Binder-Free Electrode Based on ZnO Nanorods Directly Grown on Aluminum Substrate for High Performance Supercapacitors.

ABSTRACT: Herein, for the first time, the growth of ZnO nanorods directly on aluminum (Al) substrate via a low temperature (80 °C) wet chemical method, and used as binder-free electrode for supercapacitors were reported. XRD pattern and HRTEM images showed that high crystalline nanorods grown on Al substrate with c-axis orientation. Morphological studies revealed that the nanorods possessed well defined hexagon phase with length and diameter of ~2 µm and 100-180 nm, respectively. Raman spectrum of ZnO nanorods showed that the characteristic E2H mode corresponds to the vibration associated with the oxygen atoms of ZnO. The optical properties of ZnO nanorods studied using Room-temperature PL spectra revealed a near-band-edge (NBE) peak at ~388 nm emission and deep level (DLE) at ~507 nm. Electrochemical measurements showed that ZnO nanorods on Al substrate exhibited remarkably enhanced performance as electrode for supercapacitors with a value of specific capacitance of 394 F g-1 measured with scan rate of 20 mV s-1. This unique nanorods structures also exhibited excellent stability of >98% capacitance retention for 1000 cycles that were measured at 1A g-1. The presented easy and cost-effective method might open up the possibility for the mass production of binder-free electrodes for efficient electrochemical energy storage devices.

SUBMITTER: Ahmed F

PROVIDER: S-EPMC7599740 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Binder-Free Electrode Based on ZnO Nanorods Directly Grown on Aluminum Substrate for High Performance Supercapacitors.

Ahmed Faheem F Almutairi Ghzzai G AlOtaibi Bandar B Kumar Shalendra S Arshi Nishat N Hussain Syed Ghazanfar SG Umar Ahmad A Ahmad Naushad N Aljaafari Abdullah A

Nanomaterials (Basel, Switzerland) 20201007 10

Herein, for the first time, the growth of ZnO nanorods directly on aluminum (Al) substrate via a low temperature (80 °C) wet chemical method, and used as binder-free electrode for supercapacitors were reported. XRD pattern and HRTEM images showed that high crystalline nanorods grown on Al substrate with c-axis orientation. Morphological studies revealed that the nanorods possessed well defined hexagon phase with length and diameter of ~2 µm and 100-180 nm, respectively. Raman spectrum of ZnO nan ...[more]

PMID: 33036342

Similar Datasets

Project description:Electrochemical stability of energy storage devices is one of their major concerns. Polymeric binders are generally used to enhance the stability of the electrode, but the electrochemical performance of the device is compromised due to the poor conductivity of the binders. Herein, 3D binder-free electrode based on nickel oxide deposited on graphene (G-NiO) was fabricated by a simple two-step method. First, graphene was deposited on nickel foam via atmospheric pressure chemical vapour deposition followed by electrodeposition of NiO. The structural and morphological analyses of the fabricated G-NiO electrode were conducted through Raman spectroscopy, X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and energy dispersive X-ray spectroscopy (EDS). XRD and Raman results confirmed the successful growth of high-quality graphene on nickel foam. FESEM images revealed the sheet and urchin-like morphology of the graphene and NiO, respectively. The electrochemical performance of the fabricated electrode was evaluated through cyclic voltammetry (CV), galvanostatic charge-discharge (GCD), and electrochemical impedance spectroscopy (EIS) in aqueous solution at room temperature. The G-NiO binder-free electrode exhibited a specific capacity of ? 243 C g-1 at 3 mV s-1 in a three-electrode cell. A two-electrode configuration of G-NiO//activated charcoal was fabricated to form a hybrid device (supercapattery) that operated in a stable potential window of 1.4 V. The energy density and power density of the asymmetric device measured at a current density of 0.2 A g-1 were estimated to be 47.3 W h kg-1 and 140 W kg-1, respectively. Additionally, the fabricated supercapattery showed high cyclic stability with 98.7% retention of specific capacity after 5,000 cycles. Thus, the proposed fabrication technique is highly suitable for large scale production of highly stable and binder-free electrodes for electrochemical energy storage devices.

Dataset Information

Binder-Free Electrode Based on ZnO Nanorods Directly Grown on Aluminum Substrate for High Performance Supercapacitors.

Publications

Binder-Free Electrode Based on ZnO Nanorods Directly Grown on Aluminum Substrate for High Performance Supercapacitors.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets