Adsorption and photocatalytic scavenging of 2-chlorophenol using carbon nitride-titania nanotubes based nanocomposite: Experimental data, kinetics and mechanism.

ABSTRACT: Adsorption and interaction of pollutant species on surface of the catalyst materials play an important role on the photocatalysis process. Herein, experimental data on the adsorption behavior of 2-chlorophenol (2-CP) onto graphitic pure carbon nitride (C₃N₄), titania nanotubes (TiO₂-NTs) and carbon nitride/titania nanotubes nanocomposite (C₃N₄/TiO₂-NTs) from synthetic wastewater has been summarized. The data on photocatalytic degradation of the 2-CP under both ultraviolet (UV) and visible light irradiation is also presented. This work also evaluates the 2-CP scavenging efficiency of C₃N₄/TiO₂-NTs nanocomposite prepared by calcination of 2 wt.% melamine with TiO₂-NTs at 450 °C. The adsorption and photocatalysis experiments were conducted for 180 min at pH 7 with 100 mL solution of 2-CP (40 mg/L) and 0.05 g catalyst material. The acquired data can be valuable to identify the equilibrium time for 2-CP adsorption onto C₃N₄, TiO₂-NTs, and C₃N₄/TiO₂-NTs nanocomposite. Moreover, the obtained data can be useful to identify the suitable light source for the decomposition of 2-CP in the aquatic environment. The evaluated kinetic data might be significant for identifying the adsorption and photocatalysis reaction rate onto the applied catalyst materials. The obtained adsorption and photocatalysis data have been compared with that in literature to identify the adsorption and photocatalysis behavior of 2-CP on numerous catalysts at different experimental conditions.

SUBMITTER: Barakat MA

PROVIDER: S-EPMC7770541 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Titania nanotube (TNT) powder was prepared by rapid breakdown anodization (RBA) in a perchloric acid electrolyte. The photocatalytic efficiency of the as-prepared and powders annealed at temperatures between 250 and 550 °C was tested under UV and natural sunlight irradiation by decolorization of both anionic and cationic organic dyes, i.e., methyl orange (MO) and rhodamine B (RhB), as model pollutants. The tubular structure of the nanotubes was retained up to 250 °C, while at 350 °C and above, the nanotubes transformed into nanorods and nanoparticles. Depending on the annealing temperature, the TNTs consist of anatase, mixed anatase/brookite, or anatase/rutile phases. The bandgap of the as-prepared nanotubes is 3.04 eV, and it shifts towards the visible light region upon annealing. The X-ray photoelectron spectroscopy (XPS) results show the presence of titania and impurities including chlorine on the surface of the TNTs. The atomic ratio of Ti/O remains unchanged for the annealed TNTs, but the concentration of chlorine decreases with temperature. The photoluminescence (PL) indicate high electron-hole recombination for the as-prepared TNTs, probably due to the residual impurities, low crystallinity, and vacancies in the structure, while the highest photocurrent was observed for the TNT sample annealed at 450 °C. The TNTs induce a small degradation of the dyes under UV light; however, contrary to previous reports, complete decolorization of dyes is observed under sunlight. All TNT samples showed higher decolorization rates under sunlight irradiation than under UV light. The highest reaction rate for the TNT samples was obtained for the as-prepared TNT powder sample under sunlight using RhB (?1 = 1.29 h-1). This is attributed to the bandgap, specific surface area and the crystal structure of the nanotubes. The as-prepared TNTs performed most efficiently for decolorization of RhB and outperformed the reference anatase powder under sunlight irradiation. This could be attributed to the abundance of reactive sites, higher specific surface area, and degradation mechanism of RhB. These RBA TNT photocatalyst powders demonstrate a more efficient use of the sunlight spectrum, making them viable for environmental remediation.

Dataset Information

Adsorption and photocatalytic scavenging of 2-chlorophenol using carbon nitride-titania nanotubes based nanocomposite: Experimental data, kinetics and mechanism.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets