Stable and Reversible Photoluminescence from GaN Nanowires in Solution Tuning by Ionic Concentration.

ABSTRACT: We report response of photoluminescence (PL) from GaN nanowires without protection in solutions. The distinct response is not only toward pH but toward ionic concentration under same pH. The nanowires appear to be highly stable under aqueous solution with high ionic concentration and low pH value down to 1. We show that the PL has a reversible interaction with various types of acidic and salt solutions. The quantum states of nanowires are exposed to the external environment and have a direct physical interaction which depends on the anions of the acids. As the ionic concentration increases, the PL intensity goes up or down depending on the chemical species. The response results from a competition of change in surface band bending and charge transfer to redox level in solution. That of GaN films is reported for comparison as the effect of surface band bending can be neglected so that there are only slight variations in PL intensity for GaN films. Additionally, such physical interaction does not impact on the PL peaks in acids and salts, whereas there is a red shift on PL when the nanowires are in basic solution, say NH4OH, due to chemical etching occurred on the nanowires.

SUBMITTER: Nguyen AT

PROVIDER: S-EPMC7952484 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Determination of the concentration of impurities in GaN from photoluminescence and secondary-ion mass spectrometry.

Project description:Photoluminescence (PL) was used to estimate the concentration of carbon in GaN grown by hydride vapor phase epitaxy (HVPE). The PL data were compared with profiles of the impurities obtained from secondary ion mass spectrometry (SIMS) measurements. Comparison of PL and SIMS data has revealed that apparently high concentrations of C and O at depths up to 1?µm in SIMS profiles do not represent depth distributions of these species in the GaN matrix but are rather caused by post-growth surface contamination and knocking-in impurity species from the surface. In particular, PL analysis supplemented by reactive ion etching up to the depth of 400?nm indicates that the concentration of carbon in nitrogen sites is below 2-5?×?1015?cm-3 at any depth of GaN samples grown by HVPE. We demonstrate that PL is a very sensitive and reliable tool to determine the concentrations of impurities in the GaN matrix.

| S-EPMC7010669 | biostudies-literature

Conducting polymer nanowires for control of local protein concentration in solution.

Project description:Interfacing devices with cells and tissues requires new nanoscale tools that are both flexible and electrically active. We demonstrate the use of PEDOT:PSS conducting polymer nanowires for the local control of protein concentration in water and biological media. We use fluorescence microscopy to compare the localization of serum albumin in response to electric fields generated by narrow (760 nm) and wide (1.5 μm) nanowires. We show that proteins in deionized water can be manipulated over a surprisingly large micron length scale and that this distance is a function of nanowire diameter. In addition, white noise can be introduced during the electrochemical synthesis of the nanowire to induce branches into the nanowire allowing a single device to control multiple nanowires. An analysis of growth speed and current density suggests that branching is due to the Mullins-Sekerka instability, ultimately controlled by the roughness of the nanowire surface. These small, flexible, conductive, and biologically compatible PEDOT:PSS nanowires provide a new tool for the electrical control of biological systems.

| S-EPMC8153065 | biostudies-literature

Ionic liquids with reversible photo-induced conductivity regulation in aqueous solution.

Project description:Stimulus-responsive ionic liquids have gained significant attention for their applications in various areas. Herein, three kinds of azobenzimidazole ionic liquids with reversible photo-induced conductivity regulation were designed and synthesized. The change of electrical conductivity under UV/visible light irradiation in aqueous solution was studied, and the effect of chemical structure and concentration of ionic liquids containing azobenzene to the regulation of photoresponse conductivity were discussed. The results showed that exposing the ionic liquid aqueous solution to ultraviolet light significantly increased its conductivity. Ionic liquids with longer alkyl chains exhibited an even greater increase in conductivity, up to 75.5%. Then under the irradiation of visible light, the electrical conductivity of the solution returned to its initial value. Further exploration of the mechanism of the reversible photo-induced conductivity regulation of azobenzene ionic liquids aqueous solution indicated that this may attributed to the formation/dissociation of ionic liquids aggregates in aqueous solution induced by the isomerization of azobenzene under UV/visible light irradiation and resulted the reversible conductivity regulation. This work provides a way for the molecular designing and performance regulation of photo-responsive ionic liquid and were expected to be applied in devices with photoconductive switching and micro photocontrol properties.

| S-EPMC10447455 | biostudies-literature

Enhanced UV Emission of GaN Nanowires Functionalized by Wider Band Gap Solution-Processed p-MnO Quantum Dots.

Project description:GaN-based UV light-emitting devices suffer from low efficiency. To mitigate this issue, we hybridized GaN nanowires (NWs) grown on Si substrates by plasma-assisted molecular beam epitaxy with solution-processed p-type MnO quantum dots (QDs) characterized by a wider band gap (∼5 eV) than that of GaN. Further investigations reveal that the photoluminescence intensity of the GaN NWs increases up to ∼3.9-fold (∼290%) after functionalizing them with p-MnO QDs, while the internal quantum efficiency is improved by ∼1.7-fold. Electron energy loss spectroscopy (EELS) incorporated into transmission electron microscopy reveals an increase in the density of states in QD-decorated NWs compared to the bare ones. The advanced optical and EELS analyses indicate that the energy transfer from the wider band gap p-MnO QDs to n-GaN NW can lead to substantial emission enhancement and greater radiative recombination contribution because of the good band alignment between MnO QDs and GaN NWs. This work provides valuable insights into an environmentally friendly strategy for improving UV device performance.

| S-EPMC7497627 | biostudies-literature

Photoluminescence Characteristics of Zinc Blende InAs Nanowires.

Project description:A detailed understanding of the optical properties of self-catalysed (SC), zinc blende (ZB) dominant, nanowires (NWs) is crucial for the development of functional and impurity-free nanodevices. Despite the fact that SC InAs NWs mostly crystallize in the WZ/ZB phase, there are very limited reports on the photoluminescence (PL) properties of ZB InAs NWs. Here, we report on the PL properties of Molecular Beam Epitaxy grown, SC InAs NWs. The as-grown NWs exhibit a dominant band to band (BtB) peak associated with ZB, InAs with an emission energy of ~0.41?eV in good agreement with the band gap energy of ZB InAs and significantly lower than that of the wurtzite phase (~0.48?eV). The strong BtB peak persists to near room temperature with a distinct temperature-dependent red-shift and very narrow spectral linewidth of ~20?meV (10?K) which is much smaller than previously reported values. A narrowing in PL linewidth with increasing NWs diameter is correlated with a decline in the influence of surface defects resulting from an enlargement in NWs diameter. This study demonstrates the high optical property of SC InAs NWs which is compatible with the Si-complementary metal-oxide-semiconductor technology and paves the way for the monolithic integration of InAs NWs with Si in novel nanodevices.

| S-EPMC6881312 | biostudies-literature

Reversible structure manipulation by tuning carrier concentration in metastable Cu<sub>2</sub>S.

Project description:The optimal functionalities of materials often appear at phase transitions involving simultaneous changes in the electronic structure and the symmetry of the underlying lattice. It is experimentally challenging to disentangle which of the two effects--electronic or structural--is the driving force for the phase transition and to use the mechanism to control material properties. Here we report the concurrent pumping and probing of Cu2S nanoplates using an electron beam to directly manipulate the transition between two phases with distinctly different crystal symmetries and charge-carrier concentrations, and show that the transition is the result of charge generation for one phase and charge depletion for the other. We demonstrate that this manipulation is fully reversible and nonthermal in nature. Our observations reveal a phase-transition pathway in materials, where electron-induced changes in the electronic structure can lead to a macroscopic reconstruction of the crystal structure.

| S-EPMC5604034 | biostudies-literature

Origin of the Avalanche-Like Photoluminescence from Metallic Nanowires.

Project description:Surface plasmonic systems provide extremely efficient ways to modulate light-matter interaction in photon emission, light harvesting, energy conversion and transferring, etc. Various surface plasmon enhanced luminescent behaviors have been observed and investigated in these systems. But the origin of an avalanche-like photoluminescence, which was firstly reported in 2007 from Au and subsequently from Ag nanowire arrays/monomers, is still not clear. Here we show, based on systematic investigations including the excitation power/time related photoluminescent measurements as well as calculations, that this avalanche-like photoluminescence is in fact a result of surface plasmon assisted thermal radiation. Nearly all of the related observations could be perfectly interpreted with this concept. Our finding is crucial for understanding the surface plasmon mediated thermal and photoemission behaviors in plasmonic structures, which is of great importance in designing functional plasmonic devices.

| S-EPMC4700426 | biostudies-literature

Laser-induced greenish-blue photoluminescence of mesoporous silicon nanowires.

Project description:Solid silicon nanowires and their luminescent properties have been widely studied, but lesser is known about the optical properties of mesoporous silicon nanowires (mp-SiNWs). In this work, we present a facile method to generate greenish-blue photoluminescence (GB-PL) by fast scanning a focused green laser beam (wavelength of 532?nm) on a close-packed array of mp-SiNWs to carry out photo-induced chemical modification. The threshold of laser power is 5?mW to excite the GB-PL, whose intensity increases with laser power in the range of 5-105?mW. The quenching of GB-PL comes to occur beyond 105?mW. The in-vacuum annealing effectively excites the GB-PL in the pristine mp-SiNWs and enhances the GB-PL of the laser-modified mp-SiNWs. A complex model of the laser-induced surface modification is proposed to account for the laser-power and post-annealing effect. Moreover, the fast scanning of focused laser beam enables us to locally tailor mp-SiNWs en route to a wide variety of micropatterns with different optical functionality, and we demonstrate the feasibility in the application of creating hidden images.

| S-EPMC4018655 | biostudies-literature

Project description:The semiconductor nanowire architecture provides opportunities for non-planar electronics and optoelectronics arising from its unique geometry. This structure gives rise to a large surface area-to-volume ratio and therefore understanding the effect of nanowire surfaces on nanowire optoelectronic properties is necessary for engineering related devices. We present a systematic study of the non-uniform optical properties of Au-catalyzed GaAs/AlGaAs core-shell nanowires introduced by changes in the sidewall faceting. Significant variation in intra-wire photoluminescence (PL) intensity and PL lifetime (τ PL ) was observed along the nanowire axis, which was strongly correlated with the variation of sidewall facets from {112} to {110} from base to tip. Faster recombination occurred in the vicinity of {112}-oriented GaAs/AlGaAs interfaces. An alternative nanowire heterostructure, the radial quantum well tube consisting of a GaAs layer sandwiched between two AlGaAs barrier layers, is proposed and demonstrates superior uniformity of PL emission along the entire length of nanowires. The results emphasize the significance of nanowire facets and provide important insights for nanowire device design.

| S-EPMC7750184 | biostudies-literature

Linearly polarized photoluminescence of InGaN quantum disks embedded in GaN nanorods.

Project description:We have investigated the emission from InGaN/GaN quantum disks grown on the tip of GaN nanorods. The emission at 3.21?eV from the InGaN quantum disk doesn't show a Stark shift, and it is linearly polarized when excited perpendicular to the growth direction. The degree of linear polarization is about 39.3% due to the anisotropy of the nanostructures. In order to characterize a single nanostructure, the quantum disks were dispersed on a SiO2 substrate patterned with a metal reference grid. By rotating the excitation polarization angle from parallel to perpendicular relative to the nanorods, the variation of overall PL for the 3.21?eV peak was recorded and it clearly showed the degree of linear polarization (DLP) of 51.5%.

| S-EPMC5970171 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data