Nanofibrillated Bacterial Cellulose Modified with (3-Aminopropyl)trimethoxysilane under Aqueous Conditions: Applications to Poly(methyl methacrylate) Fiber-Reinforced Nanocomposites.

ABSTRACT: The development of eco-friendly fiber-reinforced composite resins is an important objective from an environmental perspective, and nanofibrillated bacterial cellulose (NFBC), with extremely long high-aspect-ratio fibers, is a filler material with high potential for use in such composite resins. In this study, we investigated chemical modification of the surfaces of NFBC fibers by coupling with (3-aminopropyl)trimethoxysilane and fabricated nanocomposite materials using the prepared surface-modified NFBC. The product prepared by the one-pot reaction of (3-aminopropyl)trimethoxysilane with NFBC microfibrils dispersed in aqueous acid retained the same nanofibril structure as the intact NFBC. The degree of molar substitution and the silicon states on the surface of the product depended on the NFBC/(3-aminopropyl)trimethoxysilane ratio. The thermal analysis revealed that the thermal degradation temperature of the products increases with an increase of degree of molar substitution. Highly transparent (78-89% at 600 nm) poly(methyl methacrylate)-based nanocomposites were prepared by solvent casting; the nanocomposite containing 1.0 wt % (3-aminopropyl)trimethoxysilylated NFBC was only 8% less transparent than neat poly(methyl methacrylate) at 600 nm. In addition, the tensile strength of the nanocomposite was more than twice that of neat poly(methyl methacrylate) when 1 wt % of the surface-modified NFBC was added. The surface-modified NFBC is expected to be a reinforcing nanofiber material that imparts excellent physical properties to fiber-reinforced resins.

SUBMITTER: Kono H

PROVIDER: S-EPMC7676300 | biostudies-literature | 2020 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nanofibrillated Bacterial Cellulose Modified with (3-Aminopropyl)trimethoxysilane under Aqueous Conditions: Applications to Poly(methyl methacrylate) Fiber-Reinforced Nanocomposites.

Kono Hiroyuki H Uno Taiki T Tsujisaki Haruto H Matsushima Tokuo T Tajima Kenji K

ACS omega 20201102 45

The development of eco-friendly fiber-reinforced composite resins is an important objective from an environmental perspective, and nanofibrillated bacterial cellulose (NFBC), with extremely long high-aspect-ratio fibers, is a filler material with high potential for use in such composite resins. In this study, we investigated chemical modification of the surfaces of NFBC fibers by coupling with (3-aminopropyl)trimethoxysilane and fabricated nanocomposite materials using the prepared surface-modif ...[more]

PMID: 33225187

Similar Datasets

Project description:3D-printed bone scaffolds hold great promise for the individualized treatment of critical-size bone defects. Among the resorbable polymers available for use as 3D-printable scaffold materials, poly(ε-caprolactone) (PCL) has many benefits. However, its relatively low stiffness and lack of bioactivity limit its use in load-bearing bone scaffolds. This study tests the hypothesis that surface-oxidized cellulose nanocrystals (SO-CNCs), decorated with carboxyl groups, can act as multi-functional scaffold additives that (1) improve the mechanical properties of PCL and (2) induce biomineral formation upon PCL resorption. To this end, an in vitro biomineralization study was performed to assess the ability of SO-CNCs to induce the formation of calcium phosphate minerals. In addition, PCL nanocomposites containing different amounts of SO-CNCs (1, 2, 3, 5, and 10 wt%) were prepared using melt compounding extrusion and characterized in terms of Young's modulus, ultimate tensile strength, crystallinity, thermal transitions, and water contact angle. Neither sulfuric acid-hydrolyzed CNCs (SH-CNCs) nor SO-CNCs were toxic to MC3T3 preosteoblasts during a 24 h exposure at concentrations ranging from 0.25 to 3.0 mg/mL. SO-CNCs were more effective at inducing mineral formation than SH-CNCs in simulated body fluid (1x). An SO-CNC content of 10 wt% in the PCL matrix caused a more than 2-fold increase in Young's modulus (stiffness) and a more than 60% increase in ultimate tensile strength. The matrix glass transition and melting temperatures were not affected by the SO-CNCs but the crystallization temperature increased by about 5.5°C upon addition of 10 wt% SO-CNCs, the matrix crystallinity decreased from about 43 to about 40%, and the water contact angle decreased from 87 to 82.6°. The abilities of SO-CNCs to induce calcium phosphate mineral formation and increase the Young's modulus of PCL render them attractive for applications as multi-functional nanoscale additives in PCL-based bone scaffolds.

Project description:Cellulose nanocrystals (CNCs) derived from renewable plant-based materials exhibit strong potential for improving properties of polymers by their dispersal in the polymer matrix as a composite phase. However, the hydrophilicity and low thermal stability of CNCs lead to compromised particle dispersibility in common polymers and limit the processing conditions of polymer-CNC composites, respectively. One route that has been explored is the modification of CNCs to alter surface chemistry. Acrylic materials are used in a broad class of polymers and copolymers with wide commercial applications. Yet, the available methods for adding groups that react with acrylics to enhance dispersion are quite limited. In this work, a versatile chemical modification route is described that introduces acryloyl functional groups on CNCs that can in turn be polymerized in subsequent steps to create acrylic-CNC composites. The hydroxyl group on CNC surfaces was reacted with the isocyanate moiety on 2-isocyanatoethyl methacrylate (IEM), a bifunctional molecule possessing both the isocyanate group and acryloyl group. The resulting modified CNCs (mCNCs) showed enhanced hydrophobicity and dispersibility in organic solvent relative to unmodified CNCs. Fourier transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy, solid-state 13C nuclear magnetic resonance (NMR) spectroscopy, and elemental analysis verified the surface modification and allowed an estimation of the degree of modification as high as 0.4 (26.7% surface hydroxyl substitution CNC). The modified CNCs were copolymerized with methyl methacrylate, and the composites had improved dispersion relative to composites with unmodified CNCs and enhanced (104%) tensile strength at 2 wt % CNC when compared to the neat poly(methyl methacrylate) (PMMA), indicating a benefit of the reactive acryloyl groups added to the CNC surface. Overall, the modification strategy was successful in functionalizing CNCs, opening possibilities for their use in organic media and matrices.

Dataset Information

Nanofibrillated Bacterial Cellulose Modified with (3-Aminopropyl)trimethoxysilane under Aqueous Conditions: Applications to Poly(methyl methacrylate) Fiber-Reinforced Nanocomposites.

Publications

Nanofibrillated Bacterial Cellulose Modified with (3-Aminopropyl)trimethoxysilane under Aqueous Conditions: Applications to Poly(methyl methacrylate) Fiber-Reinforced Nanocomposites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets