Fabrication and Properties of Electrospun Collagen Tubular Scaffold Crosslinked by Physical and Chemical Treatments.

ABSTRACT: Tissue engineered scaffold was regarded as a promising approach instead of the autograft. In this study, small diameter electrospun collagen tubular scaffold with random continuous smooth nanofibers was successfully fabricated. However, the dissolution of collagen in concentrated aqueous (conc. aq.) acetic acid caused to the serious denaturation of collagen. A novel method ammonia treatment here was adopted which recovered the collagen triple helix structure according to the analysis of IR spectra. Further dehydrothermal (DHT) and glutaraldehyde (GTA) treatments were applied to introduce the crosslinks to improve the properties of collagen tube. The nanofibrous structure of collagen tube in a wet state was preserved by the crosslinking treatments. Swelling ratio and weight loss decreased by at least two times compared to those of the untreated collagen tube. Moreover, tensile strength was significantly enhanced by DHT treatment (about 0.0076 cN/dTex) and by GTA treatment (about 0.075 cN/dTex). In addition, the surface of crosslinked collagen tube kept the hydrophilic property. These results suggest that DHT and GTA treatments can be utilized to improve the properties of electrospun collagen tube which could become a suitable candidate for tissue engineered scaffold.

SUBMITTER: Chen X

PROVIDER: S-EPMC7957483 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Fabrication and Properties of Electrospun Collagen Tubular Scaffold Crosslinked by Physical and Chemical Treatments.

Chen Xuefei X Meng Jie J Xu Huaizhong H Shinoda Masaya M Kishimoto Masanori M Sakurai Shinichi S Yamane Hideki H

Polymers 20210228 5

Tissue engineered scaffold was regarded as a promising approach instead of the autograft. In this study, small diameter electrospun collagen tubular scaffold with random continuous smooth nanofibers was successfully fabricated. However, the dissolution of collagen in concentrated aqueous (conc. aq.) acetic acid caused to the serious denaturation of collagen. A novel method ammonia treatment here was adopted which recovered the collagen triple helix structure according to the analysis of IR spect ...[more]

PMID: 33670963

Similar Datasets

Project description:Tissue engineering techniques using novel scaffolding materials offer potential alternatives for managing tendon disorders. An ideal tendon tissue engineered scaffold should mimic the three-dimensional (3D) structure of the natural extracellular matrix (ECM) of the native tendon. Here, we propose a novel electrospun nanoyarn network that is morphologically and structurally similar to the ECM of native tendon tissues. The nanoyarn, random nanofiber, and aligned nanofiber scaffolds of a synthetic biodegradable polymer, poly(L-lactide-co-?-caprolactone) [P(LLA-CL)], and natural collagen I complex were fabricated using electrospinning. These scaffolds were characterized in terms of fiber morphology, pore size, porosity, and chemical and mechanical properties for the purpose of culturing tendon cells (TCs) for tendon tissue engineering. The results indicated a fiber diameter of 632 ± 81 nm for the random nanofiber scaffold, 643 ± 97 nm for the aligned nanofiber scaffold, and 641 ± 68 nm for the nanoyarn scaffold. The yarn in the nanoyarn scaffold was twisted by many nanofibers similar to the structure and inherent nanoscale organization of tendons, indicating an increase in the diameter of 9.51 ± 3.62 ?m. The nanoyarn scaffold also contained 3D aligned microstructures with large interconnected pores and high porosity. Fourier transform infrared analyses revealed the presence of collagen in the three scaffolds. The mechanical properties of the sample scaffolds indicated that the scaffolds had desirable mechanical properties for tissue regeneration. Further, the results revealed that TC proliferation and infiltration, and the expression of tendon-related ECM genes, were significantly enhanced on the nanoyarn scaffold compared with that on the random nanofiber and aligned nanofiber scaffolds. This study demonstrates that electrospun P(LLA-CL)/collagen nanoyarn is a novel, 3D, macroporous, aligned scaffold that has potential application in tendon tissue engineering.

Dataset Information

Fabrication and Properties of Electrospun Collagen Tubular Scaffold Crosslinked by Physical and Chemical Treatments.

Publications

Fabrication and Properties of Electrospun Collagen Tubular Scaffold Crosslinked by Physical and Chemical Treatments.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets