Preparation and Swelling Behaviors of High-Strength Hemicellulose-g-Polydopamine Composite Hydrogels.

ABSTRACT: Hemicellulose-based composite hydrogels were successfully prepared by adding polydopamine (PDA) microspheres as reinforcing agents. The effects of PDA microsphere size, dosage, and nitrogen content in hydrogel on the mechanical and rheological properties was studied. The compressive strength of hydrogel was increased from 0.11 to 0.30 MPa. The storage modulus G' was increased from 7.9 to 22.0 KPa. The gaps in the hemicellulose network are filled with PDA microspheres. There is also chemical cross-linking between them. These gaps increased the density of the hydrogel network structure. It also has good water retention and pH sensitivity. The maximum cumulative release rate of methylene blue was 62.82%. The results showed that the release behavior of hydrogel was pH-responsive, which was beneficial to realizing targeted and controlling drug release.

SUBMITTER: Ge J

PROVIDER: S-EPMC7795248 | biostudies-literature | 2021 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Preparation and Swelling Behaviors of High-Strength Hemicellulose-g-Polydopamine Composite Hydrogels.

Ge Jiayan J Gu Kaiqi K Sun Kewen K Wang Xinyue X Yao Shuangquan S Mo Xiaorong X Long Shuilian S Lan Tingting T Qin Chengrong C

Materials (Basel, Switzerland) 20210102 1

Hemicellulose-based composite hydrogels were successfully prepared by adding polydopamine (PDA) microspheres as reinforcing agents. The effects of PDA microsphere size, dosage, and nitrogen content in hydrogel on the mechanical and rheological properties was studied. The compressive strength of hydrogel was increased from 0.11 to 0.30 MPa. The storage modulus G' was increased from 7.9 to 22.0 KPa. The gaps in the hemicellulose network are filled with PDA microspheres. There is also chemical cros ...[more]

PMID: 33401706

Similar Datasets

Project description:BackgroundTissue engineering, which involves the selection of scaffold materials, presents a new therapeutic strategy for damaged tissues or organs. Scaffold design based on blends of proteins and polysaccharides, as mimicry of the native extracellular matrix, has recently become a valuable strategy for tissue engineering.ObjectiveThis study aimed to construct composite hydrogels based on natural polymers for tissue engineering.MethodsComposite hydrogels based on blends of gelatin with a polysaccharide component (chitosan or alginate) were produced and subsequently enzyme crosslinked. The other three hydrogels, chitosan hydrogel, sodium alginate hydrogel, and microbial transglutaminase-crosslinked gelatin (mTG/GA) hydrogel were also prepared. All hydrogels were evaluated for in vitro degradation property, swelling capacity, and mechanical property. Rat adipose-derived stromal stem cells (ADSCs) were isolated and seeded on (or embedded into) the above-mentioned hydrogels. The morphological features of ADSCs were observed and recorded. The effects of the hydrogels on ADSC survival and adhesion were investigated by immunofluorescence staining. Cell proliferation was tested by thiazolyl blue tetrazolium bromide (MTT) assay.ResultsCell viability assay results showed that the five hydrogels are not cytotoxic. The mTG/GA and its composite hydrogels showed higher compressive moduli than the single-component chitosan and alginate hydrogels. MTT assay results showed that ADSCs proliferated better on the composite hydrogels than on the chitosan and alginate hydrogels. Light microscope observation and cell cytoskeleton staining showed that hydrogel strength had obvious effects on cell growth and adhesion. The ADSCs seeded on chitosan and alginate hydrogels plunged into the hydrogels and could not stretch out due to the low strength of the hydrogel, whereas cells seeded on composite hydrogels with higher elastic modulus, could spread out, and grew in size.ConclusionThe gelatin-polysaccharide composite hydrogels could serve as attractive biomaterials for tissue engineering due to their easy preparation and favorable biophysical properties.

Dataset Information

Preparation and Swelling Behaviors of High-Strength Hemicellulose-g-Polydopamine Composite Hydrogels.

Publications

Preparation and Swelling Behaviors of High-Strength Hemicellulose-g-Polydopamine Composite Hydrogels.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets