Strain-induced yellow to blue emission tailoring of axial InGaN/GaN quantum wells in GaN nanorods synthesized by nanoimprint lithography.

ABSTRACT: GaN nanorods (NRds) with axial InGaN/GaN MQWs insertions are synthesized by an original cost-effective and large-scale nanoimprint-lithography process from an InGaN/GaN MQWs layer grown on c-sapphire substrates. By design, such NRds exhibit a single emission due to the c-axis MQWs. A systematic study of the emission of the NRds by time-resolved luminescence (TR-PL) and power dependence PL shows a diameter-controlled luminescence without significant degradation of the recombination rate thanks to the diameter-controlled strain tuning and QSCE. A blueshift up to 0.26 eV from 2.28 to 2.54 eV (543 nm to 488 nm) is observed for 3.2 nm thick InGaN/GaN QWs with an In composition of 19% when the NRds radius is reduced from 650 to 80 nm. The results are consistent with a 1-D based strain relaxation model. By combining state of the art knowledge of c-axis growth and the strong strain relieving capability of NRds, this process enables multiple and independent single-color emission from a single uniform InGaN/GaN MQWs layer in a single patterning step, then solving color mixing issue in InGaN based nanorods LED devices.

SUBMITTER: Avit G

PROVIDER: S-EPMC7990954 | biostudies-literature | 2021 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Strain-induced yellow to blue emission tailoring of axial InGaN/GaN quantum wells in GaN nanorods synthesized by nanoimprint lithography.

Avit Geoffrey G Robin Yoann Y Liao Yaqiang Y Nan Hu H Pristovsek Markus M Amano Hiroshi H

Scientific reports 20210324 1

GaN nanorods (NRds) with axial InGaN/GaN MQWs insertions are synthesized by an original cost-effective and large-scale nanoimprint-lithography process from an InGaN/GaN MQWs layer grown on c-sapphire substrates. By design, such NRds exhibit a single emission due to the c-axis MQWs. A systematic study of the emission of the NRds by time-resolved luminescence (TR-PL) and power dependence PL shows a diameter-controlled luminescence without significant degradation of the recombination rate thanks to ...[more]

PMID: 33762623

Similar Datasets

Project description:Cubic InGaN alloys are a promising candidate material for next-generation optoelectronic applications as they lack internal fields and promise to cover large parts of the electromagnetic spectrum from the deep UV toward the mid-infrared. This demands high-quality epitaxial growth of cubic InGaN/GaN quantum wells, especially for the red energy range. However, the growth of indium-bearing nitride quantum wells in the metastable cubic phase still poses many challenges. InGaN and GaN are typically grown at different temperatures and with different metal fluxes in molecular beam epitaxy, leading to either long waiting periods for temperature adjustment or growth under suboptimal conditions. Both degrade the crystal quality and optical properties. In this study, we apply a metal-modulated growth approach in molecular beam epitaxy that enables us to grow either self-assembled, phase pure, cubic InGaN/GaN multi quantum wells (MQWs) or homogeneous c-InGaN layers, only by adjusting the shutter duration times for Ga and In. We achieve smooth surfaces and sharp interfaces with a quantum well thickness tunable from 6 to 16 nm and a barrier thickness ranging from 4 to 10 nm. X-ray diffraction confirms >99% phase purity of our cubic layers, while time-of-flight secondary ion mass spectrometry, scanning transmission electron microscopy, and energy-dispersive X-ray spectroscopy provide detailed information on the quantum well composition and strain. Photoluminescence measurements at room temperature demonstrate the emission properties of the samples, with the emission wavelength ranging from 540 to 670 nm. Changing the barrier and QW thickness results in a shift of emission energy of up to 400 meV, which is explained by quantum confinement and strain. The high interface quality and excellent optical properties of the quantum wells without the need for multiple metal sources or long waiting times represent a significant advance in the development of next-generation optoelectronic devices.

Dataset Information

Strain-induced yellow to blue emission tailoring of axial InGaN/GaN quantum wells in GaN nanorods synthesized by nanoimprint lithography.

Publications

Strain-induced yellow to blue emission tailoring of axial InGaN/GaN quantum wells in GaN nanorods synthesized by nanoimprint lithography.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets