Evaluation of the Hemocompatibility and Anticancer Potential of Poly(?-Caprolactone) and Poly(3-Hydroxybutyrate) Microcarriers with Encapsulated Chrysin.

ABSTRACT: In this work, novel chrysin-loaded poly(?-caprolactone) and poly(3-hydroxybutyrate) microcarriers were synthesized according to a modified oil-in-water single emulsion/solvent evaporation method, utilizing poly(vinyl alcohol) surfactant as stabilizer and dispersing agent for the emulsification, and were evaluated for their physico-chemical and morphological properties, loading capacity and entrapment efficiency and in vitro release of their load. The findings suggest that the novel micro-formulations possess a spherical and relatively wrinkled structure with sizes ranging between 2.4 and 24.7 µm and a highly negative surface charge with z-potential values between (-18.1)-(-14.1) mV. The entrapment efficiency of chrysin in the poly(?-caprolactone) and poly(3-hydroxybutyrate) microcarriers was estimated to be 58.10% and 43.63%, whereas the loading capacity was found to be 3.79% and 15.85%, respectively. The average release percentage of chrysin was estimated to be 23.10% and 18.01%, respectively. The novel micromaterials were further biologically evaluated for their hemolytic activity through hemocompatibility studies over a range of hematological parameters and cytoxicity against the epithelial human breast cancer cell line MDA-MB 231. The poly(?-caprolactone) and poly(3-hydroxybutyrate) microcarriers reached an IC₅₀ value with an encapsulated chrysin content of 149.19 µM and 312.18 µM, respectively, and showed sufficient blood compatibility displaying significantly low (up to 2%) hemolytic percentages at concentrations between 5 and 500 µg·mL^-1.

SUBMITTER: Halevas E 

PROVIDER: S-EPMC7831015 | biostudies-literature | 2021 Jan

REPOSITORIES: biostudies-literature