In vitro investigation of chemical properties and biocompatibility of neurovascular braided implants.

ABSTRACT: Braiding of Nitinol micro wires is an established technology for the manufacturing of fine-meshed neurovascular implants for tortuous vessel geometries. Electropolishing of wires before the braiding process has the potential to improve the in vitro behaviour in terms of thrombogenicity and endothelial cell proliferation. In this study, we present the first in vitro investigation of braided electropolished/blue oxide Nitinol samples in a blood flow loop, showing a significantly lower activation of the coagulation pathway (represented by the TAT III marker) and a tendency towards reduced platelet adhesion. Furthermore, we applied the same surface treatment on flat disks and measured protein adhesion as well as endothelial cell proliferation. We compared our results to non-electropolished samples with a native oxide surface. While platelet deposition was reduced on electropolished/blue oxide surface, a significant increase of endothelial cell seeding was observed. Investigation of inflammatory marker expression in endothelial cells provided divergent results depending on the marker tested, demanding closer investigation. Surface analysis using Auger electron spectroscopy revealed a thin layer mainly consisting of titanium oxynitride or titanium oxide?+?titanium nitride as a potential cause of the improved biological performance. Translated to the clinical field of intracranial aneurysm treatment, the improved biocompatibility has the potential to increase both safety (low thrombogenicity) and effectiveness (aneurysm neck reconstruction).

SUBMITTER: Cattaneo G

PROVIDER: S-EPMC7695648 | biostudies-literature | 2019 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

In vitro investigation of chemical properties and biocompatibility of neurovascular braided implants.

Cattaneo Giorgio G Bräuner Chris C Siekmeyer Gerd G Ding Andreas A Bauer Sabina S Wohlschlögel Markus M Lang Lisa L Hierlemann Teresa T Akimov Maria M Schlensak Christian C Schüßler Andreas A Wendel Hans-Peter HP Krajewski Stefanie S

Journal of materials science. Materials in medicine 20190604 6

Braiding of Nitinol micro wires is an established technology for the manufacturing of fine-meshed neurovascular implants for tortuous vessel geometries. Electropolishing of wires before the braiding process has the potential to improve the in vitro behaviour in terms of thrombogenicity and endothelial cell proliferation. In this study, we present the first in vitro investigation of braided electropolished/blue oxide Nitinol samples in a blood flow loop, showing a significantly lower activation o ...[more]

PMID: 31165278

Similar Datasets

Project description:BackgroundThe improvement of bone ingrowth into prosthesis and enhancement of the combination of the range between the bone and prosthesis are important for long-term stability of artificial joints. They are the focus of research on uncemented artificial joints. Porous materials can be of potential use to solve these problems.Objectives/purposesThis research aims to observe the characteristics of the new porous Ti-25Nb alloy and its biocompatibility in vitro, and to provide basic experimental evidence for the development of new porous prostheses or bone implants for bone tissue regeneration.MethodsThe Ti-25Nb alloys with different porosities were fabricated using powder metallurgy. The alloys were then evaluated based on several characteristics, such as mechanical properties, purity, pore size, and porosity. To evaluate biocompatibility, the specimens were subjected to methylthiazol tetrazolium (MTT) colorimetric assay, cell adhesion and proliferation assay using acridine staining, scanning electron microscopy, and detection of inflammation factor interleukin-6 (IL-6).ResultsThe porous Ti-25Nb alloy with interconnected pores had a pore size of 200 µm to 500 µm, which was favorable for bone ingrowth. The compressive strength of the alloy was similar to that of cortical bone, while with the elastic modulus closer to cancellous bone. MTT assay showed that the alloy had no adverse reaction to rabbit bone marrow mesenchymal stem cells, with a toxicity level of 0 to 1. Cell adhesion and proliferation experiments showed excellent cell growth on the surface and inside the pores of the alloy. According to the IL-6 levels, the alloy did not cause any obvious inflammatory response.ConclusionAll porous Ti-25Nb alloys showed good biocompatibility regardless of the percentage of porosity. The basic requirement of clinical orthopedic implants was satisfied, which made the alloy a good prospect for biomedical application. The alloy with 70% porosity had the optimum mechanical properties, as well as suitable pore size and porosity, which allowed more bone ingrowth.

Dataset Information

In vitro investigation of chemical properties and biocompatibility of neurovascular braided implants.

Publications

In vitro investigation of chemical properties and biocompatibility of neurovascular braided implants.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets