Hierarchical Nanocauliflower Chemical Assembly Composed of Copper Oxide and Single-Walled Carbon Nanotubes for Enhanced Photocatalytic Dye Degradation.

ABSTRACT: We present the fabrication and proficient photocatalytic performance of a series of heterojunction nanocomposites with cauliflower-like architecture synthesized from copper(II) oxide (CuO) nanocrystals and carbon nanotubes with single walls (SWCNTs). These unique photocatalysts were constructed via simplistic recrystallization succeeded by calcination and were labeled as CuOSC-1, CuOSC-2, and CuOSC-3 (representing the components; CuO and SC for SWCNTs, and the calcination time in hours). The photocatalytic potency of the fabricated nanocomposites was investigated on the basis of their capability to decompose methylene blue (MB) dye under visible-light irradiation. Every as-synthesized nanocomposite was effective photocatalyst for the photodecomposition of an MB solution. Moreover, CuOSC-3 exhibited the best photocatalytic activity, with 96% degradation of the visible-light irradiated MB solution in 2 h. Pure CuO nanocrystals generated through the same route and pure SWCNTs were used as controls, where the photocatalytic actions of the nanocomposite samples were found to be remarkably better than that of either the pure CuO or the pure SWCNTs. The recycling proficiency of the photocatalysts was also explored; the results disclosed that the samples could be applied for five cycles without exhibiting a notable change in photocatalytic performance or morphology.

SUBMITTER: Sapkota KP

PROVIDER: S-EPMC7998431 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Pseudocapacitive Effects of Multi-Walled Carbon Nanotubes-Functionalised Spinel Copper Manganese Oxide.

Project description:Spinel copper manganese oxide nanoparticles combined with acid-treated multi-walled carbon nanotubes (CuMn2O4/MWCNTs) were used in the development of electrodes for pseudocapacitor applications. The CuMn2O4/MWCNTs preparation involved initial synthesis of Mn3O4 and CuMn2O4 precursors followed by an energy efficient reflux growth method for the CuMn2O4/MWCNTs. The CuMn2O4/MWCNTs in a three-electrode cell assembly and in 3 M LiOH aqueous electrolyte exhibited a specific capacitance of 1652.91 F g-1 at 0.5 A g-1 current load. Similar investigation in 3 M KOH aqueous electrolyte delivered a specific capacitance of 653.41 F g-1 at 0.5 A g-1 current load. Stability studies showed that after 6000 cycles, the CuMn2O4/MWCNTs electrode exhibited a higher capacitance retention (88%) in LiOH than in KOH (64%). The higher capacitance retention and cycling stability with a Coulombic efficiency of 99.6% observed in the LiOH is an indication of a better charge storage behaviour in this electrolyte than in the KOH electrolyte with a Coulombic efficiency of 97.3%. This superior performance in the LiOH electrolyte than in the KOH electrolyte is attributed to an intercalation/de-intercalation mechanism which occurs more easily in the LiOH electrolyte than in the KOH electrolyte.

| S-EPMC9565235 | biostudies-literature

Double-walled iron oxide nanotubes via selective chemical etching and Kirkendall process.

Project description:Double-walled oxide nanotube structures are interesting for a wide range of applications, from photocatalysis to drug delivery. In this work, a progressive oxidation method to fabricate double-walled nanotube structures is reported in detail. The approach is based on the electrodeposition of metallic iron nanowires, in porous alumina templates, followed by a selective chemical etching, nanoscale Kirkendall effect, a fast oxidation and out-diffusion of the metallic core structure during thermal annealing. To validate the formation mechanism of such core-shell structure, chemical composition and atomic structure were assessed. The resulting hematite nanotubes have a high degree of uniformity, along several microns, and a nanoscopic double-walled structure.

| S-EPMC6700129 | biostudies-literature

Biogenic hierarchical TiO?/SiO? derived from rice husk and enhanced photocatalytic properties for dye degradation.

Project description:BackgroundRice husk, an agricultural bioresource, is utilized as a non-metallic bio-precursor to synthesize biogenic hierarchical TiO?/SiO? (BH-TiO?/SiO?) and the products are applied to dye degradation.Methodology/principal findingsThe as-prepared BH-TiO?/SiO? samples are characterized by X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), nitrogen-adsorption measurement, UV-vis spectroscopy and electronic paramagnetic resonance (EPR). The results show that BH-TiO?/SiO? possesses both anatase and rutile phases with amorphous SiO? as background, which contains mesopore structure, and nitrogen derived from original rice husk is self-doped into the lattice. Besides, the light-harvesting within the visible-light range of BH-TiO?/SiO? has been enhanced. Moreover, the catalytic activity of BH-TiO?/SiO? has been proven by EPR, and both the photocatalytic activity and stability of BH-TiO?/SiO? are improved as well, which has been illustrated by cycled degradation of methylene blue dye under irradiation.Conclusions/significanceThis work provides a good way to combine natural hierarchical porous structure with synthetic material chemistry based on available biomass in the vast natural environment for the sustainable development of human society, and extends potentials of biomass in applications such as photocatalysts, sunlight splitting water and so forth.

| S-EPMC3170388 | biostudies-literature

Three-Dimensional Hierarchical Porous TiO<sub>2</sub> for Enhanced Adsorption and Photocatalytic Degradation of Remazol Dye.

Project description:Three-dimensional hierarchical mesoporous structures of titanium dioxide (3D-HPT) were synthesized by self-assembly emulsion polymerization. Polymethyl methacrylate (PMMA) and pluronic 123 (P123) were used as the soft templates and co-templates for assisting the formation of hierarchical 3D porous structures. The TiO2 crystal structure, morphology, and Remazol red dye degradation were investigated. The 3D-HPT and normal three-dimensional titanium dioxide (3D-T) presented the good connection of the nanoparticle-linked honeycomb within the form of anatase. The 3D-HPT structure showed greatly enhanced adsorption of Remazol dye, and facilitated the efficient photocatalytic breakdown of the dye. Surprisingly, 3D-HPT can adsorb approximately 40% of 24 ppm Remazol dye in the dark, which is superior to 3D-T and the commercial anatase at the same condition (approx. 5%). Moreover, 3D-HPT can completely decolorize Remazol dye within just 20 min, which is more than three folds faster than the commercial anatase, making it one of the most active photocatalysts that have been reported for degradation of Remazol dye. The superior photocatalytic performance is attributed to the higher specific surface area, amplified light-harvesting efficiency, and enhanced adsorption capacity into the hierarchical 3D inverse opal structure compared to the commercial anatase TiO2.

| S-EPMC8307786 | biostudies-literature

Three-dimensional reduced graphene oxide aerogel stabilizes molybdenum trioxide with enhanced photocatalytic activity for dye degradation.

Project description:By using three-dimensional reduced graphene oxide (rGO) aerogel as a carrier for molybdenum trioxide (MoO3), a series of rGO-MoO3 aerogels were synthesized by a self-assembly process. The results indicated that the as-prepared rGO-MoO3 aerogel had very low density and good mechanical properties, and would not deform under more than 1000 times its own pressure. The rGO-MoO3 aerogel showed more than 90% degradation efficiency for MB within 120 min. After six cycles of recycling, the degradation rate of MB only decreased by 1.6%. As supported by the electron paramagnetic resonance (EPR) measurements, the presence of the rGO aerogel enhanced electron conduction, prolonged carrier lifetime and inhibited electron and hole recombination, thus improving the photocatalytic efficiency of composite aerogel. Besides, the hydroxyl radical (OH˙) and radical anion (˙O2 -) played an important role in the photodegradation of the dye. The outstanding adsorption and photocatalytic degradation performance of the rGO-MoO3 aerogel was attributed to its unique physical properties, such as high porosity, simple recycling process, high hydrophobicity, low density and excellent mechanical stability. The findings presented herein indicated that the rGO-MoO3 aerogel had good application potential, and could serve as a promising photocatalyst for the degradation of dyes in wastewater.

| S-EPMC9075745 | biostudies-literature

Enhancement of photocatalytic efficacy by exploiting copper doping in nano-hydroxyapatite for degradation of Congo red dye.

Project description:This research deals with the photocatalytic activity of hydroxyapatite and the improvement of efficiency by doping various percentages of copper; the catalysts were synthesized by the wet-chemical method. Pure and copper-doped photocatalysts were characterized by several techniques including X-ray diffraction (XRD), Fourier Transform Infrared (FTIR) spectroscopy, Raman spectroscopy, scanning electron microscopy (SEM), thermogravimetric analysis (TGA), dynamic scanning calorimetry (DSC), and UV-Vis spectroscopy. The competency of pure and copper-doped hydroxyapatite as photocatalysts was assessed by their interaction with Congo red dye. The crystallographic parameters of the catalysts were also estimated by employing the XRD technique, and a relationship was established between the calculated parameters and photocatalytic performance. Crystallite size was calculated from various model equations, which revealed an acceptable crystallite size of 42-68 nm. Copper doping in hydroxyapatite impressively augmented the photocatalytic efficacy, for example 99% dye was degraded upon 0.63% Cu-doping compared to 75% for the pure HAp, which was exemplified not only by the reaction rate but also by the quantum yield. The degradation percentages changed with time but became fixed at 200 min. The molar extinction coefficient was estimated by employing the Beer-Lambert law and further utilized to compute the photonic efficiency of the catalysts. In the study of the photochemical reaction, a simplified reaction process was proposed, and the potentials of the conduction band and valence band were assessed, which influenced the activity. The doping of Cu in crystalline hydroxyapatite will enhance the photocatalytic activity towards Congo red dye under all experimental conditions.

| S-EPMC9704492 | biostudies-literature

Trimetallic composite nanofibers for antibacterial and photocatalytic dye degradation of mixed dye water.

Project description:Membrane technology is an advanced approach to making a healthier and cleaner environment. Using such catalytic membrane technology to get clean, usable water by removal of dye impurities as well as pathogenic microbes is the main goal behind the research work. Here, we present the synthesis and efficacy study of polymethyl methacrylate (PMMA)-based Ag/ZnO/TiO2 trimetallic bifunctional nanofibers with antibacterial and photocatalytic activity. The nanofibers have been proven to be effective for the degradation of methylene blue (MB 93.4%), rhodamine B (Rh 34.6%), auramine-O (Au 65.0%) and fuchsin basic (FB 69.8%) dyes individually within 90 min in daylight. The study is further extended in abating a mixture of these dyes from contaminated water using composite nanofibers. Also, in the case of a mixture of these dyes (3 ppm each), nanofibers show dye degradation efficiency (DDE) of 90.9% (MB), 62.4% (Au) and 90.3% (FB and Rh) in 60 min. The role of Ag nanoparticles with a synergic photocatalytic effect on ZnO and TiO2 is also demonstrated. Also, PMMA/ZnO/TiO2 composite fiber membrane in synergy with silver particles shows better antibacterial activity against Gram-negative bacteria E. coli, making PMMA/Ag/ZnO/TiO2 fibers a promising candidate in water purification.

| S-EPMC7446745 | biostudies-literature

Nitrogen-Doped Alkylamine-Intercalated Layered Titanates for Photocatalytic Dye Degradation.

Project description:A layered titanate, K2Ti4O9, is intercalated with various n-alkylamines through ion-exchange reaction in aqueous medium. On heating, the intercalated amine is partially deintercalated, yielding nitrogen-doped amine-intercalated titanates. The modified titanates are studied as catalysts in methylene blue degradation under UV irradiation. Heat-treated long-chain amine titanates exhibit better photocatalytic activity in comparison to short chain amine titanates. The improved catalytic activity could be attributed to two factors: (i) increased surface access as the titanate layers are well separated, pillared by the alkylamine chains and (ii) nitrogen doping.

| S-EPMC6648551 | biostudies-literature

Single-walled vs. Multi-walled Carbon Nanotubes: Influence of Physico-Chemical Properties on Toxicogenomics Responses in Mouse Lungs

Project description:Transcriptional profiling of mouse lung tissue comparing control vs exposure to different carbon nanotubes. The aim was to determine if the physico-chemical properties influence the genotoxic, inflammatory and pro-fibrotic responses.

2023-03-16 | GSE223520 | GEO

Preparation of TiO₂/Carbon Nanotubes/Reduced Graphene Oxide Composites with Enhanced Photocatalytic Activity for the Degradation of Rhodamine B.

Project description:In this report, ternary titanium dioxide (TiO₂)/carbon nanotubes (CNTs)/reduced graphene oxide (rGO) composites were fabricated by a facile and environmentally friendly one-pot solvethermal method for the removal of Rhodamine B (RhB). Its structures were represented by X-ray powder diffraction (XRD), Raman spectrometry, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The photocatalytic performance was tested by the degradation efficiency of RhB under UV-vis light irradiation. The experimental results indicated that photocatalytic activity improved as the ratio of CNTs:TiO₂ ranged from 0.5% to 3% but reduced when the content increased to 5% and 10%, and the TiO₂/CNTs/rGO-3% composites showed superior photocatalytic activity compared with the binary ones (i.e., TiO₂/CNTs, TiO₂/rGO) and pristine TiO₂. The rate constant k of the pseudo first-order reaction was about 1.5 times that of TiO₂. The improved photocatalytic activity can be attributed to the addition of rGO and CNTs, which reduced the recombination of photo-induced electron-hole pairs, and the fact that CNTs and rGO, with a high specific surface area and high adsorption ability to efficiently adsorb O₂, H₂O and organics, can increase the hydroxyl content of the photocatalyst surface.

| S-EPMC6027058 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data