Comparison of microleakage between different restorative materials to restore marginal gap at crown margin.

ABSTRACT:

Background

An occurrence of secondary caries around the indirect restoration margin is reported to remain a leading cause of failures.

Objective

This study aimed to test the interfacial microleakage of conventional glass-ionomer (CGI), resin-modified glass ionomer (RMGI) and Nano-hybrid composite (CR) restorations at a full veneer margin crown.

Methods

Ninety human extracted molar teeth were divided into three groups (n = 30). Each group was subdivided into three subgroups (n = 10) according to the extent of the structural defects; The structural defect in G1 had a depth of 1.5 mm, width and length at 2 mm and 1 mm intrusion within the crown cervical margin. The corresponding structural defect dimension values for G2 were 2, 5, 4 and 2 mm with defects extending onto the root structure. Meanwhile, G3: structural deficiency of 2 mm depth, 3 mm width and 3 mm length and with 1.5 mm extension into the prepared teeth. These structural defects in each subgroup were restored with CGI, RMGI and CR. Artificial carious lesion formation was induced at the cervical finish line with a demineralizing solution. The artificial carious lesions were restored as per the group distribution. Subsequently, teeth samples were prepared and cemented with Nickel-chromium full coverage restorations utilizing glass-ionomer luting cement. Teeth samples were thermocycled, isolated with nail varnish, and immersed in 0.1% methylene blue for 24 h. The teeth samples were sectioned longitudinally, dye penetration was evaluated with a stereomicroscope. The data were analyzed with Kruskal-Wallis and Mann-Whitney U tests.

Results

CGI-G1 recorded the highest micro-leakage score at 1.450; while CR-G3 recorded the least score (0.350). At a cementum-restoration interface, CR-G1 (0.850) documented the lowest micro-leakage; RMGI-G3 had a greater value at 1.700.

Conclusions

The hybrid CR could be effectively used to restore the restoration of a marginal gap around crown margins.

SUBMITTER: Haralur SB

PROVIDER: S-EPMC7916530 | biostudies-literature | 2021

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Comparison of microleakage between different restorative materials to restore marginal gap at crown margin.

Haralur Satheesh B SB Al Ghaseb Ghaseb Ahmed GA Alqahtani Norah Ali NA Alqahtani Bader B

PeerJ 20210225

<h4>Background</h4>An occurrence of secondary caries around the indirect restoration margin is reported to remain a leading cause of failures.<h4>Objective</h4>This study aimed to test the interfacial microleakage of conventional glass-ionomer (CGI), resin-modified glass ionomer (RMGI) and Nano-hybrid composite (CR) restorations at a full veneer margin crown.<h4>Methods</h4>Ninety human extracted molar teeth were divided into three groups (<i>n</i> = 30). Each group was subdivided into three sub ...[more]

PMID: 33665019

Similar Datasets

Project description:PurposeTo compare the short-term restorative effect and periodontal health status of restorations with different materials in full-crown restoration of mandibular premolar tooth defects.MethodsA total of 105 cases (123 affected teeth) of mandibular premolar tooth defects who visited the Department of Stomatology between January 2019 and January 2020 were selected, of which 58 cases (68 affected teeth) restored with cobalt-chromium alloy porcelain crowns were included in the metal-ceramic crown (MCC) group and 47 cases (55 affected teeth) repaired by zirconium dioxide all-ceramic crowns were assigned to the zirconia crown (ZC) group. The restorative effect, inflammatory factors (high-sensitivity C-reactive protein (hs-CRP) and tumor necrosis factor-α (TNF-α)) and periodontal health indicators (human cartilage glycoprotein-39 (YKL-40), resistin, aspartate aminotransferase (AST), and alkaline phosphatase (ALP)) after treatment, and the occurrence of adverse reactions were compared between the two groups.ResultsThe ZC group outperformed the MCC group in terms of margin fitness, restoration fracture, gingival condition, and color matching. After restoration, hs-CRP and TNF-α were statistically decreased in both groups, while YKL-40, resistin, AST, and ALP were significantly increased; and compared with the MCC group, hs-CRP, TNF-α, YKL-40, resistin, AST, and ALP were lower in the ZC group. The ZC group also scored statistically higher in retention effect, aesthetic effect, masticatory function, voice function, and comfort. Moreover, the ZC group had a higher total effective rate and a lower incidence of adverse reactions than the MCC group, with statistical significance.ConclusionsZirconia dioxide all-ceramic crowns contribute to a better short-term restorative effect in the full-crown restoration of mandibular premolar tooth defects, with little impact on periodontal health and high patient satisfaction, which deserves popularization and application.

Project description:Fabricating method may affect the surface properties and biological characteristics of provisional restorations. This study aimed to evaluate the surface roughness, plaque accumulation, and cytotoxicity of provisional restorative materials fabricated by the conventional, digital subtractive and additive methods. Sixty-six bar-shaped specimens (2×4×10 mm) were fabricated by using provisional restorative materials through the conventional, digital subtractive and additive methods (n = 22 per group). Ten specimens of each group were used for surface roughness and plaque accumulation tests, 10 specimens for cytotoxicity assay, and 2 specimens of each group were used for qualitative assessment by scanning electron microscopy. The Ra (roughness average) and Rz (roughness height) values (μm) were measured via profilometer, and visual inspection was performed through scanning electron microscopy. Plaque accumulation of Streptococcus mutans and cytotoxicity on human gingival fibroblast-like cells were evaluated. The data were analyzed with one-way ANOVA and Tukey's post hoc test (α = 0.05). Surface roughness, biofilm accumulation and cytotoxicity were significantly different among the groups (P<0.05). Surface roughness was significantly higher in the conventional group (P<0.05); however, the two other groups were not significantly different (P>0.05). Significantly higher bacterial attachment was observed in the additive group than the subtractive (P<0.001) and conventional group (P = 0.025); while, the conventional and subtractive groups were statistically similar (P = 0.111). Regarding the cytotoxicity, the additive group had significantly higher cell viability than the subtractive group (P = 0.006); yet, the conventional group was not significantly different from the additive (P = 0.354) and subtractive group (P = 0.101). Surface roughness was the highest in conventionally cured group; but, the additive group had the most plaque accumulation and lowest cytotoxicity.

Dataset Information

Comparison of microleakage between different restorative materials to restore marginal gap at crown margin.

Background

Objective

Methods

Results

Conclusions

Publications

Comparison of microleakage between different restorative materials to restore marginal gap at crown margin.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets