Fabrication, Mechanical Properties and In-Vitro Behavior of Akermanite Bioceramic.

ABSTRACT: Pure nanocrystalline akermanite (Ca2MgSi2O7) powder was synthesized by mechanical activation with subsequent annealing of talc, calcium carbonate, and silicate powders as the initial materials. Powder samples were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and transmission electron microscopy (TEM) techniques. The results showed that pure nanocrystalline akermanite with a crystalline size of 35 nm was synthesized after ball milling the initial powders for 20 h with subsequent annealing at 900 °C for 1 h. Mechanical properties of bulk akermanite samples were studied as well. The results showed that the produced akermanite tablets sintered at 1200 °C for 5 h had a Young's modulus of 3800 MPa, an ultimate compressive strength of 24.7 MPa, and a density of 2.489 g/cm3. The in-vitro behavior of the produced akermanite was evaluated by soaking the samples in an SBF solution. The results showed that the produced akermanite had the apatite formation ability on its surface and can be a good candidate for bone tissue engineering applications.

SUBMITTER: Tavangarian F

PROVIDER: S-EPMC7672555 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Fabrication, Mechanical Properties and In-Vitro Behavior of Akermanite Bioceramic.

Tavangarian Fariborz F Zolko Caleb A CA Sadeghzade Sorour S Fayed Marwan M Davami Keivan K

Materials (Basel, Switzerland) 20201030 21

Pure nanocrystalline akermanite (Ca2MgSi2O7) powder was synthesized by mechanical activation with subsequent annealing of talc, calcium carbonate, and silicate powders as the initial materials. Powder samples were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and transmission electron microscopy (TEM) techniques. The results showed that pure nanocrystalline akermanite with a crystalline size of ...[more]

PMID: 33143317

Similar Datasets

Project description:Structural parameters of the implants such as shape, size, and porosity of the pores have been extensively investigated to promote bone tissue repair, however, it is unknown how the pore interconnectivity affects the bone growth behaviors in the scaffolds. Herein we systematically evaluated the effect of biodegradable bioceramics as a secondary phase filler in the macroporous networks on the mechanical and osteogenic behaviors in sparingly dissolvable bioceramic scaffolds. The pure hardystonite (HT) scaffolds with ∼550 & 800 μm in pore sizes were prepared by digital light processing, and then the Sr-doped calcium silicate (SrCSi) bioceramic slurry without and with 30 % organic porogens were intruded into the HT scaffolds with 800 μm pore size and sintered at 1150 °C. It indicated that the organic porogens could endow spherical micropores in the SrCSi filler, and the invasion of the SrCSi component could not only significantly enhance the compressive strength and modulus of the HT-based scaffolds, but also induce osteogenic differentiation of bone marrow mesenchymal stem cells (BMSCs). The pure HT scaffolds showed extremely slow bio-dissolution in Tris buffer after immersion for 8 weeks (∼1 % mass decay); in contrast, the SrCSi filler would readily dissolve into the aqueous medium and produced a steady mass decay (>6 % mass loss). In vivo experiments in rabbit femoral bone defect models showed that the pure HT scaffolds showed bone tissue ingrowth but the bone growth was impeded in the SrCSi-intruded scaffolds within 4 weeks; however, the group with higher porosity of SrCSi filler showed appreciable osteogenesis after 8 weeks of implantation and the whole scaffold was uniformly covered by new bone tissues after 16 weeks. These findings provide some new insights that the pore interconnectivity is not inevitable to impede bone ingrowth with the prolongation of implantation time, and such a highly biodegradable and bioactive filler intrusion strategy may be beneficial for optimizing the performances of scaffolds in bone regenerative medicine applications.

Project description:Pancreatic ductal adenocarcinoma (PDAC) is almost universally fatal, in large part due to a protective fibrotic barrier generated by tumor-associated stromal (TAS) cells. This barrier is thought to promote cancer cell survival and confounds attempts to develop effective therapies. We present a 3D in vitro system that replicates the mechanical properties of the PDAC microenvironment, representing an invaluable tool for understanding the biology of the disease. Mesoscale indentation quantified viscoelastic metrics of resected malignant tumors, inflamed chronic pancreatitis regions, and histologically normal tissue. Both pancreatitis (2.15?±?0.41?kPa, Mean?±?SD) and tumors (5.46?±?3.18?kPa) exhibit higher Steady-State Modulus (SSM) than normal tissue (1.06?±?0.25?kPa; p?<?.005). The average viscosity of pancreatitis samples (63.2?±?26.7?kPa·s) is significantly lower than that of both normal tissue (252?±?134?kPa·s) and tumors (349?±?222?kPa·s; p?<?.005). To mimic this remodeling behavior, PDAC and TAS cells were isolated from human PDAC tumors. Conditioned medium from PDAC cells was used to culture TAS-embedded collagen hydrogels. After 7?days, TAS-embedded gels in control medium reached SSM (1.45?±?0.12?kPa) near normal pancreas, while gels maintained with conditioned medium achieved higher SSM (3.38?±?0.146?kPa) consistent with tumors. Taken together, we have demonstrated an in vitro system that recapitulates in vivo stiffening of PDAC tumors. In addition, our quantification of viscoelastic properties suggests that elastography algorithms incorporating viscosity may be able to more accurately distinguish between pancreatic cancer and pancreatitis. STATEMENT OF SIGNIFICANCE:Understanding tumor-stroma crosstalk in pancreatic ductal adenocarcinoma (PDAC) is challenged by a lack of stroma-mimicking model systems. To design appropriate models, pancreatic tissue must be characterized with a method capable of evaluating in vitro models as well. Our indentation-based characterization tool quantified the distinct viscoelastic signatures of inflamed resections from pancreatitis, tumors from PDAC, and otherwise normal tissue to inform development of mechanically appropriate engineered tissues and scaffolds. We also made progress toward a 3D in vitro system that recapitulates mechanical properties of tumors. Our in vitro model of stromal cells in collagen and complementary characterization system can be used to investigate mechanisms of cancer-stroma crosstalk in PDAC and to propose and test innovative therapies.

Dataset Information

Fabrication, Mechanical Properties and In-Vitro Behavior of Akermanite Bioceramic.

Publications

Fabrication, Mechanical Properties and In-Vitro Behavior of Akermanite Bioceramic.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets