reduced in lateral size and thickness. In about 30 min, the thickness of GO decreased dramatically from several atomic layers to fewer atomic layers to a single atomic layer, which was completely stripped off; after that, the monolayer lateral size reduction dominated until it remained constant. Surface functional sites, such as hydroxyl groups, showed little change in the experiments. However, GO mainly reduces the C=O and C-O bonds in MER, except for the conjugated carbon backbone (C-C). The SER adsorption kinetics of all temperatures fitted the pseudo-first-order and pseudo-second-order models, yet room temperature preferred the latter. An overall adsorption enhancement appeared as sonication time, but the equilibrium capacity of SER GO generally increased with thickness and decreased with the single-layer lateral size, while MER GO conversed concerning the thickness. The escalated temperature facilitated the exfoliation of GO regarding the adsorption mechanism. Thus, the isotherm behaviors of the SER GO changed from the Freundlich model to Langmuir as size and temperature changed, while the MER GO were all of the Freundlich. A record capacity of ~4.3 g of AO per gram of GO was obtained from the MER adsorption with a sixty-minute ultrasonicated GO at 313.15 K. This work promises a cornerstone for MER adsorption with GO as an adsorbent.

Project description:The intake of heavy metals into the body, even at very low concentrations, may cause a decrease in central nervous system functions; deterioration of blood composition; and liver, kidney, and lung damage. Therefore, heavy metal ions must be removed from water. In this study, silver, magnetic iron/copper, and iron oxide nanoparticles were synthesized using Lathyrus brachypterus extract and then Fe/Cu-AT, Fe3O4-AT, Fe/Cu-CS, and Fe3O4-CS magnetic nanocomposite beads were synthesized using alginate and chitosan. The removal of Cd(II), Pb(II), Ni(II), and Cu(II) ions from aqueous phases using synthesized nanoadsorbents was investigated by single and competitive (double and quaternary) adsorption techniques. The kinetic usability of the magnetic iron oxide chitosan (Fe3O4-CS) nanocomposite beads with the highest removal efficiency was evaluated. Based on experimental results, the order of removal was found to be 98.39, 75.52, 51.54, and 45.34%, and it was listed as Pb(II) > Cu(II) > Cd(II) > Ni(II), respectively. The Dubinin-Radushkevich, Freundlich, Langmuir, and Temkin isotherm models were used, and experimental results revealed that the experimental data fit the Langmuir model better. The maximum adsorption capacities (qm) obtained from the Langmuir isotherm model of Fe3O4-CS were found to be 8.71, 23.75, 18.57, and 12.38 mg/g for Ni(II), Pb(II), Cu(II), and Cd(II) ions, respectively. When the kinetic data were applied to the Lagergren, Ho-McKay, and Elovich models, it was observed that the adsorption kinetics mostly conformed to the Ho-McKay second-order rate equation. The binary and quaternary competitive adsorption data showed that Fe3O4-CS were selective toward Cu(II) and Pb(II). The reusability of the Fe3O4-CS nanoadsorbent was performed as three cycles with the same concentration. The adsorption capacities were found to be 95.81, 70.65, 50.50, and 42.75%, in turn for Pb(II), Cu(II), Cd(II), and Ni(II) ions after three cycles, which revealed that the Fe3O4-CS nanoadsorbent can be used after three cycles without losing its efficiency.

Dataset Information

Improved Removal Capacity and Equilibrium Time of Maghemite Nanoparticles Growth in Zeolite Type 5A for Pb(II) Adsorption.

Publications

Improved Removal Capacity and Equilibrium Time of Maghemite Nanoparticles Growth in Zeolite Type 5A for Pb(II) Adsorption.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets