Recyclable High-Performance Epoxy-Anhydride Resins with DMP-30 as the Catalyst of Transesterification Reactions.

ABSTRACT: Epoxy-anhydride resins are widely used in engineering fields due to their excellent performance. However, the insolubility and infusibility make the recycling of epoxy resins challenging. The development of degradable epoxy resins with stable covalent networks provides an efficient solution to the recycling of thermosets. In this paper, 2,4,6-tris(dimethylaminomethyl)phenol (DMP-30) is incorporated into the epoxy-glutaric anhydride (GA) system to prepare high-performance epoxy resins that can be recycled below 200 °C at ordinary pressure via ethylene glycol (EG) participated transesterification. The tertiary amine groups in DMP-30 can catalyze the curing reaction of epoxy and anhydride, as well as the transesterification between ester bonds and alcoholic hydroxyl groups. Compared with early recyclable anhydride-cured epoxy resins, the preparation and recycling of diglycidyl ether of bisphenol A (DGEBA)/GA/DMP-30 systems do not need any special catalysts such as TBD, Zn(Ac)₂, etc., which are usually expensive, toxic, and have poor compatibility with other compounds. The resulting resins have glass transition temperatures and strengths similar to those of conventional epoxy resins. The influences of GA content, DMP-30 content, and temperature on the dissolution rate were studied. The decomposed epoxy oligomer (DEO) is further used as a reaction ingredient to prepare new resins. It is found that the DEO can improve the toughness of epoxy resins significantly. This work provides a simple method to prepare readily recyclable epoxy resins, which is of low-cost and easy to implement.

SUBMITTER: Zhao W

PROVIDER: S-EPMC7831910 | biostudies-literature | 2021 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Recyclable High-Performance Epoxy-Anhydride Resins with DMP-30 as the Catalyst of Transesterification Reactions.

Zhao Wenzhe W An Le L Wang Shujuan S

Polymers 20210118 2

Epoxy-anhydride resins are widely used in engineering fields due to their excellent performance. However, the insolubility and infusibility make the recycling of epoxy resins challenging. The development of degradable epoxy resins with stable covalent networks provides an efficient solution to the recycling of thermosets. In this paper, 2,4,6-tris(dimethylaminomethyl)phenol (DMP-30) is incorporated into the epoxy-glutaric anhydride (GA) system to prepare high-performance epoxy resins that can be ...[more]

PMID: 33477708

Similar Datasets

Project description:Photoresists (or photo-resins) are the main and most important raw material used for lithography techniques such as deep X-ray (DXRL), ultraviolet (UVL), deep-UV (DUVL), and extreme UV (EUVL). In previous work, we showed how complicated could be the synthesis of the resins used to produce photoresist. In this study, we follow up on the strategy of tuning deep and macro levels of properties to formulate photo-resins. They were developed from a primary basis, using epoxy resins, a solvent, and a photoinitiator in several concentrations. The formulations were evaluated initially by the UVL technique, using a squared pattern of 2.3 mm2. The most suitable compositions were then studied in a pattern structure varying from 50 down to 1 µm width, applying UVL and DUVL. The patterned structures were compared with the chemical composition of the photo-resins. Considering the deep level of properties, polydispersion, and epoxidation degree were evaluated. Regarding the macro level of properties, the concentration of photoinitiator was studied. Promising results have been achieved with the control of the deep and macro levels methodology. By means of UV lithography, it was possible to note, for a large feature size above 2.0 mm2, the formulations presented good quality structures with a broad range of epoxidation degrees and photoinitiator concentrations, respectively from 3 to 100% (mol·molpolymer-1) and from 10 to 40% (mol·molpolymer-1). For structures smaller than 50 µm width, the composition of the photo-resins may be restricted to a narrow range of values regarding the formulation. The results indicate that the polydispersion of the oligomers might be a significant property to control. There is a tendency to better outcome with a low polydispersity (resins P1 and P2). Regarding UV and deep-UV irradiation, the best results were achieved with UV. Nevertheless, for DUV, the sensitivity seems to be more intense, leading to well-defined structures with over-exposure effects.

Dataset Information

Recyclable High-Performance Epoxy-Anhydride Resins with DMP-30 as the Catalyst of Transesterification Reactions.

Publications

Recyclable High-Performance Epoxy-Anhydride Resins with DMP-30 as the Catalyst of Transesterification Reactions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets